Temperature-insensitive optical fibers
Assignee: United States Department of the Navy
•
Filing: 1982-10-01
•
Granted: 1984-11-13
•
Expires: 2002-10-01
Abstract
Abstract A temperature-insensitive fiber comprises a lightpropagating core having <IMAGE> not in excess of 5.5x10-6K-1, wherein n represents the refractive index, T represents the temperature, and rho represents the density of the core material, a cladding layer on the core with a Poisson ratio about equal to that of the core; a substrate layer on the cladding layer having a Young's modulus greater than that of the core, a Poisson ratio about equal to that of the core, thermal expansion co-efficient not more than one fourth of that of the core, and a thickness of at least five times greater than the radius of the core; and an elastomeric protective layer on the substrate layer.
Inventors
- 👤 Nicholas Lagakos
- 👤 Joseph A. Bucaro
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 23:18
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/44; G02B6/4439; G02B6/02; G02B6/02395
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
200 words
An optical fiber with reduced temperature sensitivity which comprises: a light-propagating core having the factor ##EQU3## less than 5.5×10 -6 K -1 wherein n represents the index of refraction, T represents the temperature, and ρ represents the density of said core; a cladding layer in contact with said core having an index of refraction lower than that of said core, a Young's modulus at least about equal to that of said core, a Poisson's ratio about equal to that of said core, and a thickness equal to at least about one-half of the radius of said core; a substrate layer in contact with said cladding layer having a Young's modulus greater than that of said core, a Poisson ratio within about 25 percent of that of said core, a thickness at least about one and one-half times greater than the radius of said core, and a coefficient of thermal expansion of not more than one fourth of that of said core; and at least one protective coating layer in contact with said substrate layer having a Young's modulus not in excess of about 1×10 -3 times that of said core and a Poisson ratio from about 0.48 to about 0.52.
Claim 2
Dependent Claim
200 words
An optical fiber with reduced temperature sensitivity which comprises: a light-propagating core having the factor ##EQU3## less than 5.5×10 -6 K -1 wherein n represents the index of refraction, T represents the temperature, and ρ represents the density of said core; a cladding layer in contact with said core having an index of refraction lower than that of said core, a Young's modulus at least about equal to that of said core, a Poisson's ratio about equal to that of said core, and a thickness equal to at least about one-half of the radius of said core; a substrate layer in contact with said cladding layer having a Young's modulus greater than that of said core, a Poisson ratio within about 25 percent of that of said core, a thickness at least about one and one-half times greater than the radius of said core, and a coefficient of thermal expansion of not more than one fourth of that of said core; and at least one protective coating layer in contact with said substrate layer having a Young's modulus not in excess of about 1×10 -3 times that of said core and a Poisson ratio from about 0.48 to about 0.52.
Claim 3
Dependent Claim
45 words
The fiber of claim 1 wherein the thickness of said cladding layer is from one half to five times the radius of said core and the coefficient of thermal expansion of said substrate layer is no more than one tenth of that of said core.
Claim 4
Dependent Claim
42 words
The fiber of claim 2 wherein the Young's moduli of said protective coatings are not greater than 1×10 -4 times that of said core and the total thickness of said protective coatings is at least five times the radius of said core.
Claim 5
Dependent Claim
63 words
The fiber of claim 3 wherein the Young's moduli of said protective coatings are not greater than 1×10 -6 times that of said core, the total thickness of said protective coatings is at least ten times the radius of said core, and the coefficient of thermal expansion of said substrate layer is no more than one twenty fifth of that of said core.
Claim 6
Dependent Claim
102 words
The fiber of claim 4 wherein said core consists essentially of a glass selected from the group consisting of boron oxide, borosilicate glass having at least about 20 weight percent of boron oxide, barium borate glass having from about 30 to about 50 weight percent of barium oxide, silica phosphate glass having at least about 30 weight percent of P 2 O 5 , glasses consisting essentially of barium borate and boron oxide, glasses having at least about 50 weight percent barium borate, boron oxide or both and at least two from the group consisting of aluminum, sodium oxide, and potassium oxide.
Claim 7
Dependent Claim
46 words
The fiber of claim 4 wherein said core consists essentially of a glass selected from the groups consisting of boron oxide, borosilicate glass having at least 30 weight percent of boron oxide, and barium borate glass having from 35 to 45 weight percent of barium oxide.
Claim 8
Dependent Claim
63 words
The fiber of claim 4 wherein said core consists of a glass comprising 63 to 68 weight percent of SiO 2 , 3 to 4 weight percent of NaO, 1 to 2 weight percent of PbO, 3 to 4 weight percent of BaO, 3.5 weight percent of Nd 2 O 3 and 3 to 4 weight percent of Sb 2 O 3 .
Claim 9
Dependent Claim
45 words
The fiber of claim 1 wherein the thickness of said cladding layer is at least equal to fifteen times the radius of said core and the coefficient of thermal expansion of said substrate layer is no more than one tenth of that of said core.
Claim 10
Dependent Claim
42 words
The fiber of claim 8 wherein the Young's moduli of said protective coatings are not greater than 1×10 -4 times that of said core and the total thickness of said protective coatings is at least five times the radius of said core.
Claim 11
Dependent Claim
62 words
The fiber of claim 9 wherein the Young's moduli of said protective coatings are not greater than 1×10 -6 times that of said core, the total thickness of said protective coatings is at least ten times that of said core, and the coefficient of thermal expansion of said substrate layer is no more than one twenty fifth of that of said core.
Claim 12
Dependent Claim
102 words
The fiber of claim 10 wherein said core consists essentially of a glass selected from the group consisting of boron oxide, borosilicate glass having at least about 20 weight percent of boron oxide, barium borate glass having from about 30 to about 50 weight percent of barium oxide, silica phosphate glass having at least about 30 weight percent of P 2 O 5 , glasses consisting essentially of barium borate and boron oxide, glasses having at least about 50 weight percent barium borate, boron oxide or both and at least two from the group consisting of aluminum, sodium oxide, and potassium oxide.
Claim 13
Dependent Claim
46 words
The fiber of claim 10 wherein said core consists essentially of a glass selected from the group consisting of boron oxide, borosilicate glass having at least 30 weight percent of boron oxide, and barium borate glass having from 35 to 45 weight percent of barium oxide.
Claim 14
Dependent Claim
63 words
The fiber of claim 10 wherein said core consists of a glass comprising 63 to 68 weight percent of SiO 2 , 3 to 4 weight percent of NaO, 1 to 2 weight percent of PbO, 3 to 4 weight percent of BaO, 3.5 weight percent of Nd 2 O 3 and 3 to 4 weight percent of Sb 2 O 3 .
References Cited (Backward Citations)
US4089586A
Cited
US4213672A
Cited
US4295739A
Cited
US4373768A
Cited
US4417782A
Cited
US4265667A
Cited
US4432606A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-13 | 1988-05-14 | 1988-11-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-13 | 1992-05-14 | 1992-11-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-13 | 1996-05-14 | 1996-11-13 | $7700.00 | Window Closed / Lapsed |