US4435839A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Foil bearing rubbing surface coating application methods
Assignee: Garrett Corp
•
Filing: 1982-09-21
•
Granted: 1984-03-06
•
Expires: 2002-09-21
Abstract
Abstract A specially designed method is used to apply a graphite fluoride (CFx)-polyimide binder dry lubricant coating to the rubbing contact surface of a foil element used in a high speed gas foil bearing.
Inventors
- 👤 Alston L. Gu
- 👤 Alexander Silver
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 16:33
CPC Classifications
F; F16; F16C; F16C17/00; F16C17/02; F16C17/024; F16C33/00; F16C33/02; F16C33/04; F16C33/06; F16C33/14; Y; Y10; Y10S; Y10S384/00; Y10S384/90; Y10S384/907; Y10T; Y10T29/00; Y10T29/49; Y10T29/49636; Y10T29/49639; Y10T29/49702
Claims Analysis
Total Claims: 33
Claim 1
Independent Claim
106 words
A method of applying a dry lubricant coating to a rubbing contact surface of a bearing, said method comprising the steps of: (a) providing a coating mixture comprising a dry lubricant material and a liquid binder; (b) applying a multiplicity of subcoats of said mixture to the rubbing contact surface to form a multilayered lubricant coating thereon; (c) curing each successive subcoat at a first temperature to individually solidify the subcoats; (d) deroughening the surfaces of selected ones of the subcoats positioned at predetermined thickness intervals of said multilayered coating; and (e) curing the multilayered coating at a second temperature substantially higher than said first temperature.
Claim 2
Independent Claim
106 words
A method of applying a dry lubricant coating to a rubbing contact surface of a bearing, said method comprising the steps of: (a) providing a coating mixture comprising a dry lubricant material and a liquid binder; (b) applying a multiplicity of subcoats of said mixture to the rubbing contact surface to form a multilayered lubricant coating thereon; (c) curing each successive subcoat at a first temperature to individually solidify the subcoats; (d) deroughening the surfaces of selected ones of the subcoats positioned at predetermined thickness intervals of said multilayered coating; and (e) curing the multilayered coating at a second temperature substantially higher than said first temperature.
Claim 3
Dependent Claim
24 words
The method of claim 1 further comprising the step of (f) applying a dry lubricant material upon the surface of the cured multilayered coating.
Claim 4
Dependent Claim
41 words
The method of claim 2 wherein said step (d) includes deroughening the surface of the last-applied subcoat, and wherein said step (f) is performed by burnishing a dry lubricant powder into said last-applied subcoat prior to the deroughening of its surface.
Claim 5
Dependent Claim
24 words
The method of claim 1 wherein said step (a) is performed by providing a coating mixture comprising graphite fluoride (CFx) powder and polyimide varnish.
Claim 6
Dependent Claim
35 words
The method of claim 1 wherein said step (a) is performed by providing a coating mixture comprising graphite fluoride (CFx) powder, polyimide varnish, an N-methylpyrrolidone and xylene thinning liquid, and a fluorocarbon solution wetting agent.
Claim 7
Dependent Claim
77 words
The method of claim 1 wherein said step (a) is performed by providing a coating mixture comprising a quantity of polyimide varnish, a quantity of N-methylpyrrolidone and xylene thinning liquid having a volume approximately three times the volume of said quantity of polyimide varnish, a quantity of CF 1 .0 powder having a weight equal to approximately 0.43 times the weight of said quantity of polyimide varnish, and a small quantity of a fluorocarbon solution wetting agent.
Claim 8
Dependent Claim
28 words
The method of claim 1 wherein said step (c) is performed by curing said subcoats at an initial cure temperature of approximately 225° F. to approximately 275° F.
Claim 9
Dependent Claim
27 words
The method of claim 7 wherein said step (e) includes curing said multilayered coating at a final cure temperature between approximately 650° F. and approximately 750° F.
Claim 10
Dependent Claim
49 words
The method of claim 8 wherein said step (e) is performed by exposing said multilayered coating to an initial temperature of approximately 212° F., gradually elevating the curing temperature to said final cure temperature, and then curing the multilayered coating at said final cure temperature for approximately one hour.
Claim 11
Dependent Claim
32 words
The method of claim 1 wherein said step (d) is performed by deroughening the surfaces of subcoats positioned at thickness intervals equal to approximately one third the thickness of said multilayered coating.
Claim 12
Dependent Claim
26 words
A bearing having a rubbing contact surface coated in accordance with the method of claim 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10.
Claim 13
Independent Claim
166 words
A method of utilizing graphite fluoride (CFx) to lubricate the rubbing contact surface of a foil element in a high speed foil bearing, said method comprising the steps of: (a) forming a coating mixture comprising CFx powder and a liquid polyimide binder; (b) applying a multiplicity of subcoats of said mixture to the rubbing contact surface to form a multilayered lubricant coating thereon; (c) curing each successive subcoat to individually solidify the subcoats; (d) deroughening the surfaces of selected ones of the subcoats positioned at predetermined thickness intervals of said multilayered coating; (e) curing the multilayered coating by exposing the same to a relatively low curing temperature, raising the curing temperature to a substantially higher level, and then curing the multilayered coating at the higher temperature for a predetermined length of time; (f) burnishing CFx powder into the surface of the cured multilayered coating; and (g) deroughening the burnished surface of the cured multilayered coating to reduce the total coating thickness to a predetermined finished thickness.
Claim 14
Independent Claim
166 words
A method of utilizing graphite fluoride (CFx) to lubricate the rubbing contact surface of a foil element in a high speed foil bearing, said method comprising the steps of: (a) forming a coating mixture comprising CFx powder and a liquid polyimide binder; (b) applying a multiplicity of subcoats of said mixture to the rubbing contact surface to form a multilayered lubricant coating thereon; (c) curing each successive subcoat to individually solidify the subcoats; (d) deroughening the surfaces of selected ones of the subcoats positioned at predetermined thickness intervals of said multilayered coating; (e) curing the multilayered coating by exposing the same to a relatively low curing temperature, raising the curing temperature to a substantially higher level, and then curing the multilayered coating at the higher temperature for a predetermined length of time; (f) burnishing CFx powder into the surface of the cured multilayered coating; and (g) deroughening the burnished surface of the cured multilayered coating to reduce the total coating thickness to a predetermined finished thickness.
Claim 15
Dependent Claim
31 words
The method of claim 12 wherein said step (d) is performed by deroughening subcoats mutually spaced apart by distances equal to approximately one third of the thickness of said multilayered coating.
Claim 16
Dependent Claim
24 words
The method of claim 13 wherein said step (b) is performed by applying approximately nine subcoats of said mixture to the rubbing contact surface.
Claim 17
Dependent Claim
22 words
The method of claim 14 wherein said step (g) is performed in a manner reducing the total coating thickness to approximately 0.001".
Claim 18
Dependent Claim
46 words
The method of claim 12 wherein said step (e) includes gradually raising said curing temperature from approximately 212° F. to a higher curing temperature between approximately 650° F. and approximately 750° F. and then curing said multilayered coating at the higher temperature for approximately one hour.
Claim 19
Dependent Claim
24 words
A foil bearing foil element having a rubbing contact surface coated in accordance with the method of claim 12, 13, 14, 15 or 16.
Claim 20
Independent Claim
119 words
A method of forming a dry lubricant film on the rubbing contact surface of a foil bearing foil element, said method comprising the steps of: (a) forming a coating mixture comprising CFx powder, polyimide varnish, an N-methylpyrrolidone and xylene thinning liquid, and a fluorocarbon solution wetting agent; (b) depositing on the rubbing contact surface a multiplicity of subcoats of said mixture to form a multilayered lubrication coating thereon, (c) individually curing each successive subcoat at an initial curing temperature; (d) deroughening the surfaces of only some of the cured subcoats mutually spaced apart by predetermined thickness intervals of said multilayered coating; and (e) curing said multilayered coating at a final curing temperature substantially higher than said initial curing temperature.
Claim 21
Independent Claim
119 words
A method of forming a dry lubricant film on the rubbing contact surface of a foil bearing foil element, said method comprising the steps of: (a) forming a coating mixture comprising CFx powder, polyimide varnish, an N-methylpyrrolidone and xylene thinning liquid, and a fluorocarbon solution wetting agent; (b) depositing on the rubbing contact surface a multiplicity of subcoats of said mixture to form a multilayered lubrication coating thereon, (c) individually curing each successive subcoat at an initial curing temperature; (d) deroughening the surfaces of only some of the cured subcoats mutually spaced apart by predetermined thickness intervals of said multilayered coating; and (e) curing said multilayered coating at a final curing temperature substantially higher than said initial curing temperature.
Claim 22
Dependent Claim
27 words
The method of claim 18 further comprising the step of (f) applying a thin layer of dry lubricant material to the surface of the cured multilayered coating.
Claim 23
Dependent Claim
27 words
The method of claim 19 wherein said step (f) is performed by burnishing a small amount of CFx powder into the surface of the cured multilayered coating.
Claim 24
Dependent Claim
28 words
The method of claim 20 wherein said step (d) includes deroughening the surface of the last-applied subcoat and wherein said step (f) is performed prior to such deroughening.
Claim 25
Dependent Claim
28 words
The method of claim 18 wherein said step (e) is performed by curing said multilayered coating at a final curing temperature between approximately 650° F. and 750° F.
Claim 26
Dependent Claim
49 words
The method of claim 18 wherein said step (e) is performed by exposing the multilayered coating to a temperature of approximately 212° F., gradually elevating the temperature to said final curing temperature, and then curing said multilayered coating at said final curing temperature for a predetermined period of time.
Claim 27
Dependent Claim
40 words
The method of claim 23 wherein said step (e) includes elevating said temperature to a final curing temperature between approximately 650° F. and 750° F. and then curing said multilayered coating at said final curing temperature for approximately one hour.
Claim 28
Dependent Claim
33 words
The method of claim 18 wherein said step (d) is performed by deroughening the surfaces of subcoats spaced apart by thickness intervals equal to approximately one third the thickness of said multilayered coating.
Claim 29
Dependent Claim
24 words
The method of claim 25 wherein said step (b) is performed by depositing approximately nine subcoats of said mixture on the rubbing contact surface.
Claim 30
Dependent Claim
35 words
A foil bearing foil element having a rubbing contact surface coated with a dry lubricant film applied thereto in accordance with the method of claim 18, 19, 20, 21, 22, 23, 24, 25 or 26.
Claim 31
Independent Claim
132 words
A method of making a coated foil element for use in a high speed foil bearing, said method comprising the steps of: (a) providing a compliant foil element having a rubbing contact surface; (b) providing a coating mixture comprising graphite fluoride powder and polyimide varnish; (c) applying a predetermined number of coating subsets of said mixture to said rubbing contact surface to form thereon a multilayered lubricant coating; (d) curing each successive mixture subcoat in each of said coating subsets at a first curing temperature to individually solidify each of the subcoats; (e) deroughening the surface of each of said coating subsets; (f) curing said multilayered coating at a second curing temperature substantially higher than said first curing temperature; and (g) burnishing graphite fluoride into the surface of the last-applied coating subset.
Claim 32
Independent Claim
132 words
A method of making a coated foil element for use in a high speed foil bearing, said method comprising the steps of: (a) providing a compliant foil element having a rubbing contact surface; (b) providing a coating mixture comprising graphite fluoride powder and polyimide varnish; (c) applying a predetermined number of coating subsets of said mixture to said rubbing contact surface to form thereon a multilayered lubricant coating; (d) curing each successive mixture subcoat in each of said coating subsets at a first curing temperature to individually solidify each of the subcoats; (e) deroughening the surface of each of said coating subsets; (f) curing said multilayered coating at a second curing temperature substantially higher than said first curing temperature; and (g) burnishing graphite fluoride into the surface of the last-applied coating subset.
Claim 33
Dependent Claim
11 words
A coated foil element made by the method of claim 28.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-03-06 | 1987-09-05 | 1988-03-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-03-06 | 1991-09-05 | 1992-03-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-03-06 | 1995-09-05 | 1996-03-06 | $7700.00 | Window Closed / Lapsed |