Process for preparation of sintered silicon nitride
Assignee: Sumitomo Electric Industries Ltd
•
Filing: 1986-04-08
•
Granted: 1988-08-16
•
Expires: 2006-04-08
Abstract
Abstract Disclosed is a process for preparation of a sintered silicon nitride. The process comprises the steps of: mixing a powder of silicon nitride with a powder of a sintering agent; compacting the obtained mixture; and sintering the compacted mixture in a non-oxidizing atmosphere. The feature of the process is that the powder of the sintering agent includes a powder mixture of oxide and/or hydroxide of at least two kinds of metals which has been prepared by co-precipitation. Due to the use of the co-precipitated powder as the sintering agent, it is possible to obtain a sintered silicon nitride having an excellent strength and uniformity in quality. The obtained sintered silicon nitride is preferably used as an engineering ceramic.
Inventors
- 👤 Akira Yamakawa
- 👤 Masaya Miyake
- 👤 Takao Nishioka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 13:32
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/593; C04B35/5935
Claims Analysis
Total Claims: 42
Claim 1
Independent Claim
81 words
A process for preparing a sintered silicon nitride comprising the steps of: providing a powder of a sintering agent as a powder mixture, prepared by co-precipitation, consisting of an oxide and/or hydroxide of at least two kinds of metals selected from the group consisting of Mg, Al, Si, Sc, T, lanthanide, Ti, Zr and Hf; mixing a powder of silicon nitride with the powder of the sintering agent; compacting the obtained mixture; and sintering the compacted mixture in a non-oxidizing atmosphere.
Claim 2
Dependent Claim
81 words
A process for preparing a sintered silicon nitride comprising the steps of: providing a powder of a sintering agent as a powder mixture, prepared by co-precipitation, consisting of an oxide and/or hydroxide of at least two kinds of metals selected from the group consisting of Mg, Al, Si, Sc, T, lanthanide, Ti, Zr and Hf; mixing a powder of silicon nitride with the powder of the sintering agent; compacting the obtained mixture; and sintering the compacted mixture in a non-oxidizing atmosphere.
Claim 3
Dependent Claim
41 words
A process as claimed in claim 1, wherein the sintering agent is mixed in an amount of 1.0 to 50 wt% calculated in terms of the oxide contained therein on the basis of the total weight of the sintered silicon nitride.
Claim 4
Dependent Claim
29 words
A process as claimed in claim 2, wherein the co-precipitated powder consists of an oxide and/or hydroxide of metals selected from the group consisting of Zr, Y and lanthanide.
Claim 5
Dependent Claim
33 words
A process as claimed in claim 3, wherein the co-precipitated powder consists of an oxide and/or hydroxide of Zr and at least one element selected from the group consisting of Y and lanthanide.
Claim 6
Dependent Claim
91 words
A process as claimed in claim 4, wherein the co-precipitated powder consists of ZrO 2 and an oxide of at least one element selected from the group consisting of Y and lanthanide, and the content of ZrO 2 being 1 to 25 vol% on the basis of the total volume of the sintered silicon nitride and the content of the oxide of Y or lanthanide being 0.5 to 10 wt% calculated in terms of the amount of the element on the basis of the total weight of the sintered silicon nitride.
Claim 7
Dependent Claim
36 words
A process as claimed in claim 5, wherein ZrO 2 is cubic crystal which has been stabilized with at least one member selected from the group consisting of CaO, MgO and Y 2 O 3 .
Claim 8
Dependent Claim
43 words
A process as claimed in claim 6, wherein, in order to provide the sintering agent, hydroxides of Zr and Y are co-precipitated and the co-precipitate is then burned to provide a powder of cubic ZrO 2 stabilized with Y 2 O 3 .
Claim 9
Dependent Claim
41 words
A process as claimed in claim 4, further incorporating in the mixture 1 to 15 wt% of at least one element selected from the group consisting of the elements of IVa (except Zr), Va and VIa groups of the Periodic Table.
Claim 10
Dependent Claim
48 words
A process as claimed in claim 8, wherein the at least one element is selected from IVa (except Zr), Va and VIa group of the Periodic Table and is added to the mixture in the form of anyone of carbide, nitride, carbonitride, oxide and the solid solution thereof.
Claim 11
Dependent Claim
51 words
A process as claimed in claim 9, wherein the oxide of at least one element selected from the group consisting of IVa (except Zr), Va and VIa groups of the Periodic Table is added to the mixture in the co-precipitated form with oxide or hydroxide of Zr and Y or lanthanide.
Claim 12
Dependent Claim
41 words
A process as claimed in claim 1, wherein the hydroxides of metal have been prepared by adjusting the pH of an aqueous solution containing a water-soluble metal chloride, metal nitrate or organic metal salt to thereby co-precipitate the metal hydroxides therefrom.
Claim 13
Dependent Claim
20 words
A process as claimed in claim 11, further burning the metal hydroxides to thereby provide a co-precipitate of metal oxides.
Claim 14
Dependent Claim
21 words
A process as claimed in claim 1, wherein the mean particle size of the co-precipitated powder is smaller than 2 microns.
Claim 15
Dependent Claim
16 words
A process as claimed in claim 1, wherein the sintering is conducted under a depressurized condition.
Claim 16
Dependent Claim
16 words
A process as claimed in claim 1, wherein the sintering is conducted under a pressurized condition.
Claim 17
Dependent Claim
58 words
A process for preparing a sintered silicon nitride comprising the steps of: providing a powder consisting of ZrO 2 and Y 2 O 3 prepared by co-precipitation; mixing a powder of silicon nitride with the powder of ZrO 2 and Y 2 O 3 ; compacting the obtained mixture; and sintering the compacted mixture in a non-oxidizing atmosphere.
Claim 18
Dependent Claim
58 words
A process for preparing a sintered silicon nitride comprising the steps of: providing a powder consisting of ZrO 2 and Y 2 O 3 prepared by co-precipitation; mixing a powder of silicon nitride with the powder of ZrO 2 and Y 2 O 3 ; compacting the obtained mixture; and sintering the compacted mixture in a non-oxidizing atmosphere.
Claim 19
Dependent Claim
64 words
A process as claimed in claim 16, wherein the content of ZrO 2 is 1 to 25 vol% on the basis of the total volume of the sintered silicon nitride and the content of the oxide of Y is 0.5 to 10 wt% calculated in terms of the amount of the element on the basis of the total weight of the sintered silicon nitride.
Claim 20
Dependent Claim
36 words
A process as claimed in claim 17, wherein ZrO 2 is cubic crystal which has been stabilized with at least one member selected from the group consisting of CaO, MgO and Y 2 O 3 .
Claim 21
Dependent Claim
36 words
A process as claimed in claim 18, wherein hydroxides of Zr and Y are co-precipitated and the co-precipitate is then burned to provide a powder of cubic ZrO 2 stabilized with Y 2 O 3 .
Claim 22
Dependent Claim
41 words
A process as claimed in claim 16, further incorporating to the mixture 1 to 15 wt% in at least one element selected from the group consisting of the elements of IVa (except Zr), Va and VIa groups of the Periodic Table.
Claim 23
Dependent Claim
48 words
A process as claimed in claim 20, wherein the at least one element is selected from IVa (except Zr), Va and VIa groups of the Periodic Table and is added to the mixture in the form of anyone of carbide, nitride, carbonitride, oxide and the solid solution thereof.
Claim 24
Dependent Claim
52 words
A process as claimed in claim 21, wherein the oxide of at least one element selected from the group consisting of IVa (except Zr), Va and VIa groups of the Periodic Table is added to the mixture in the co-precipitated form with the and lanthanide oxide or hydroxide of Zr and Y.
Claim 25
Dependent Claim
47 words
A process as claimed in claim 16, wherein, in order to provide the sintering agent, the hydroxides of metal have been prepared by adjusting the pH of an aqueous solution containing a water-soluble metal chloride, metal nitrate or organic metal salt to co-precipitate the metal hydroxides therefrom.
Claim 26
Dependent Claim
20 words
A process as claimed in claim 23, further burning the metal hydroxides to thereby provide a co-precipitate of metal oxides.
Claim 27
Dependent Claim
21 words
A process as claimed in claim 16, wherein the mean particule size of the co-precipitated powder is smaller than 2 microns.
Claim 28
Dependent Claim
16 words
A process as claimed in claim 16, wherein the sintering is conducted under a depressurized condition.
Claim 29
Dependent Claim
16 words
A process as claimed in claim 16, wherein the sintering is conducted under a pressurized condition.
Claim 30
Dependent Claim
114 words
A process for preparing a sintered silicon nitride comprising the steps of: preparing an aqueous solution containing water-soluble chloride, nitrate or organic salt of at least two metals selected from the group consisting of Mg, Al, Si, Sc, Y, lanthanide, Ti, Zr and Hf; adjusting the pH of said aqueous solution to thereby co-precipitate hydroxides of said metals therefrom; burning the co-precipitated hydroxides to form oxides of said metals in the form of powder; mixing a powder of silicon nitride with said burned metal oxide powder; compacting the obtained mixture; and sintering the compacted mixture in a non-oxidizing atmosphere; whereby providing a sintered silicon nitride having improved strength and uniformity in its mechanical properties.
Claim 31
Dependent Claim
114 words
A process for preparing a sintered silicon nitride comprising the steps of: preparing an aqueous solution containing water-soluble chloride, nitrate or organic salt of at least two metals selected from the group consisting of Mg, Al, Si, Sc, Y, lanthanide, Ti, Zr and Hf; adjusting the pH of said aqueous solution to thereby co-precipitate hydroxides of said metals therefrom; burning the co-precipitated hydroxides to form oxides of said metals in the form of powder; mixing a powder of silicon nitride with said burned metal oxide powder; compacting the obtained mixture; and sintering the compacted mixture in a non-oxidizing atmosphere; whereby providing a sintered silicon nitride having improved strength and uniformity in its mechanical properties.
Claim 32
Dependent Claim
41 words
A process as claimed in claim 28, wherein the burned powder is mixed in an amount of 1.0 to 50 wt% calculated in terms of the oxide contained therein on the basis of the total weight of the sintered silicon nitride.
Claim 33
Dependent Claim
26 words
A process as claimed in claim 29, wherein the burned powder consists of oxides of metals selected from the group consisting of Zr, Y and lanthanide.
Claim 34
Dependent Claim
30 words
A process as claimed in claim 30, wherein the burned powder consists of oxides of Zr and at least one element selected from the group consisting of Y and lanthanide.
Claim 35
Dependent Claim
69 words
A process as claimed in claim 31, wherein the content of ZrO 2 being 1 to 25 vol% on the basis of the total volume of the sintered silicon nitride and the content of the oxide of Y or lanthanide being 0.5 to 10 wt% calculated in terms of the amount of the element Y or lanthanide on the basis of the total weight of the sintered silicon nitride.
Claim 36
Dependent Claim
22 words
A process as claimed in claim 32, wherein the burned powder includes cubic ZrO 2 stabilized with Y 2 O 3 .
Claim 37
Dependent Claim
41 words
A process as claimed in claim 31, further incorporating in the mixture 1 to 15 wt% of at least one element selected from the group consisting of the elements of IVa (except Zr), Va and VIa groups of the Periodic Table.
Claim 38
Dependent Claim
48 words
A process as claimed in claim 34, wherein the at least one element is selected from IVa (except Zr), Va and VIa groups of the Periodic Table and is added to the mixture in the form of anyone of carbide, nitride, carbonitride, oxide and the solid solution thereof.
Claim 39
Dependent Claim
49 words
A process as claimed in claim 35, wherein the oxide of at least one element selected from the group consisting of IVa (except Zr), Va and VIa groups of the Periodic Table is added to the mixture in the co-precipitated form with oxides of Zr and Y or lanthanide.
Claim 40
Dependent Claim
21 words
A process as claimed in claim 28, wherein the mean particle size of the burned powder is smaller than 2 microns.
Claim 41
Dependent Claim
16 words
A process as claimed in claim 28, wherein the sintering is conducted under a depressurized condition.
Claim 42
Dependent Claim
16 words
A process as claimed in claim 28, wherein the sintering is conducted under a pressurized condition.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-16 | 1992-02-15 | 1992-08-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-16 | 1996-02-15 | 1996-08-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-16 | 2000-02-15 | 2000-08-16 | $7700.00 | Window Closed / Lapsed |