Abstract A device header with a multilayer coating overlying its entire surface, and a method of making said header, are disclosed. The multilayer coating comprises an electrolytic nickel layer and a gold layer in the device mounting area of the header, whereas the rest of the header is coated with electroless nickel, a first gold layer, electrolytic nickel, and a second gold layer. In the fabrication, the electroless nickel layer is deposited over the entire header followed by the first gold layer. Upon removing these layers from the device mounting area, the first gold layer remaining on the rest of the header acts as a mask for the etching of the mounting area preparatory to deposition of electrolytic nickel and the second gold layer. The header has the advantage of the excellent coverage of electroless nickel over most of its surface, but with the advantage of high purity electrolytic nickel in the device mounting area.
A method for fabricating a header which includes a steel base plate with a copper or copper alloy heatsink affixed to a major surface of said base plate, said heatsink having a device mounting area thereon, said method comprising depositing electroless nickel onto the entire header; depositing a first layer of gold over said electroless nickel; removing said electroless nickel layer and said first gold layer in the device mounting area; chemically cleaning the exposed copper or copper alloy of said device mounting area; depositing electrolytic nickel onto the entire header; and, depositing a second layer of gold over the electrolytic nickel.
Claim 2
Independent Claim
102 words
A method for fabricating a header which includes a steel base plate with a copper or copper alloy heatsink affixed to a major surface of said base plate, said heatsink having a device mounting area thereon, said method comprising depositing electroless nickel onto the entire header; depositing a first layer of gold over said electroless nickel; removing said electroless nickel layer and said first gold layer in the device mounting area; chemically cleaning the exposed copper or copper alloy of said device mounting area; depositing electrolytic nickel onto the entire header; and, depositing a second layer of gold over the electrolytic nickel.
Claim 3
Dependent Claim
46 words
The method of claim 1 wherein the exposed copper or copper alloy of said device mounting area is cleaned with a solution comprising from about 60 to 70 percent by volume of nitric acid and from about 30 to 40 percent by volume of sulfuric acid.
Claim 4
Dependent Claim
26 words
The method of claim 1 wherein said layer of electrolytic nickel is of a thickness sufficient to prevent diffusion of the copper or copper alloy therethrough.
Claim 5
Dependent Claim
22 words
The method of claim 3 wherein said layer of electrolytic nickel is from about 0.5 micrometers to about 5.0 micrometers in thickness.
Claim 6
Dependent Claim
19 words
The method of claim 4 wherein said layer of electrolytic nickel is about 1.5 to 2.5 micrometers in thickness.
Claim 7
Dependent Claim
20 words
The method of claim 1 wherein said second layer of gold is of a thickness sufficient for subsequent device mounting.
Claim 8
Dependent Claim
22 words
The method of claim 6 wherein said second layer of gold is from about 2.0 micrometers to about 10 micrometers in thickness.
Claim 9
Dependent Claim
19 words
The method of claim 7 wherein said second layer of gold is about 4.0 to 6.0 micrometers in thickness.