Water-based thermoforming adhesives
Assignee: ROYAL ADHESIVES AND SEALANTS LLC
•
Filing: 1987-05-05
•
Granted: 1988-08-09
•
Expires: 2007-05-05
Abstract
Abstract This invention presents new water-based adhesives suitable for use in thermoforming lamination systems. More particularly, this invention presents water-based adhesive-forming compositions comprising an aromatic polyurethane in water dispersion or emulsion and a compatible cross-linking agent; also includable in the compositions are thickening agents and pigments. These new adhesives, it has been found, exhibit bonding strengths and temperature resistance far superior to the solvent and water-based adhesives currently used in industrial applications, and are useful in thermoforming lamination processes. Also disclosed is a one-step thermoform lamination edge-folding process using the adhesive.
Inventors
- 👤 Pak T. Leung
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 11:08
CPC Classifications
C; C09; C09J; C09J175/00; C09J175/04; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/0838; C08G18/0842; C08G18/0861; C08G18/0866; C08G18/10; C08G2170/00; C08G2170/80
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
101 words
An adhesive forming composition comprising: (a) an aqueous aromatic polyurethane emulsion or dispersion comprising a polyurethane compound of repeating urethane subunits, each having at least one aromatic substituent associated therewith; and (b) an effective amount of a cross-linking agent which is water-dispersible and stable in the presence of water yet being able to induce cross-linking of the polyurethane at room temperature at a rate sufficient to permit the composition to form an adhesive having suitable ultimate bond strength and green strength; said emulsion or dispersion having a sufficient solids content to enable the resultant adhesive to join and hold components together.
Claim 2
Dependent Claim
101 words
An adhesive forming composition comprising: (a) an aqueous aromatic polyurethane emulsion or dispersion comprising a polyurethane compound of repeating urethane subunits, each having at least one aromatic substituent associated therewith; and (b) an effective amount of a cross-linking agent which is water-dispersible and stable in the presence of water yet being able to induce cross-linking of the polyurethane at room temperature at a rate sufficient to permit the composition to form an adhesive having suitable ultimate bond strength and green strength; said emulsion or dispersion having a sufficient solids content to enable the resultant adhesive to join and hold components together.
Claim 3
Dependent Claim
18 words
The adhesive-forming composition of claim 1 wherein the emulsion or dispersion has a solids content ranging from 10-60%.
Claim 4
Dependent Claim
22 words
The adhesive-forming composition of claim 1 wherein the amount of cross-linking agent is between 0.1 and 20%, by weight, of the composition.
Claim 5
Dependent Claim
21 words
The adhesive-forming composition of claim 1 further comprising an effective amount of a thickener to increase the viscosity of said composition.
Claim 6
Dependent Claim
21 words
The adhesive-forming composition of claim 4 wherein the amount of thickener is between 0.1 and 5%, by weight, of the composition.
Claim 7
Dependent Claim
20 words
The adhesive-forming composition of claim 1 further comprising an effective amount of pigment to impart a color to said composition.
Claim 8
Dependent Claim
21 words
The adhesive-forming composition of claim 6, wherein the amount of pigment is between 0.1 and 10% by weight, of the composition.
Claim 9
Dependent Claim
18 words
The adhesive-forming composition of claim 1 wherein the cross-linking agent is a solvent-free, water-dispersible, unblocked organic isocyanate compound.
Claim 10
Dependent Claim
15 words
The adhesive-forming composition of claim 8 wherein the organic isocyanate compound is an aliphatic polyisocyanate.
Claim 11
Dependent Claim
13 words
A cross-linked polyurethane adhesive formed from the adhesive forming composition of claim 1.
Claim 12
Dependent Claim
13 words
The adhesive composition of claim 4 wherein the thickener is an acrylate thickener.
Claim 13
Dependent Claim
98 words
An adhesive-forming composition comprising: (a) an aqueous aromatic polyurethane emulsion or dispersion comprising a polyurethane compound of repeating urethane subunits, each having at least one aromatic substituent associated therewith; and (b) an effective amount of a cross-linking agent of a solvent-free, water-dispersible, unblocked organic isocyanate compound which is able to induce cross-linking of the polyurethane at room temperature at a rate sufficient to permit the composition to form an adhesive having suitable ultimate bond strength and green strength; said emulsion or dispersion having a sufficient solids content to enable the resultant adhesive to join and hold components together.
Claim 14
Dependent Claim
98 words
An adhesive-forming composition comprising: (a) an aqueous aromatic polyurethane emulsion or dispersion comprising a polyurethane compound of repeating urethane subunits, each having at least one aromatic substituent associated therewith; and (b) an effective amount of a cross-linking agent of a solvent-free, water-dispersible, unblocked organic isocyanate compound which is able to induce cross-linking of the polyurethane at room temperature at a rate sufficient to permit the composition to form an adhesive having suitable ultimate bond strength and green strength; said emulsion or dispersion having a sufficient solids content to enable the resultant adhesive to join and hold components together.
Claim 15
Dependent Claim
18 words
The adhesive-forming composition of claim 12 wherein the emulsion or dispersion has a solids content ranging from 10-60%.
Claim 16
Dependent Claim
22 words
The adhesive-forming composition of claim 12 wherein the amount of cross-linking agent is between 0.1 and 20% by weight, of the composition.
Claim 17
Dependent Claim
21 words
The adhesive-forming composition of claim 12 further comprising an effective amount of a thickener to increase the viscosity of said composition.
Claim 18
Dependent Claim
12 words
The adhesive-forming composition of claim 12 wherein the thickener is an acrylate.
Claim 19
Dependent Claim
21 words
The adhesive-forming composition of claim 15 wherein the amount of thickener is between 0.1 and 5%, by weight, of the composition.
Claim 20
Dependent Claim
21 words
The adhesive-forming composition of claim 12 further comprising an effective amount of a pigment to impart a color to said composition.
Claim 21
Dependent Claim
21 words
The adhesive-forming composition of claim 18 wherein the amount of pigment is between 0.1 and 10% by weight, of the composition.
Claim 22
Dependent Claim
15 words
The adhesive-forming composition of claim 12 wherein the organic isocyanate compound is an aliphatic polyisocyanate.
Claim 23
Dependent Claim
13 words
A cross-linked polyurethane adhesive formed from the adhesive forming composition of claim 12.
Claim 24
Dependent Claim
151 words
An adhesive-forming composition comprising: (a) an aqueous aromatic polyurethane emulsion or dispersion comprising a polyurethane compound of repeating urethane subunits, each having at least one aromatic substituent associated therewith; (b) a cross-linking agent in an amount of between 0.1 and 20%, by weight of the composition, of a solvent-free, water-dispersible, unblocked organic isocyanate compound which is able to induce cross-linking of the polyurethane at room temperature at a rate sufficient to permit the composition to form an adhesive having suitable ultimate bond strength and green strength; (c) between 0.1 and 5%, by weight of the composition, of a thickener to increase the viscosity of the composition; and (d) between 0.1 and 10%, by weight of the composition, of a pigment to impart a color to the composition; said emulsion or dispersion having a solids content of between 10 and 60% to enable the resultant adhesive to join and hold components together.
Claim 25
Dependent Claim
151 words
An adhesive-forming composition comprising: (a) an aqueous aromatic polyurethane emulsion or dispersion comprising a polyurethane compound of repeating urethane subunits, each having at least one aromatic substituent associated therewith; (b) a cross-linking agent in an amount of between 0.1 and 20%, by weight of the composition, of a solvent-free, water-dispersible, unblocked organic isocyanate compound which is able to induce cross-linking of the polyurethane at room temperature at a rate sufficient to permit the composition to form an adhesive having suitable ultimate bond strength and green strength; (c) between 0.1 and 5%, by weight of the composition, of a thickener to increase the viscosity of the composition; and (d) between 0.1 and 10%, by weight of the composition, of a pigment to impart a color to the composition; said emulsion or dispersion having a solids content of between 10 and 60% to enable the resultant adhesive to join and hold components together.
Claim 26
Dependent Claim
12 words
The adhesive-forming composition of claim 22 wherein the thickener is an acrylate.
Claim 27
Dependent Claim
15 words
The adhesive-forming composition of claim 22 wherein the organic isocyanate compound is an aliphatic polyisocyanate.
Claim 28
Dependent Claim
13 words
A cross-linked polyurethane adhesive formed from the adhesive forming composition of claim 22.
References Cited (Backward Citations)
US3948708A
Cited
US4084996A
Cited
US4225372A
Cited
US4465534A
Cited
US4465537A
Cited
US4507413A
Cited
US4643785A
Cited
US4543144A
Cited
US4526828A
Cited
US4526828B1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-09 | 1992-02-08 | 1992-08-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-09 | 1996-02-08 | 1996-08-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-09 | 2000-02-08 | 2000-08-09 | $7700.00 | Window Closed / Lapsed |