Internal mold release agents, their use for preparing molded articles using polyisocyanate-addition polymerization, and a process for preparing molded articles

Claim 2

An internal mold release agent for the preparation of molded articles using polyisocyanate addition polymerization comprising; and (A) at least one ketimine, aldimine, enamine, cyclic Schiff base or a mixture of at least two of said compounds; and (B) at least one metal salt of an organic carboxylic acid having from 8 to 24 carbon atoms; and (C) optionally including at least one organic carboxylic acid, organic sulfonic acid, mineral acid or amidosulfonic acid.

Claim 3

The internal mold release agent of claim 1 wherein said mold release agent comprises: (A) from 5 to 90 parts by weights of at least one of said ketimine, aldimine, enamine, cyclic Schiff base or a mixture of at least two of said compounds; (B) from 10 to 95 parts by weight of at least one of said metal salt of an organic carboxylic acid having from 8 to 24 carbon atoms; and (C) from 0 to 50 parts by weight of at least one of said carboxylic acid, organic sulfonic acid, mineral acid, or amidosulfonic acid, based on 100 parts by weight of components (A) and (B).

Claim 4

The internal mold release agent according to claim 2 wherein said ketimines and/or aldimines (A) are prepared through the reaction of: optionally substituted aliphatic, cycloaliphatic, heterocyclic and/or aromatic primary monoamines having from 1 to 20 carbon atoms and/or primary polyamines having from 2 to 20 carbon atoms, optionally substituted aliphatic, cycloaliphatic, heterocyclic and/or aromatic primary mono and/or polyamines, which additionally contain in bonded form secondary and/or tertiary amino groups and/or heterocyclic radicals and/or hydroxyl groups and/or ether groups, or linear, branched or cyclic alkanolamines having from 2 to 22 carbon atoms and/or polyoxyalkylene-polyamines having molecular weights from 204 to 5000, with aromatic, aliphatic-aromatic, cycloaliphatic or aliphatic ketones and/or diketones or optionally substituted aliphatic and/or aromatic aldehydes, dialdehydes and/or acetals.

Claim 5

The internal mold release agent according to claim 2 wherein said enamines and/or polyenamines (A) are prepared through the reaction of optionally substituted aliphatic, cycloaliphatic, heterocyclic and/or aromatic secondary mono and/or polyamines with aliphatic aldehydes or cycloaliphatic ketones.

Claim 6

The internal mold release agent according claim 2 wherein 2-methylΔ 1 -piperidine and/or 3,4-dihydroisoquinoline are used as said cyclic Schiff base.

Claim 7

The internal mold release agent according to claim 2 wherein said aldimine or ketimine (A) has in bonded form an enolizable hydrogen atom.

Claim 8

The internal mold release agent according to claim 2 wherein the metal of said metal salts (B) belongs to group IA, IB, IIA or IIB from the periodic table, or is aluminum, chromium, molybdenum, iron, cobalt, zinc, nickel, lead, antimony or bismuth.

Claim 9

The internal mold release agent according to claim 2 wherein at least one metal salt of stearic and/or isostearic acid is used as metal salt (B).

Claim 10

The internal mold release agent according to claim 8 wherein zinc stearate, zinc isostearate, calcium stearate, sodium stearate or a mixture of at least two of said stearates is used as metal salt (B).

Claim 11

The internal mold release agent according to claim 2 wherein aliphatic monocarboxylic acids having from 1 to 20 carbon atoms, aliphatic dicarboxylic acids having from 2 to 36 carbon atoms or their anhydrides, or aromatic monocarboxylic acids having from 7 to 12 carbon atoms and/or aromatic dicarboxylic acids having from 8 to 17 carbon atoms or their anhydrides; or mixtures of said aliphatic and aromatic acids are used as organic carboxylic acids (C).

Claim 12

A non-cellular, molded article cellular molded article, or molded article having a cellular core and noncellular peripheral zone prepared by polyisocyante addition polymerization carried out in the presence of an internal mold release agent according to claim 2.

Claim 13

The article according to claim 11 wherein said polyisocyanate addition polymerization is reaction injection molding.

Claim 14

The article according to claim 12 wherein said cellular mold articles have a density of from 0.3 to 1.1 g/cm 3 ; said molded articles having a cellular core and non-cellular peripheral zone have an overall density of from 0.05 to 1.2 g/cm 3 ; or said non-cellular molded articles have a density of from 0.9 to 1.4 g/cm 3 .

Claim 15

The article according to claim 13 wherein said article is comprised of polyurethane, polyurea, polyurethane-polyurea, polyurethane-polyurea-polyamide or polyurea-polyamide plastic.

Claim 16

A process for the preparation of cellular or noncellular molded articles or molded articles having a cellular core and non-cellular peripheral zone having improved demolding properties using polyisocyanate addition polymerization by reacting; (a) an organic polyisocyanate; (b) a higher molecular weight compound having at least 2 reactive hydrogen atoms; (c) a chain extending agent and/or cross linker; in the presence of (e) an internal mold release agent; (f) a catalyst; and optionally in the presence of (g) a blowing agent; (h) auxiliaries and/or additives in open, or closed molds, wherein said internal mold release agent (e) is a mixture comprised of (A) from 5 to 90 parts by weight of at least one ketimine, aldimine, enamine, cyclic Schiff base or a mixture of at least two of said compounds, (B) from 10 to 95 parts by weight of at least one metal salt of an organic carboxylic acid having from 8 to 24 carbon atoms; and (C) from 0 to 50 parts by weight of at least one organic carboxylic acid, organic sulfonic acid, mineral acid or amidosulfonic acid, based on 100 parts by weight of the initial components (A) and (B).

Claim 17

A process for the preparation of cellular or noncellular molded articles or molded articles having a cellular core and non-cellular peripheral zone having improved demolding properties using polyisocyanate addition polymerization by reacting; (a) an organic polyisocyanate; (b) a higher molecular weight compound having at least 2 reactive hydrogen atoms; (c) a chain extending agent and/or cross linker; in the presence of (e) an internal mold release agent; (f) a catalyst; and optionally in the presence of (g) a blowing agent; (h) auxiliaries and/or additives in open, or closed molds, wherein said internal mold release agent (e) is a mixture comprised of (A) from 5 to 90 parts by weight of at least one ketimine, aldimine, enamine, cyclic Schiff base or a mixture of at least two of said compounds, (B) from 10 to 95 parts by weight of at least one metal salt of an organic carboxylic acid having from 8 to 24 carbon atoms; and (C) from 0 to 50 parts by weight of at least one organic carboxylic acid, organic sulfonic acid, mineral acid or amidosulfonic acid, based on 100 parts by weight of the initial components (A) and (B).

Claim 18

The process of claim 15 wherein said polyisocyanate addition polymerization is reaction injection molding.

Claim 19

The process according to claim 16 wherein the internal mold release agent (e) is used in a quantity of from 0.1 to 15 parts by weight based on 100 parts by weight of initial components (b) and (c).