Primer composition for a metallic material and a coating method using the same
Assignee: Nippon Paint Co Ltd
•
Filing: 1986-09-12
•
Granted: 1988-07-12
•
Expires: 2006-09-12
Abstract
Abstract A primer composition for metallic material comprising (a) a urethane epoxy ester resin having primary hydroxyl groups and a number average molecular weight of 6000 to 12,000, (b) a chromate anticorrosive pigment and (c) a polyethylene wax having a density of 0.94 or more, a molecular weight of 1000 to 10,000 and an acid value of 15 or less (KOH mg/g), the pigment volume concentration being 24 to 45% of the total solids of the composition. A chemical pretreatment on various metallic materials for improvements in scratch resistance, corrosion resistance and the like can be obviated by the use of said primer composition.
Inventors
- 👤 Masaaki Takimoto
- 👤 Tamotsu Sobata
- 👤 Shinji Nakano
- 👤 Yuichi Yoshida
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 22:02
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/42; C08G18/4294; C08G18/64; C08G18/6407; C08G18/6415; C08G18/643; C09; C09D; C09D175/00; C09D175/04; C09D5/00; C09D5/08; B; B05; B05D; B05D2202/00; B05D2350/00; B05D2350/20; C08G2150/00; C08G2150/90
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
91 words
A primer composition for metallic material comprising: (a) 25 to 70% by weight of a primary hydroxyl group bearing urethane epoxy ester resin (C) which is obtained by reaction of a primary hydroxyl group bearing epoxy ester resin (A) and a partially blocked polyisocyanate compound (B) so as to give a ratio of primary hydroxyl groups in said (A) to free isocyanate groups in said (B) of 10/1 to 10/8, and whose number average molecular weight is 6000 to 12,000, (b) 25 to 50% by weight of chromate anticorrosive pigment, and
Claim 2
Dependent Claim
91 words
A primer composition for metallic material comprising: (a) 25 to 70% by weight of a primary hydroxyl group bearing urethane epoxy ester resin (C) which is obtained by reaction of a primary hydroxyl group bearing epoxy ester resin (A) and a partially blocked polyisocyanate compound (B) so as to give a ratio of primary hydroxyl groups in said (A) to free isocyanate groups in said (B) of 10/1 to 10/8, and whose number average molecular weight is 6000 to 12,000, (b) 25 to 50% by weight of chromate anticorrosive pigment, and
Claim 3
Dependent Claim
69 words
(c) 1 to 10% by weight of polyethylene wax having a density of 0.94 or more, a molecular weight of 1000 to 10,000 and an acid value of 15 or less as KOH mg/g, the composition having a pigment volume concentration of 25 to 45% of the total solid matter of the composition, all weight percentages being based on the weight of the total solid matter of the composition.
Claim 4
Dependent Claim
69 words
(c) 1 to 10% by weight of polyethylene wax having a density of 0.94 or more, a molecular weight of 1000 to 10,000 and an acid value of 15 or less as KOH mg/g, the composition having a pigment volume concentration of 25 to 45% of the total solid matter of the composition, all weight percentages being based on the weight of the total solid matter of the composition.
Claim 5
Dependent Claim
83 words
A composition according to claim 1, wherein the primary hydroxyl group bearing epoxy ester resin (A) is a reaction product of: (a 1 ) an epoxy resin having a phenol content of 50% or more and an epoxy equivalent of 100 to 6000 which is selected from the group consisting of a bisphenol epoxy resin, a resorcinol epoxy resin and a mixture thereof, (a 2 ) a dicarboxylic acid, and (a 3 ) a secondary amine having at least one primary hydroxyl group.
Claim 6
Dependent Claim
105 words
A composition according to claim 1, wherein the primary hydroxyl group bearing epoxy ester resin (A) is a reaction product of: (a 1 ) an epoxy resin having a phenol content of 50% or more and an epoxy equivalent of 100 to 6000 which is selected from the group consisting of a bisphenol epoxy resin, a resorcinol epoxy resin and a mixture thereof, (a 2 ) a dicarboxylic acid, (a 3 ) a secondary amine having at least one primary hydroxyl group, and (a 4 ) a cyclic ester compound represented by the formula: ##STR7## in which n is an integer of 4 to 10.
Claim 7
Dependent Claim
102 words
A composition according to claim 1, wherein the primary hydroxyl group bearing epoxy ester resin (A) is a reaction product of: (a 1 ) an epoxy resin having a phenol content of 50% or more and an epoxy equivalent of 100 to 6000 which is selected from the group consisting of a bisphenol epoxy resin, a resorcinol epoxy resin and a mixture thereof, (a 2 ) a dicarboxylic acid, (a 3 )' a tertiary amine or an ammonium compound, and (a 4 ) a cyclic ester compound represented by the formula: ##STR8## in which n is an integer of 4 to 10.
Claim 8
Dependent Claim
53 words
A composition according to claim 1, wherein the partially blocked polyisocyanate compound (B) is a reaction product of: (b 1 ) a polyisocyanate compound, and (b 2 ) an isocyanate blocking agent, the ratio of isocyanate groups in (b 1 ) to active hydrogen atoms in (b 2 ) being 5/1 to 5/4.
Claim 9
Dependent Claim
29 words
A composition according to claim 1, wherein the chromate anticorrosive pigment is strontium chromate pigment or a mixture of strontium chromate pigment and less than 50% calcium chromate pigment.
Claim 10
Dependent Claim
19 words
A composition according to claim 1, wherein a pH controlling pigment is included together with the chromate anticorrosive pigment.
Claim 11
Dependent Claim
33 words
A composition according to claim 7, wherein the pH controlling pigment is a pigment whose solubility in water is 0.001 to 5% and whose pH is a brine suspension is 6 to 11.
Claim 12
Dependent Claim
18 words
A composition according to claim 8, wherein the pH controlling pigment is calcium carbonate or dihydrogen aluminium tripolyphosphate.
Claim 13
Dependent Claim
61 words
A composition according to claim 1, wherein up to 40% by weight of said urethane epoxy resin (C) is replaced by a resol phenol resin of the formula: ##STR9## in which n is 0 or an integer of 1 to 4; W is --CH 2 -- or --CH 2 --O--CH 2 --; and R is CH 3 , H or ##STR10##
Claim 14
Dependent Claim
31 words
A method for coating a metallic material comprising applying the coating composition of claim 1 onto a metallic material, baking and drying the coating, and then applying a top coat thereon.
Claim 15
Dependent Claim
23 words
A method according to claim 11 wherein the metallic material is a galvanized iron or an aluminium containing hot dipped galvanized sheet steel.
Claim 16
Dependent Claim
24 words
A method according to claim 11 wherein the metallic material is previously washed with an aqueous alkaline solution, washed with water and then dried.
Claim 17
Dependent Claim
32 words
A method according to claim 13 wherein the alkaline solution is an aqueous solution of at least one alkali selected from the group consisting of alkali silicates, alkali carbonates and alkali phoshates.
Claim 18
Dependent Claim
24 words
A method according to claim 11 wherein the metallic material is previously treated with an aqueous acidic solution containing chromic acid and then dried.
References Cited (Backward Citations)
CA640547A
Cited
US3954693A
Cited
US3992358A
Cited
US4042550A
Cited
US4542070A
Cited
US4433014A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-07-12 | 1992-01-11 | 1992-07-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-07-12 | 1996-01-11 | 1996-07-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-07-12 | 2000-01-11 | 2000-07-12 | $7700.00 | Window Closed / Lapsed |