US4755400A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Hot roll fuser and method of making a fuser roll
Assignee: IBM Information Products Corp
•
Filing: 1987-03-19
•
Granted: 1988-07-05
•
Expires: 2007-03-19
Abstract
Abstract An electrophotographic fuser roll includes a hard external surface having low surface energy and high abrasion resistance. This surface is formed by sequentially coating a metal roll with two layers of a polymeric material. The polymeric material is not cured until after the second layer is applied. Once the material is cured, it is subjected to a polishing step that also generates heats. In this way, the roll's surface is both polished and heat treated.
Inventors
- 👤 Lawrence P. Dempsey
- 👤 Dean S. Ehn
- 👤 Reid W. Gunnell
- 👤 Bruce P. Reinhardt
- 👤 Lance A. Walker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 11:06
CPC Classifications
G; G03; G03G; G03G15/00; G03G15/20; G03G15/2003; G03G15/2014; G03G15/2053; G03G15/2057
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
110 words
A method of manufacturing a polymer coated electrophotographic fuser roll comprising the sequential steps of: applying primer coat means (11 and 12) to a cylindrical metal roll (10), applying a first coat (16) of a fluoropolymer to said primer coat means, heating, without curing, said first fluoropolymer coat, applying a second coat (15) of a fluoropolymer to said first fluoropolymer coat, curing said first and second fluoropolymer coatings at an elevated temperature, and polishing the exposed surface (17) of said second fluoropolymer coat in a manner that generates sufficient heat to increase the hardness and to lower the surface energy of said coated roll in the absence of additional coats.
Claim 2
Independent Claim
110 words
A method of manufacturing a polymer coated electrophotographic fuser roll comprising the sequential steps of: applying primer coat means (11 and 12) to a cylindrical metal roll (10), applying a first coat (16) of a fluoropolymer to said primer coat means, heating, without curing, said first fluoropolymer coat, applying a second coat (15) of a fluoropolymer to said first fluoropolymer coat, curing said first and second fluoropolymer coatings at an elevated temperature, and polishing the exposed surface (17) of said second fluoropolymer coat in a manner that generates sufficient heat to increase the hardness and to lower the surface energy of said coated roll in the absence of additional coats.
Claim 3
Dependent Claim
17 words
The method of claim 1 wherein said first and second coats are formed of the same material.
Claim 4
Dependent Claim
33 words
The method of claim 2 wherein said primer coat means in from 0.0007 to 0.0011 inch thick, and each of said first and second fluoropolymer coats are from 0.0004 to 0.0006 inch thick.
Claim 5
Dependent Claim
36 words
The method of claim 2 wherein said primer coat means includes a primer coat (11) that is applied directly to said metal roll, and an intermediate polymer coat (12) that is applied to said primer coat.
Claim 6
Dependent Claim
22 words
The method of claim 4 wherein said intermediate coat (12) comprises substantially the same material as said first and second fluoropolymer coats.
Claim 7
Dependent Claim
42 words
The method of claim 5 wherein said primer coat is from 0.0003 to 0.0005 inch thick, said intermediate coat is from 0.0004 to 0.0006 inch thick, and each of said first and second fluoropolymer coats are from 0.0004 to 0.0006 inch thick.
Claim 8
Dependent Claim
47 words
The method of claim 1 including the step of preparing said metal roll for the application of said primer coat means by producing a roughness of from 180 to 220 microinches on the surface of said metal roll prior to the application of said primer coat means.
Claim 9
Dependent Claim
28 words
The method of claim 7 including the step of stress relieving said metal roll by the application of heat prior to the application of said primer coat means.
Claim 10
Dependent Claim
16 words
The method of claim 8 wherein said first and second coats comprise the same polymeric material.
Claim 11
Dependent Claim
33 words
The method of claim 9 wherein said primer coat means is from 0.0007 to 0.0011 inch thick, and each of said first and second fluoropolymer coats are from 0.0004 to 0.0006 inch thick.
Claim 12
Dependent Claim
36 words
The method of claim 9 wherein said primer coat means includes a primer coat (11) that is applied directly to said metal roll, and an intermediate polymer coat (12) that is applied to said primer coat.
Claim 13
Dependent Claim
12 words
The method of claim 11 wherein said intermediate coat comprises a fluoropolymer.
Claim 14
Dependent Claim
42 words
The method of claim 12 wherein said primer coat is from 0.0003 to 0.0005 inch thick, said intermediate coat is from 0.0004 to 0.0006 inch thick, and each of said first and second fluoropolymer coats are from 0.0004 to 0.0006 inch thick.
Claim 15
Dependent Claim
31 words
The method of claim 1 wherein said polishing step comprises polishing said exposed surface with a non-woven talc cloth while exerting a force thereagainst of about 26 pounds per square inch.
Claim 16
Dependent Claim
42 words
The method of claim 14 wherein said polishing step includes the step of rotating said roll to achieve a surface speed of about 462 feet per minute as said talc cloth is moved back and forth across the surface of said roll.
Claim 17
Dependent Claim
19 words
The method of claim 15 wherein said polishing step achieves a surface finish of less than about 25 microinches.
Claim 18
Dependent Claim
47 words
The method of claim 16 including the step of preparing said metal roll for the application of said primer coat means by producing a roughness of from 180 to 220 microinches on the surface of said metal roll prior to the application of said primer coat means.
Claim 19
Dependent Claim
28 words
The method of claim 17 including the step of stress relieving said metal roll by the application of heat prior to the application of said primer coat means.
Claim 20
Dependent Claim
16 words
The method of claim 18 wherein said first and second coats comprise the same polymeric material.
Claim 21
Dependent Claim
33 words
The method of claim 19 wherein said primer coat means is from 0.0007 to 0.0011 inch thick, and each of said first and second fluoropolymer coats are from 0.0004 to 0.0006 inch thick.
Claim 22
Dependent Claim
36 words
The method of claim 20 wherein said primer coat means includes a primer coat (11) that is applied directly to said metal roll, and an intermediate polymer coat (12) that is applied to said primer coat.
Claim 23
Dependent Claim
11 words
The method of claim 21 wherein intermediate coat comprises a fluoropolymer.
Claim 24
Dependent Claim
26 words
The method of claim 22 wherein said primer coat is from 0.0003 to 0.0005 inch thick, said intermediate coat is from 0.0004 to 0.0006 inch thick.
Claim 25
Dependent Claim
20 words
The method of claim 14 wherein prior to said polishing step, said surface is subjected to a wet sanding step.
Claim 26
Dependent Claim
39 words
The method of claim 24 wherein said wet sanding step comprises an initial step of wet sanding with a low grit paper for about 30 seconds, followed by wet sanding with a higher grid paper for about 2 minutes.
Claim 27
Dependent Claim
23 words
The method of claim 25 wherein said wet sanding steps include the application of a force of about 26 pounds per square inch.
Claim 28
Dependent Claim
30 words
The method of claim 26 wherein said polishing step and said sanding step are accompanied by rotation of said roll at a surface speed of about 462 feet per minute.
References Cited (Backward Citations)
US3765924A
Cited
US3776760A
Cited
US3852861A
Cited
US3810776A
Cited
US3971115A
Cited
US3940518A
Cited
US4207059A
Cited
US4258089A
Cited
US4145181A
Cited
US4284668A
Cited
US4435839A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-07-05 | 1992-01-04 | 1992-07-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-07-05 | 1996-01-04 | 1996-07-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-07-05 | 2000-01-04 | 2000-07-05 | $7700.00 | Window Closed / Lapsed |