Roofing adhesive
Assignee: Building Materials Corp of America
•
Filing: 1987-04-06
•
Granted: 1988-07-05
•
Expires: 2007-04-06
Abstract
Abstract A low temperature self-sealing roofing adhesive blend comprising (a) 50-95% by weight of a bituminous component having an asphalt component Index (ACI) less than 0.26 and an asphaltene content less than 20% which component is a road paving asphalt or a blend of road paving asphalt and a hard resin asphalt combined in a weight ratio of between about 1:2 and about 5:1; (b) 1-6% by weight of a thermoplastic block polymer of styrene and butadiene monomers consisting essntially of between 0% and 90% of the styrene/butadiene diblock polymer having a Brookfield viscosity (25 wt. % toluene solution) at 77° F. of between about 500 and about 5,000 cps and between 100% and 10% of the styrene/butadiene/styrene triblock polymer having a Brookfield viscosity (25 wt. % toluene solution) at 77° F. of between about 1,000 and about 50,000 cps and (c) 4-40% by weight of an inert filler. The invention also pertains to the use of the above blend as a roofing self-sealing adhesive.
Inventors
- 👤 Steven S. Lalwani
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 23:25
CPC Classifications
C; C09; C09J; C09J195/00; C08; C08L; C08L2666/00; C08L2666/02; C08L2666/24
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
97 words
A bituminous adhesive blend consisting essentially of: (a) 50-95% by weight of a bituminous component comprising a road paving grade asphalt or a mixture of road paving grade asphalt and a hard resin asphalt in a weight ratio of between about 1:10 and about 10:1, said component having an ACI less than 0.26 and an asphaltene content less than 20%; (b) 1-6% by weight of a thermoplastic block copolymer of styrene and butadiene wherein the weight ratio of styrene to butadiene is between about 1:1 and about 1:10; and (c) 4-40% by weight of an inert filler.
Claim 2
Dependent Claim
97 words
A bituminous adhesive blend consisting essentially of: (a) 50-95% by weight of a bituminous component comprising a road paving grade asphalt or a mixture of road paving grade asphalt and a hard resin asphalt in a weight ratio of between about 1:10 and about 10:1, said component having an ACI less than 0.26 and an asphaltene content less than 20%; (b) 1-6% by weight of a thermoplastic block copolymer of styrene and butadiene wherein the weight ratio of styrene to butadiene is between about 1:1 and about 1:10; and (c) 4-40% by weight of an inert filler.
Claim 3
Dependent Claim
17 words
The blend of claim 1 wherein the ACI of the bituminous component is at least about 0.20.
Claim 4
Dependent Claim
32 words
The blend of claim 1 wherein the bituminous component is a mixture and the weight ratio of road paving grade asphalt to hard resin asphalt is between about 1:2 and about 5:1.
Claim 5
Dependent Claim
23 words
The blend of claim 1 wherein the bituminous component is road paving grade asphalt having a needle penetration at 77° F. of 40-80.
Claim 6
Dependent Claim
77 words
The blend of claim 1 wherein the thermoplastic copolymer of styrene and butadiene consists essentially of between 0% and about 90% by weight of diblock copolymer having a Brookfield viscosity (25 wt. % toluene solution) at 77° F. of between about 500 and about 5,000 cps and between 100% and about 10% by weight of triblock copolymer having a Brookfield viscosity (25 wt. % toluene solution) at 77° F. of between about 1,000 and about 50,000 cps.
Claim 7
Dependent Claim
16 words
The blend of claim 5 wherein the thermoplastic triblock copolymer has a linear or branched structure.
Claim 8
Dependent Claim
23 words
The blend of claim 5 wherein the thermoplastic diblock copolymer has a linear structure and the styrene-butadiene-styrene triblock copolymer has a radial structure.
Claim 9
Dependent Claim
17 words
The blend of claim 1 wherein the filler is selected from the group of limestone and sand.
Claim 10
Dependent Claim
36 words
The blend of claim 1 wherein the bituminous component is a mixture and the hard resin asphalt is a propane cut petroleum asphalt having a softening point of between about 165° F. and about 195° F.
Claim 11
Dependent Claim
57 words
The process of producing the adhesive of claim 1 which comprises gradually adding component (b) to at least the road paving grade asphalt of component (a) at a temperature between about 250 and about 450° F. to dissolve component (b) in the asphalt of component (a) mixing to obtain uniformity of the mixture and adding component (c).
Claim 12
Dependent Claim
47 words
The process of claim 10 wherein the bituminous component is a mixture and is maintained at a temperature of between about 300° F. and about 400° F. and component (b) followed by component (c) is added to component (a) and mixed therein to provide a uniform composition.
Claim 13
Dependent Claim
71 words
The process of claim 10 wherein component (a) is a mixture and component (b) is mixed with the road paving grade asphalt of component (a) at a temperature of between about 250° F. and about 400° F. until a uniform composition is formed, the hard asphalt of component (a) is then added to the uniform composition with mixing at between about 300° F. and about 400° F. followed by component (c).
Claim 14
Dependent Claim
27 words
The blend of claim 1 having less than 10% filler which additionally contains between about 0.05% and about 5% by weight of a stearically hindered phenolic antioxidant.
Claim 15
Dependent Claim
32 words
The process of claim 10 wherein the adhesive contains less than 10% of filler and a stearically hindered phenolic antioxidant is added and mixed into the composition before the addition of filler.
References Cited (Backward Citations)
US4430465A
Cited
US4459157A
Cited
US4460723A
Cited
US4547399A
Cited
US4485201A
Cited
US4490493A
Cited
US4530652A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-07-05 | 1992-01-04 | 1992-07-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-07-05 | 1996-01-04 | 1996-07-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-07-05 | 2000-01-04 | 2000-07-05 | $7700.00 | Window Closed / Lapsed |