Thermochemical surface treatments of materials in a reactive gas plasma
Assignee: OC Oerlikon Balzers AG
•
Filing: 1987-06-12
•
Granted: 1988-08-09
•
Expires: 2007-06-12
Abstract
Abstract A method for the thermochemical surface treatment of workpieces in a reactive gas plasma is disclosed in which an appreciable reduction in the amount of reactive gas and energy used is achieved by working at gas pressures below 10 pascals (Pa). Particularly advantageous results are achieved with a low-voltage electrical arc discharge, which leads to an ionization of the gases used (about 50%) that is substantially higher than that, which is achieved with the methods described in the art 6 (approximately 1%). Surfaces, treated by such a conduct of the reaction, are distinguished by an increased hardness and better wear properties. The method of the invention moreover allows more numerous variation possibilities than do the methods described in the art and enables the conduct of the method to be adapted in a flexible manner to the specific requirements of the particular case. The inventive method permits a time sequence of the several treatment steps with different reactive gases or gas mixtures and thus a combination of different foreign elements in the treated substrate surface.
Inventors
- 👤 Erich Bergmann
- 👤 Elmar Hummer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 10:29
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/02; C23C16/0272; C23C14/00; C23C14/02; C23C14/021; C23C14/022; C23C8/00; C23C8/06; C23C8/36
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
74 words
A method for the thermochemical surface treatment of materials in a reaction chamber the method comprising the steps of: maintaining a gas pressure in the reaction chamber of less than 10 pascals (Pa) generating a gas plasma in an arc discharge of low voltage having a low current density lying in the range of 10 5 to 7×10 5 A/m 2 and treating the materials in the reaction chamber with said reactive gas plasma.
Claim 2
Independent Claim
74 words
A method for the thermochemical surface treatment of materials in a reaction chamber the method comprising the steps of: maintaining a gas pressure in the reaction chamber of less than 10 pascals (Pa) generating a gas plasma in an arc discharge of low voltage having a low current density lying in the range of 10 5 to 7×10 5 A/m 2 and treating the materials in the reaction chamber with said reactive gas plasma.
Claim 3
Dependent Claim
19 words
The method according to claim 1, wherein the pressure lies in the range of 0.06 to 0.6 pascals (Pa).
Claim 4
Dependent Claim
38 words
The method according to claim 1, wherein said step of treating in a gas plasma includes generating the gas plasma in an arc discharge the electrical arc being discharged between a heated, gas-stabilized cathode and a liquid-cooled anode.
Claim 5
Dependent Claim
28 words
The method according to claim 2, wherein the arc discharge is used simultaneously to generate the gas plasma and to heat a substrate positioned in the reaction chamber.
Claim 6
Dependent Claim
27 words
The method according to claim 1 wherein the materials to be treated are subjected to a plasma-chemical etching before the thermochemical surface treatment in the gas plasma.
Claim 7
Dependent Claim
27 words
The method according to claim 1 further comprising the step of: implanting different foreign elements at consecutive times in the substrate surface by changing the process parameters.
Claim 8
Dependent Claim
41 words
The method according to claim 1 wherein the surface treatment in the gas plasma is supplemented by a coating process in the gas plasma, including applying a coating material on the substrate by physical processes (so-called physical vapor deposition or PVD).
Claim 9
Dependent Claim
29 words
The method according to claim 7, wherein the physical coating process includes one of the steps of ion plating, cathode sputtering and spark vaporization or any combination of these.
Claim 10
Dependent Claim
34 words
The method according to claim 7, wherein the surface is treated in a first step with nitrogen and a coating of titanium nitride is applied in a second step according to the PVD process.
Claim 11
Dependent Claim
17 words
Method as defined in claim 9, wherein the second step of the process consists of ion plating.
Claim 12
Dependent Claim
41 words
The method according to claim 1 wherein the surface treatment in the gas plasma is supplemented by a coating process in the gas plasma, including applying the coating material on the substrate by chemical processes (so-called chemical vapor deposition or CVD).
Claim 13
Dependent Claim
33 words
The method according to claim 1 wherein the surface treatment in the gas plasma is supplemented by the step of coating utilizing physical processes (PVD) as well as coating utilizing chemical processes (CVD).
Claim 14
Dependent Claim
36 words
The method according to claim 1 further comprising the step of introducing one or several of the following elements: boron, carbon, nitrogen, aluminum, silicon, phosphorus, sulfur, titanium, vanadium, chromium, tin, into the surface of the substrate.
Claim 15
Dependent Claim
20 words
The method according to claim 1 further comprising the step of generating magnetic lines of flux guiding the arc discharge.
Claim 16
Dependent Claim
29 words
The method according to claim 14 wherein the magnetic lines of flux guiding the arc discharge are perpendicular to the flow of the a reactive gas or gas mixture.
Claim 17
Independent Claim
75 words
A method of treating the surface of an article comprising the steps of: positioning the article within a reaction chamber; maintaining a gas pressure in the reaction chamber of less than 10 pascals (Pa) generating a gas plasma in an arc discharge of low voltage having a low current density lying in the range of 10 5 to 7×10 5 A/m 2 and treating the article in the reaction chamber with said reactive gas plasma.
Claim 18
Independent Claim
75 words
A method of treating the surface of an article comprising the steps of: positioning the article within a reaction chamber; maintaining a gas pressure in the reaction chamber of less than 10 pascals (Pa) generating a gas plasma in an arc discharge of low voltage having a low current density lying in the range of 10 5 to 7×10 5 A/m 2 and treating the article in the reaction chamber with said reactive gas plasma.
Claim 19
Dependent Claim
19 words
The method according to claim 16, wherein the pressure lies in the range of 0.06 to 0.6 pascals (Pa).
Claim 20
Dependent Claim
62 words
The method according to claim 16, wherein said step of treating in a gas plasma includes generating the gas plasma in an arc discharge the electrical arc being discharged between a heated, gas-stabilized cathode and a liquid-cooled anode and said step of positioning the article includes positioning the article on a substrate holder located between said gas-stabilized cathode and said liquid-cooled anode.
Claim 21
Dependent Claim
28 words
The method according to claim 16, wherein the arc discharge is used simultaneously to generate the gas plasma and to heat a substrate positioned in the reaction chamber.
Claim 22
Dependent Claim
20 words
The method according to claim 16, further comprising the step of: generating magnetic lines of flux guiding the arc discharge.
Claim 23
Dependent Claim
29 words
The method according to claim 21, wherein the magnetic lines of flux guiding the arc discharge are perpendicular to the flow of the a reactive gas or gas mixture.
Claim 24
Dependent Claim
38 words
The method according to claim 16, wherein said article has at least two different implanted foreign elements, the depth distribution of which differs with respect to the average value, as well as with respect to the standard deviation.
Claim 25
Dependent Claim
42 words
The method according to claim 22 wherein said article originally has two different implanted foreign elements, the average values of the depth distribution of which are inversely proportional to the reaction enthalpy of the element in question with the sub strate material.
Claim 26
Dependent Claim
111 words
A product treated by a process comprising the steps of: positioning the untreated product within a reaction chamber on a substrate; introducing gas into the reaction chamber and maintaining a gas pressure in the reaction chamber of less than 10 (Pa); generating a gas plasma in an arc discharge of low voltage having a low current density lying in the range of 10 5 to 7×10 5 A/m 2 , the gas plasma being generated with an electrical discharged between a heated gas-stabilized cathode and a liquid-cooled anode, said substrate being positioned between the cathode and the anode; and, treating the article in the reaction chamber with said reactive gas plasma.
Claim 27
Dependent Claim
111 words
A product treated by a process comprising the steps of: positioning the untreated product within a reaction chamber on a substrate; introducing gas into the reaction chamber and maintaining a gas pressure in the reaction chamber of less than 10 (Pa); generating a gas plasma in an arc discharge of low voltage having a low current density lying in the range of 10 5 to 7×10 5 A/m 2 , the gas plasma being generated with an electrical discharged between a heated gas-stabilized cathode and a liquid-cooled anode, said substrate being positioned between the cathode and the anode; and, treating the article in the reaction chamber with said reactive gas plasma.
Claim 28
Dependent Claim
33 words
The product-by-process according to claim 24, further comprising the steps of: generating magnetic lines of flux guiding the arc discharge for treating the article in the reaction chamber with said reactive gas plasma.
Claim 29
Dependent Claim
25 words
The product-by-process according to claim 25, wherein the magnetic lines of flux guiding the arc discharge are transverse to the flow of the reactive gas.
Claim 30
Dependent Claim
38 words
The product-by-process according to claim 24, wherein said article has at least two different implanted foreign elements, the depth distribution of which differs with respect to the average value, as well as with respect to the standard deviation.
Claim 31
Dependent Claim
41 words
The product-by-process according to claim 24, wherein: said article originally has two different implanted foreign elements, the average values of the depth distribution of which are inversely proportional to the reaction enthalpy of the element in question with the substrate material.
References Cited (Backward Citations)
US4645895A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-09 | 1992-02-08 | 1992-08-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-09 | 1996-02-08 | 1996-08-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-09 | 2000-02-08 | 2000-08-09 | $7700.00 | Window Closed / Lapsed |