Particles dispersed aluminum matrix composites and method for making same
Assignee: Altemira Co Ltd
•
Filing: 1987-08-26
•
Granted: 1988-07-12
•
Expires: 2007-08-26
Abstract
Abstract An aluminum matrix composite containing evenly dispersed reinforcement particles in the aluminum matrix wherein the contents of oxygen and carbon are controlled so that their volume percentage is not larger than 20% and wherein the contents of the reinforcement particles, oxygen and carbon are controlled so that their volume percentage is not larger than 40%. The control of oxygen and carbon is effected by carrying out the main process at a non-oxidizing atmosphere and minimizing the addition of an anti-seizure agent required to facilitate the mechanical alloying treatment.
Inventors
- 👤 Tsunemasa Miura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 10:02
CPC Classifications
C; C22; C22C; C22C1/00; C22C1/10; C22C1/1084; C22C32/00
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
56 words
A particles dispersed aluminum matrix composite, which comprises oxygen, carbon, and reinforcement particles, wherein the volume percentage of oxygen and carbon is not larger than 20%, and wherein the volume percentage of the reinforcement particles is 10% or more, and wherein the volume percentage of the reinforcement particles, oxygen and carbon is not larger than 40%.
Claim 2
Dependent Claim
56 words
A particles dispersed aluminum matrix composite, which comprises oxygen, carbon, and reinforcement particles, wherein the volume percentage of oxygen and carbon is not larger than 20%, and wherein the volume percentage of the reinforcement particles is 10% or more, and wherein the volume percentage of the reinforcement particles, oxygen and carbon is not larger than 40%.
Claim 3
Dependent Claim
23 words
An aluminum matrix composite as defined in claim 1, wherein the average diameter of the reinforcement particles is not larger than 10 μm.
Claim 4
Dependent Claim
27 words
An aluminum matrix composite as defined in claim 2, wherein the reinforcement particles are one or more substances selected from oxides, carbides, nitrides, borides, and intermetallic compounds.
Claim 5
Independent Claim
154 words
A method for making An aluminum matrix composite, the method comprising: mixing aluminum powder and reinforcement particles so as to obtain a primary powdery mixture, wherein the volume percentage of the reinforcement particles is 10% or more; applying the powdery mixture to a mechanical alloying treatment so as to obtain a secondary powdery composite; removing dissolved gases by heat from the powdery composite under reduced pressure; applying pressure to the powdery composite in a confined space filled therewith so as to form it into a mass; wherein the process from the mechanical alloying treatment up to the pressure application is carried out at a non-oxidizing atmosphere, and the addition of an anti-seizure agent is minimized so as to ensure the volume percentage of oxygen and carbon is not larger than 20%, and wherein the contents of oxygen, carbon and reinforcement particles are controlled to ensure that their volume percentage is not larger than 40%.
Claim 6
Independent Claim
154 words
A method for making An aluminum matrix composite, the method comprising: mixing aluminum powder and reinforcement particles so as to obtain a primary powdery mixture, wherein the volume percentage of the reinforcement particles is 10% or more; applying the powdery mixture to a mechanical alloying treatment so as to obtain a secondary powdery composite; removing dissolved gases by heat from the powdery composite under reduced pressure; applying pressure to the powdery composite in a confined space filled therewith so as to form it into a mass; wherein the process from the mechanical alloying treatment up to the pressure application is carried out at a non-oxidizing atmosphere, and the addition of an anti-seizure agent is minimized so as to ensure the volume percentage of oxygen and carbon is not larger than 20%, and wherein the contents of oxygen, carbon and reinforcement particles are controlled to ensure that their volume percentage is not larger than 40%.
Claim 7
Dependent Claim
21 words
A method as defined in claim 4, wherein the reinforcement particles have an average diameter of not larger than 10 μm.
Claim 8
Dependent Claim
25 words
A method as defined in claim 5, wherein the reinforcement particles are one or more substances selected from oxides, carbides, nitrides, borides, and intermetallic compounds.
Claim 9
Dependent Claim
36 words
A method as defined in claim 4, wherein the quantity of the anti-seizure agent is limited to the range of 5 to 60 cc per 1 kg of a mixture of matrix powder and reinforcement particles.
References Cited (Backward Citations)
US4292079A
Cited
US4297136A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-07-12 | 1992-01-11 | 1992-07-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-07-12 | 1996-01-11 | 1996-07-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-07-12 | 2000-01-11 | 2000-07-12 | $7700.00 | Window Closed / Lapsed |