Low thermal expansion ZrTiO4 --Al2 TiO5 --ZrO2 compositions
Assignee: Vibrantz Corp
•
Filing: 1987-08-07
•
Granted: 1988-07-19
•
Expires: 2007-08-07
Abstract
Abstract A low thermal expansion ceramic composition having a predominant Al 2 TiO 5 phase along with zirconium titanate and zirconia phases. The final overall ceramic composition after firing has a low thermal expansion between 24°-1000° C. of not greater than 1.5×10 -6 ° C. -1 and a thermal stability in air such that (a) upon heating to 1200° C. for at least 4 hours there is substantially no decomposition of the Al 2 TiO 5 phase to rutile or alumina as measured by X-ray diffraction, (b) physical growth after thermal cycling between 200° and 1150° C. for 300 cycles does not exceed 1.5%, and (c) the composition maintains a low average thermal expansion between 24°-1000° C. of not greater than 1.5×10 -6 ° C. -1 after the isothermal heating or cycling conditions. The composition is preferably made by forming a mixture of the equivalent of 50-90 volume percent Al 2 TiO 5 or a solid solution having a substantial amount of Al 2 TiO 5 in the solid solution, and zirconium titanate and then heating the mixture at a temperature of 1250° C. or higher.
Inventors
- 👤 Frederick J. Parker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 10:42
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/48; C04B35/49; C04B35/46; C04B35/462; C04B35/478
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
136 words
A ceramic composition comprising a predominant Al 2 TiO 5 phase along with zirconium titanate and zirconia phases where the final overall ceramic composition has a low thermal expansion between 24°-1000° C. of not greater than 1.5×10 -6 ° C. -1 and a thermal stability in air such that (a) upon heating at 1200° C. for at least 4 hours there is substantially no decomposition of the Al 2 TiO 5 phase to rutile or alumina as measured by X-ray diffraction, (b) physical growth after thermal cycling between 200° and 1150° C. for 300 cycles does not exceed 1.5%, and (c) the composition maintains a low average thermal expansion between 24°-1000° C. of not greater than 1.5×10 -6 ° C. -1 after the isothermal heating at 1200° C. for at least 4 hours or cycling conditions.
Claim 2
Dependent Claim
136 words
A ceramic composition comprising a predominant Al 2 TiO 5 phase along with zirconium titanate and zirconia phases where the final overall ceramic composition has a low thermal expansion between 24°-1000° C. of not greater than 1.5×10 -6 ° C. -1 and a thermal stability in air such that (a) upon heating at 1200° C. for at least 4 hours there is substantially no decomposition of the Al 2 TiO 5 phase to rutile or alumina as measured by X-ray diffraction, (b) physical growth after thermal cycling between 200° and 1150° C. for 300 cycles does not exceed 1.5%, and (c) the composition maintains a low average thermal expansion between 24°-1000° C. of not greater than 1.5×10 -6 ° C. -1 after the isothermal heating at 1200° C. for at least 4 hours or cycling conditions.
Claim 3
Dependent Claim
48 words
A ceramic composition according to claim 1, further comprising in solid solution with at least the zirconium titanate or the Al 2 TiO 5 an oxide selected from the group consisting of ZrO 2 , TiO 2 , SiO 2 , Fe 2 O 3 and mixtures thereof.
Claim 4
Dependent Claim
38 words
A ceramic composition according to claim 2, wherein the Al 2 TiO 5 phase contains a phase decomposition stabilizer selected from the group consisting of SiO 2 , ZrO 2 , Fe 2 O 3 or mixtures thereof.
Claim 5
Dependent Claim
33 words
A ceramic composition according to claim 3, wherein the phase decomposition stabilizer oxide is present in an amount of from 1 to 5 mole % of the total Al 2 TiO 5 composition.
Claim 6
Dependent Claim
47 words
A ceramic composition according to claim 1, wherein the composition is made by firing at a temperature of 1250° C. or higher a starting mixture of a source of ZrO 2 , a source of TiO 2 , and a source of Al 2 O 3 .
Claim 7
Dependent Claim
52 words
A ceramic composition according to claim 5, wherein the starting mixture prior to firing comprises at least the equivalent of (a) 50-90 volume percent Al 2 TiO 5 or a solid solution having a substantial amount of Al 2 TiO 5 in the solid solution, and (b) 10-50 volume percent zirconium titanate.
Claim 8
Dependent Claim
35 words
A ceramic composition according to claim 6, wherein the zirconium titanate is in an amount from 10 to 50 volume percent, and has a composition within the range ZrTi 1+x O 4+2x , where 0≦x<1.
Claim 9
Dependent Claim
20 words
A ceramic composition according to claim 7, wherein the starting mixture further comprises a phase of free ZrO 2 .
Claim 10
Dependent Claim
19 words
A ceramic composition according to claim 8, wherein the free ZrO 2 further comprises TiO 2 in solid solution.
Claim 11
Dependent Claim
47 words
Ceramic compositions according to claim 5, wherein the starting mixture before firing comprises at least one pre-reacted phase of Al 2 TiO 5 , zirconium titanate or their solid solutions containing minor amounts of compatible oxides, and the components necessary to form the remaining phases after firing.
Claim 12
Dependent Claim
60 words
A ceramic composition according to claim 5, wherein the starting mixture before firing comprises a mixture of (a) the compound Al 2 TiO 5 or a solid solution of Al 2 TiO 5 containing minor amounts of compatible oxides in solid solution and (b) prereacted zirconium titanate made from about equal molar amounts of ZrO 2 and TiO 2 .
Claim 13
Dependent Claim
27 words
A ceramic composition according to claim 11 wherein the compatible oxide is selected from the group of SiO 2 , Fe 2 O 3 or mixtures thereof.
Claim 14
Dependent Claim
129 words
A method of making a low thermal expansion ceramic composition as defined in claim 1 comprising (1) forming a starting mixture of reactants prior to firing which stoichiometrically will have (a) 50-90 volume percent Al 2 TiO 5 or a solid solution having a substantial amount of Al 2 TiO 5 in the solid solution, and (b) 10-50 volume percent zirconium titanate; said mixture being either (i) prereacted Al 2 TiO 5 and prreacted zirconium titanate, (ii) prereacted Al 2 TiO 5 and sources of TiO 2 and ZrO 2 to form ziroconium titanate, or (iii) prereacted zirconium titanate and sources of Al 2 O 3 and TiO 2 to form Al 2 TiO 5 ; and (2) heating the mixture at a temperature of 1250° C. or higher.
Claim 15
Dependent Claim
34 words
A method according to claim 13, wherein the zirconium titanate is in an amount from 10 to 50 volume percent, and has a composition within the range ZrTi 1+x O 4+2x , where 0≦x<1.
Claim 16
Dependent Claim
16 words
A method according to claim 13, wherein the heating is done in the presence of air.
Claim 17
Dependent Claim
19 words
A method according to claim 14, wherein the starting mixture further comprises a phase of free ZrO 2 .
Claim 18
Dependent Claim
18 words
A method according to claim 16, wherein the free ZrO 2 further comprises TiO 2 in solid solution.
Claim 19
Dependent Claim
49 words
A method of making low thermal expansion ceramic compositions according to claim 13, comprising combining at least one pre-reacted phase of Al 2 TiO 5 and sources of TiO 2 and ZrO 2 to form zirconium titanate, and heating the mixture at a temperature of 1250° C. or higher.
Claim 20
Dependent Claim
51 words
A method of making low thermal expansion ceramic compositions according to claim 13, comprising combining at least one pre-reacted phase of zirconium titanate and sources of Al 2 O 3 and TiO 2 to form Al 2 TiO 5 and heating the mixture at a temperature of 1250° C. or higher.
Claim 21
Dependent Claim
46 words
A method of making low thermal expansion ceramic compositions according to claim 13, comprising combining Al 2 TiO 5 and prereacted zirconium titanate made from about equal amounts of ZrO 2 and TiO 2 and heating the mixture at a temperature of 1250° C. or higher.
Claim 22
Dependent Claim
31 words
A method according to claim 20, further comprising adding to the starting mixture a compatible oxide selected from the group of SiO 2 , Fe 2 O 3 or mixtures thereof.
Claim 23
Dependent Claim
22 words
An extruded catalyst support made of the low thermal expansion ceramic composition according to claim 1 and having good thermal shock resistance.
Claim 24
Dependent Claim
16 words
An extruded catalyst support according to claim 22, wherein the support has a honeycomb cross section.
Claim 25
Dependent Claim
22 words
An extruded catalyst support made of the low thermal expansion ceramic composition according to claim 5 and having good thermal shock resistance.
Claim 26
Dependent Claim
16 words
An extruded catalyst support according to claim 24, wherein the support has a honeycomb cross section.
Claim 27
Dependent Claim
22 words
An extruded catalyst support made of the low thermal expansion ceramic composition according to claim 6 and having good thermal shock resistance.
Claim 28
Dependent Claim
16 words
An extruded catalyst support according to claim 26, wherein the support has a honeycomb cross section.
References Cited (Backward Citations)
US2776896A
Cited
DE1915787A1
Cited
JPS5223113A
Cited
US4126477A
Cited
JPS5563387A
Cited
JPS5562843A
Cited
JPS5562841A
Cited
JPS5562840A
Cited
JPS5562842A
Cited
JPS55121967A
Cited
JPS55121966A
Cited
SU899600A1
Cited
US4327188A
Cited
US4307198A
Cited
US4316964A
Cited
US4483944A
Cited
JPS6046970A
Cited
BE898604R
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-07-19 | 1992-01-18 | 1992-07-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-07-19 | 1996-01-18 | 1996-07-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-07-19 | 2000-01-18 | 2000-07-19 | $7700.00 | Window Closed / Lapsed |