Plasma and ion plating treatment of polymer fibers to improve adhesion to RFL rubber
Assignee: Teijin Ltd
•
Filing: 1987-03-20
•
Granted: 1988-07-12
•
Expires: 2007-03-20
Abstract
Abstract A modified fibrous material useful as a reinforcing material for rubber articles is produced by applying a cold plasma treatment to a fibrous material comprising at least one type of synthetic fibers selected from aromatic polyamide fibers and polyester fibers under a reduced pressure; by applying an ion-plating treatment with a polyamide vapor to the resultant cold plasma-treated fibrous material under a reduced pressure; by impregnating the resultant ion-plated fibrous material with an RFL adhesive composition comprising a resorcinol-formaldehye precondensation product and a rubber latex; and by curing the adhesive composition in the fibrous material.
Inventors
- 👤 Masashi Furukawa
- 👤 Tadahiko Takata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 14:19
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/04; C08J5/06; D; D06; D06M; D06M10/00; D06M10/04; D06M10/08; D06M10/10; C08J2321/00; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2964; Y10T428/2967; Y10T428/2969
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
104 words
A process for producing a modified fibrous material useful for reinforcing rubber articles, comprising the steps of: applying a cold plasma treatment to a fibrous material comprising at least one type of synthetic fibers selected from aromatic polyamide fibers and polyester fibers, under a reduced pressure; applying an ion-plating treatment with a polyamide vapor to the resultant cold plasma-treated fibrous material under a reduced pressure to an extent such that the resultant ion-plated polyamide layer has a thickness of from 0.05 to 1 μm; and impregnating the resultant ion-plated fibrous material with an adhesive composition comprising a resorcinol-formaldehyde precondensation product and a rubber latex.
Claim 2
Dependent Claim
104 words
A process for producing a modified fibrous material useful for reinforcing rubber articles, comprising the steps of: applying a cold plasma treatment to a fibrous material comprising at least one type of synthetic fibers selected from aromatic polyamide fibers and polyester fibers, under a reduced pressure; applying an ion-plating treatment with a polyamide vapor to the resultant cold plasma-treated fibrous material under a reduced pressure to an extent such that the resultant ion-plated polyamide layer has a thickness of from 0.05 to 1 μm; and impregnating the resultant ion-plated fibrous material with an adhesive composition comprising a resorcinol-formaldehyde precondensation product and a rubber latex.
Claim 3
Dependent Claim
25 words
The process as claimed in claim 1, wherein the aromatic polyamide fibers in the fibrous material are selected from poly-p-phenylene terephthalamide fibers and poly-p-benzamide fibers.
Claim 4
Dependent Claim
152 words
The process as claimed in claim 1, wherein the aromatic polyamide fibers in the fibrous material comprises an aromatic polyetheramide having repeating units of the formulae (I), (II), (IV), and optionally, (III): ##STR2## wherein Ar 1 , Ar 2 and Ar 3 respectively represent, independently from each other, amember selected from the group consisting of substituted and unsubstituted divalent aromatic hydrocarbon ring residues having two bonds extending in coaxial or parallel relationship to each other and substituted and unsubstituted divalent aromatic heterocyclic ring residues having two bonds located on two atoms spaced a largest distance in the ring, Ar 4 and Ar 5 respectively represent, independently from each other, a member selected from the group consisting of p-phenylene radical and x'-phenylene radical, and R 1 , R 2 , R 3 , R 4 and R 5 respectively represent, independently from each other, an alkyl radical having 1 to 5 carbon atoms.
Claim 5
Dependent Claim
71 words
The process as claimed in claim 3, wherein the sum of the molar amounts of the repeating units of the formula (I) and (IV) is substantially equal to that of formula (II), the repeating units of the formula (III) are in an amount of 0 to 90 molar %, and the repeating units of the formula (IV) are in an amount of 5 to 50 molar %, in the aromatic polyetheramide.
Claim 6
Dependent Claim
28 words
The process as claimed in claim 1, wherein the polyester fibers in the fibrous material are selected from polyethylene terephthalate fibers, polybutylene terephthalate fibers and polyethylene naphthalate fibers.
Claim 7
Dependent Claim
39 words
The process as claimed in claim 1, wherein the cold plasma treatment is carried out in an atmosphere containing at least one member selected from the group consisting of oxygen, nitrogen, ammonia, nitrogen monoxide, argon, helium, and tetrafluoromethane gases.
Claim 8
Dependent Claim
25 words
The process as claimed in claim 1, wherein the cold plasma treatment is carried out at a temperature of from 20° C. to 200° C.
Claim 9
Dependent Claim
25 words
The process as claimed in claim 1, wherein the cold plasma treatment is carried out under a pressure of from 10 -5 to 10 Torr.
Claim 10
Dependent Claim
32 words
The process as claimed in claim 1, wherein the polyamide vapor to be used in the ion-plating treatment consists of at least one member selected from poly-ε-capramide, polyhexamethylene adipamide, and polyhexamethylene sebacamide.
Claim 11
Dependent Claim
24 words
The process as claimed in claim 1, wherein the ion-plating treatment is carried out under a reduced pressure of 10 -5 to 10 Torr.
Claim 12
Dependent Claim
25 words
The process as claimed in claim 1, wherein the ion-plated polyamide deposited on the fibrous material is in a thickness of 0.05 to 1 μm.
Claim 13
Dependent Claim
31 words
The process as claimed in claim 1, wherein in the adhesive composition, the rubber is selected from natural rubber, styrene-butadiene copolymer rubber, vinyl pyridine-styrene-butadiene terpolymer rubber, nitrile rubber, and chloroprene rubber.
Claim 14
Dependent Claim
28 words
The process as claimed in claim 1, wherein the resorcinol-formaldehyde precondensation product and the rubber latex are in a dry solid weight ratio of from 1:1 to 1:15.
Claim 15
Dependent Claim
28 words
The process as claimed in claim 1, wherein the adhesive composition is impregnated in an amount of 0.1 to 10% by dry solid weight in the fibrous material.
Claim 16
Dependent Claim
28 words
The process as claimed in claim 1, wherein the adhesive composition impregnated in the fibrous material is dried and cured at a temperature of 120° C. or more.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-07-12 | 1992-01-11 | 1992-07-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-07-12 | 1996-01-11 | 1996-07-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-07-12 | 2000-01-11 | 2000-07-12 | $7700.00 | Window Closed / Lapsed |