Plastic optical fibers
Assignee: Mitsubishi Chemical Corp
•
Filing: 1985-05-29
•
Granted: 1988-08-09
•
Expires: 2005-05-29
Abstract
Abstract PCT No. PCT/JP85/00294 Sec. 371 Date Jan. 28, 1986 Sec. 102(e) Date Jan. 28, 1986 PCT Filed May 29, 1985 PCT Pub. No. WO85/05699 PCT Pub. Date Dec. 19, 1985.There is provided a plastic optical fiber capable of exhibiting good light transmitting characteristics even at high temperatures, which comprises a core layer, a cladding layer, and a protective layer as basic consititutional units, wherein the protective layer has a heat distortion temperature [HDT] of at least 120 DEG C., a thickness of at least 10 mu m, and a cross-sectional area of at least 0.07 times the sum of cross-sectional areas of the core and cladding layers. There is also provided such a plastic optical fiber good in high-temperature light transmitting characteristics, which comprises a core layer, a cladding layer, and a protective layer as basic constitutional units and has a plastic coating layer having a silane-crosslinked structure provided as an outer layer thereof, wherein the protective layer has a heat distortion temperature [HDT] of at least 120 DEG C., a thickness of at least 10 mu m, and a cross-sectional area of at least 0.07 times the sum of cross-sectional areas of the core and cladding layers.
Inventors
- 👤 Takashi Yamamoto
- 👤 Ryuji Murata
- 👤 Yasuteru Tahara
- 👤 Hiromu Terada
- 👤 Kenichi Sakunaga
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 19:16
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/44; G02B6/4401; G02B6/4429; G02B6/443; G02B6/02; G02B6/02033; G02B6/4436; B; B29; B29C; B29C48/00; B29C48/03; B29C48/05; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2938; Y10T428/2962; Y10T428/2964; Y10T428/2967
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
64 words
A plastic optical fiber comprising a core layer, a cladding layer, and a protective layer as basic constitutional units, characterized in that the protective layer has a heat distortion temperature [HDT] of at least 120° C., a thickness of at least 10 μm, and a cross-sectional area of at least 0.07 times the sum of the cross-sectional areas of the core and cladding layers.
Claim 2
Dependent Claim
64 words
A plastic optical fiber comprising a core layer, a cladding layer, and a protective layer as basic constitutional units, characterized in that the protective layer has a heat distortion temperature [HDT] of at least 120° C., a thickness of at least 10 μm, and a cross-sectional area of at least 0.07 times the sum of the cross-sectional areas of the core and cladding layers.
Claim 3
Dependent Claim
32 words
The plastic optical fiber of claim 1, wherein the cross-sectional area of the protective layer is from 0.07 to 100 times the sum of cross-sectional areas of the core and cladding layers.
Claim 4
Dependent Claim
64 words
The plastic optical fiber of claim 1, wherein the relation between the melt flow rate [MFR] 3 of the protective layer polymer and the melt flow rate [MFR] 1 of the core layer polymer is represented by [MFR] 1 ≦[MFR] 3 , wherein both the melt flow rates are measured under the same conditions of test temperature 230° C. and test load 5 kg.
Claim 5
Dependent Claim
65 words
The plastic optical fiber of claim 1, wherein the relation between the melt flow rate [MFR] 1 of the core layer polymer and the melt flow rate [MFR] 2 of the cladding layer polymer is represented by [MFR] 1 ≦[MFR] 2 ≦40 g/10 min, where both the melt flow rates are measured under the conditions of test temperature 230° C. and test load 5 kg.
Claim 6
Dependent Claim
29 words
The plastic optical fiber of claim 1, wherein a primary coating or primary and secondary coatings forming the protective layer comprise an ethylenic polymer, said polymer being water proof.
Claim 7
Dependent Claim
27 words
The plastic optical fiber of claim 1, wherein the thermal shrinkage of a secondary coating material forming the protective layer is up to 10% at 100° C.
Claim 8
Dependent Claim
27 words
The plastic optical fiber of claim 1, wherein the thermal shrinkage of a primary coating material forming the protective layer is up to 10% at 100° C.
Claim 9
Dependent Claim
84 words
The plastic optical fiber of claim 1, wherein the protective layer is constituted by a primary coating consisting of a material having a flexural elastic modulus ε 1 (kg/cm 2 ) and a cross-sectional area A 1 (cm 2 ) and a secondary coating consisting of a material having a flexural elastic modulus ε 2 (kg/cm 2 ) and a cross-sectional area A 2 (cm 2 ), and these materials of the primary and secondary coatings are organic polymers satisfying ε.sub.1 A.sub.1 ≦ε.sub.2 A.sub.2.
Claim 10
Dependent Claim
37 words
The plastic optical fiber of claim 1, wherein the protective layer consists of either a polymer comprised substantially of 4-methylpentene-1 units or a polycarbonate exhibiting an intrinsic viscosity (in methylene chloride, at 20° C.) of 0.4-0.8 dl/g.
Claim 11
Dependent Claim
68 words
The plastic optical fiber of claim 8, wherein the flexural elastic modulus ε 0 (kg/cm 2 ) of the polymer forming the core, the flexural elastic modulus ε 1 (kg/cm 2 ) of the polymer forming the primary coating, and the flexural elastic modulus ε 2 (kg/cm 2 ) of the polymer forming the secondary coating satisfy the following conditions: ε.sub.1 ≦ε.sub.2 1×10.sup.2 ≦ε.sub.1 ≦ε.sub.0 1×10.sup.2 ≦ε.sub.2 ≦5×10.sup.4
Claim 12
Dependent Claim
80 words
The plastic optical fiber of claim 9, wherein the melt flow rate [MFR] 1 of the core layer polymer measured under the conditions of test temperature 230° C. and test load 5 kg and the melt flow rate [MFR] 2 of the cladding layer polymer measured under the same conditions satisfy the relation [MFR].sub.1 ≦[MFR].sub.2 ≦40 g/10 min , and the protective layer consists of an organic polymer having a flexural elastic modulus of up to 5,000 kg/cm 2 .
Claim 13
Dependent Claim
20 words
The plastic optical fiber of claim 1, wherein the thickness of the protective layer is from 10 to 250 μm.
Claim 14
Dependent Claim
50 words
The plastic optical fiber of claim 9, wherein the core layer consists of a transparent methacrylic polymer containing at least 70% by weight of methyl methacrylate units, and the cladding layer consists of a substantially transparent fluorine-containing polymer having a refractive index 0.01% lower than that of the core layer.
Claim 15
Dependent Claim
45 words
The plastic optical fiber of claim 9, wherein the polymer forming the cladding layer contains monomer units represented by the general formula: ##STR6## wherein R represents a C 1 -C 5 alkyl, fluorinated C 1 -C 5 alkyl, or C 3 -C 6 cycloalkyl group.
Claim 16
Dependent Claim
21 words
The plastic optical fiber of claim 1, the core-cladding structure of which is formed at a spinning temperature of 240°-270° C.
Claim 17
Dependent Claim
38 words
The plastic optical fiber of claim 1, the shrinkage of said fiber being not more than 5% when said fiber is subjected to wet heat treatment for 24 hours under the conditions of 90° C. and 95% RH.
Claim 18
Dependent Claim
32 words
The plastic optical fiber of claim 1, the shrinkage of said fiber being not more than 5% when said fiber is subjected to dry heat treatment at 120° C. for 24 hours.
Claim 19
Dependent Claim
32 words
The plastic optical fiber of claim 1, the shrinkage of said fiber being not more than 5%, when said fiber is subjected to dry heat treatment at 130° C. for 24 hours.
Claim 20
Dependent Claim
35 words
The plastic optical fiber of claim 1, the shrinkage of said fiber being not more than 5% when said fiber is subjected to wet heat treatment in boiling water at 100° C. for 24 hours.
Claim 21
Dependent Claim
82 words
A plastic optical fiber comprising a core layer, a cladding layer, and a protective layer as basic constitutional units, characterized in that a plastics coating layer having a silane-crosslinked structure is provided as an outer layer of the fiber, and that the protective layer has a heat distortion temperature [HDT] of at least 120° C., a thickness of at least 10 μm, and a cross-sectional area of at least 0.07 times the sum of cross-sectional areas of the core and cladding layers.
Claim 22
Dependent Claim
82 words
A plastic optical fiber comprising a core layer, a cladding layer, and a protective layer as basic constitutional units, characterized in that a plastics coating layer having a silane-crosslinked structure is provided as an outer layer of the fiber, and that the protective layer has a heat distortion temperature [HDT] of at least 120° C., a thickness of at least 10 μm, and a cross-sectional area of at least 0.07 times the sum of cross-sectional areas of the core and cladding layers.
Claim 23
Dependent Claim
64 words
The plastic optical fiber of claim 20, wherein the relation between the melt flow rate [MFR] 3 of the protective layer polymer and the melt flow rate [MFR] 1 of the core layer polymer is represented by [MFR] 1 ≦[MFR] 3 , where both the melt flow rates are measured under the same conditions of test temperature 230° C. and test load 5 kg.
Claim 24
Dependent Claim
65 words
The plastic optical fiber of claim 20, wherein the relation between the melt flow rate [MFR] 1 of the core layer polymer and the melt flow rate [MFR] 2 of the cladding layer polymer is represented by [MFR] 1 ≦[MFR] 2 ≦40 g/10 min, where both the melt flow rates are measured under the conditions of test temperature 230° C. and test load 5 kg.
Claim 25
Dependent Claim
89 words
The plastic optical fiber of claim 20, wherein the protective layer is constituted by a primary coating consisting of a material having a flexural elastic modulus ε 1 (kg/cm 2 ) and a cross-sectional area A 1 (cm 2 ) and a secondary coating consisting of a material having a flexural elastic modulus ε 2 (kg/cm 2 ) and a cross-sectional area A 2 (cm 2 ), and these materials of the primary and secondary coatings are organic polymers satisfying ε 1 A 1 ≦ε 2 A 2 .
Claim 26
Dependent Claim
37 words
The plastic optical fiber of claim 20, wherein the protective layer consists of either a polymer comprised mainly of 4-methylpentene-1 units or a polycarbonate exhibiting an intrinsic viscosity (in methylene chloride, at 20° C.) of 0.4-0.8 dl/g.
Claim 27
Dependent Claim
68 words
The plastic optical fiber of claim 24, wherein the flexural elastic modulus ε 0 (kg/cm 2 ) of the polymer forming the core, the flexural elastic modulus ε 1 (kg/cm 2 ) of the polymer forming the primary coating, and the flexural elastic modulus ε 2 (kg/cm 2 ) of the polymer forming the secondary coating satisfy the following conditions: ε.sub.1 ≦ε.sub.2 1×10.sup.2 ≦ε.sub.1 ≦ε.sub.0 1×10.sup.2 ≦ε.sub.2 ≦5×10.sup.4.
Claim 28
Dependent Claim
80 words
The plastic optical fiber of claim 20, wherein the melt flow rate [MFR] 1 of the core layer polymer measured under the conditions of test temperature 230° C. and test load 5 kg and the melt flow rate [MFR] 2 of the cladding layer polymer measured under the same conditions satisfy the relation: [MFR].sub.1 ≦[MFR].sub.2 ≦40 g/10 min , and the protective layer consists of an organic polymer having a flexural elastic modulus of up to 5,000 kg/cm 2 .
Claim 29
Dependent Claim
50 words
The plastic optical fiber of claim 20, wherein the core layer consists of a transparent methacrylic polymer containing at least 70% by weight of methyl methacrylate units and the cladding layer consists of a substantially transparent fluorine-containing polymer having a refractive index 0.01% lower than that of the core layer.
Claim 30
Dependent Claim
46 words
The plastic optical fiber of claim 20, wherein the polymer forming the cladding layer contains monomer units represented by the general formula: ##STR7## , wherein R represents a C 1 -C 5 alkyl, fluorinated C 1 -C 5 alkyl, or C 3 -C 6 cycloalkyl group.
Claim 31
Dependent Claim
49 words
The plastic optical fiber of claim 27, wherein, in the plastic coating layer having a silane-crosslinked structure, the silane crosslinkage structure comprises Si--O--Si-- and the plastic structure is comprised of an organic polymer selected from polyethylene, chlorinated polyethylene, ethylene-propylene copolymer, ethylene-vinyl acetate copolymer, ethylene-ethyl acrylate copolymer, and tetrafluoroethylene-propylene copolymer.
Claim 32
Dependent Claim
67 words
The plastic optical fiber of claim 27, wherein the protective layer is comprised of at least one organic material selected from the group consisting of polyolefins such as polyethylene, ethylenic copolymeric ionomer, polypropylene, and poly(4-methylpentene-1); halogen-containing polymers such as polyvinylidene fluoride, vinylidene fluoride copolymer, polytetrafluoro ethylene, tetrafluoro ethylene copolymer, polyvinyl chloride, and polyvinylidene chloride; and resins such as polyester, polyamide, polycarbonate, polyacetal, ABS resin, and SBR resin.
Claim 33
Dependent Claim
32 words
The plastic optical fiber of claim 20, the shrinkage of said fiber being not more than 5% when said fiber is subjected to dry heat treatment at 120? C. for 24 hours.
Claim 34
Dependent Claim
32 words
The plastic optical fiber of claim 25, the shrinkage of said fiber being not more than 5% when said fiber is subjected to dry heat treatment at 130? C. for 24 hours.
Claim 35
Dependent Claim
35 words
The plastic optical fiber of claim 25, the shrinkage of said fiber being not more than 5% when said fiber is subjected to wet heat treatment in boiling water at 100? C. for 24 hours.
References Cited (Backward Citations)
US3930103A
Cited
US3993834A
Cited
US3980390A
Cited
US4147407A
Cited
US4114981A
Cited
US4138194A
Cited
US4381269A
Cited
US4681400A
Cited
US4505543A
Cited
JPS5869805U
Cited
US4642265A
Cited
US4544235A
Cited
US4482205A
Cited
US4593974A
Cited
US4547040A
Cited
US4693553A
Cited
JPS60247605A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-09 | 1992-02-08 | 1992-08-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-09 | 1996-02-08 | 1996-08-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-09 | 2000-02-08 | 2000-08-09 | $7700.00 | Window Closed / Lapsed |