Porous metal structures made by thermal spraying fugitive material and metal
Assignee: RTX Corp
•
Filing: 1985-05-20
•
Granted: 1988-07-26
•
Expires: 2005-05-20
Abstract
Abstract Porous metal deposits especially useful in gas turbine engines as compressor seals are made by thermal spraying a metal powder and a meltable polymer powder mixture, wherein the spraying process and a subsequent polymer removal process are chosen to produce less than 30 weight percent oxide. Oxide contents of 4-25% are typical. When 86 weight percent nichrome is sprayed with 14 weight percent polymethylmethacrylate the polymer is removed by heating in air to about 315° C. The resultant porous structure will have an oxide content of 7% and an apparent density of about 32%. A meltable polymer additionally produces a more desirable pore structure.
Inventors
- 👤 Harry E. Eaton
- 👤 Richard C. Novak
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:00
CPC Classifications
C; C23; C23C; C23C4/00; C23C4/04; C23C4/18; F; F01; F01D; F01D11/00; F01D11/08; F01D11/12; F01D11/122
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
107 words
The method of making a porous metal structure which comprises thermal spraying a mixture of metal powder and polymer powder onto a substrate to first form a sprayed deposit and then heating the deposit to cause the polymer to flee from the deposit, characterized by using a polymer powder which becomes molten and spherical in shape during spraying and which by virtue of its melted shape thereby produces in the metal structure a desirable pore shape; and, endothermically decomposing the polymer by heating the sprayed deposit to a temperature of less than 540° C., to produce less than 30 weight percent oxide content in the remaining deposit.
Claim 2
Independent Claim
107 words
The method of making a porous metal structure which comprises thermal spraying a mixture of metal powder and polymer powder onto a substrate to first form a sprayed deposit and then heating the deposit to cause the polymer to flee from the deposit, characterized by using a polymer powder which becomes molten and spherical in shape during spraying and which by virtue of its melted shape thereby produces in the metal structure a desirable pore shape; and, endothermically decomposing the polymer by heating the sprayed deposit to a temperature of less than 540° C., to produce less than 30 weight percent oxide content in the remaining deposit.
Claim 3
Dependent Claim
14 words
The method of claim 1 wherein the heating takes place in an oxidizing environment.
Claim 4
Dependent Claim
20 words
The method of claim 1 wherein the polymer is selected from the group consisting of polystrenes, polyethylenes, polypropylenes and polyacrylates.
Claim 5
Dependent Claim
10 words
The method of claim 3 wherein the polymer is polymethylmethacrylate.
Claim 6
Dependent Claim
35 words
The method of claim 3 wherein the Tyler Sieve Series Mesh size of the metal powder is between 250 and 500 mesh and the size of the polymer powder is between 80 and 400 mesh.
Claim 7
Dependent Claim
48 words
The method of claim 1 wherein the porous metal structure is deposited on a metal substrate in the shape of a seal for a gas turbine engine and wherein the porous metal structure does not glaze when rubbed by a titanium alloy blade moving at about 290 m/s.
Claim 8
Dependent Claim
15 words
The method of claim 1, wherein the heating is to a temperature of 250°-430° C.
Claim 9
Dependent Claim
19 words
The method of claim 1, wherein the sprayed deposit is comprised of about 35 to 45 volume percent polymer.
Claim 10
Dependent Claim
12 words
The method of claim 1, wherein the volume percent polymer is 37-43.
Claim 11
Independent Claim
119 words
The method of making a porous metal structure for use as a seal in a gas turbine engine which comprises thermal spraying a mixture of nickel alloy metal powder and polymer powder onto a substrate to first form a sprayed deposit and then heating the deposit to cause the polymer to flee from the deposit, characterized by spraying polyacrylate polymer powder as spherical molten droplets together with the metal to form a sprayed deposit comprised of 35-45 volume percent polymer; and endothermically decomposing the polymer by heating the sprayed deposit to a temperature of less than 540° C. in air, to thereby produce a porous metal structure having a desirable pore shape and less than 30 weight percent oxide.
Claim 12
Independent Claim
119 words
The method of making a porous metal structure for use as a seal in a gas turbine engine which comprises thermal spraying a mixture of nickel alloy metal powder and polymer powder onto a substrate to first form a sprayed deposit and then heating the deposit to cause the polymer to flee from the deposit, characterized by spraying polyacrylate polymer powder as spherical molten droplets together with the metal to form a sprayed deposit comprised of 35-45 volume percent polymer; and endothermically decomposing the polymer by heating the sprayed deposit to a temperature of less than 540° C. in air, to thereby produce a porous metal structure having a desirable pore shape and less than 30 weight percent oxide.
References Cited (Backward Citations)
US2718473A
Cited
US3350178A
Cited
US3540884A
Cited
US3723165A
Cited
US4025669A
Cited
US4269903A
Cited
US4336276A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-07-26 | 1992-01-25 | 1992-07-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-07-26 | 1996-01-25 | 1996-07-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-07-26 | 2000-01-25 | 2000-07-26 | $7700.00 | Window Closed / Lapsed |