US4755365A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of producing high purity zirconia powder from zircon powder
Assignee: JFE Steel Corp
•
Filing: 1986-10-01
•
Granted: 1988-07-05
•
Expires: 2006-10-01
Abstract
Abstract In producing zirconia powder by desiliconizing heat treatment of a mixture of zircon powder and a powdery carbon-containing material, optionally with addition of a zirconia stabilizing oxide such as calcia or yttria, in a nonoxidizing atmosphere the conversion of silica into SiO and dissipation of gaseous SiO are promoted and completed by performing the heat treatment under reduced pressure, viz. at a pressure not higher than 0.6 atm. Zirconia powder of very high purity can surely be obtained, even when a large batch of the raw material mixture is treated, by performing the reduced pressure desiliconizing heat treatment in two stages: first at 1200°-1550° C. until almost complete conversion of silica to SiO and then at 1550°-2000° C. The mole ratio of C to SiO 2 in the raw material mixture must be 0.4-2.0. For further enhancement of purity, zirconia powder obtained by the desiliconizing treatment may be subjected to oxidation heat treatment. Efficiency of the desiliconizing heat treatment can be enhanced by precedingly forming the raw material mixture into porous lump(s) whose bulk density is in the range from 0.7 to 2.0.
Inventors
- 👤 Toshihiko Funahashi
- 👤 Ryoji Uchimura
- 👤 Yukio Oguchi
- 👤 Kenichi Ueda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 09:54
CPC Classifications
C; C01; C01G; C01G25/00; C01G25/02; C01P; C01P2004/00; C01P2004/51; C01P2004/60; C01P2004/61; C01P2004/62; C01P2004/80; C01P2006/00; C01P2006/10; C01P2006/80
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
207 words
A method of producing a zirconia powder from zirconia containing SiO 2 , comprising the steps of: preparing a raw material mixture comprising said zircon powder containing said SiO 2 and a powdery carbon-containing material such that the mole ratio of C, which is contained in said carbon-containing material and does not gasify at temperatures below 1000° C. in a nonoxidizing atmosphere, to SiO 2 contained in said zircon powder is in the range from 0.4 to 2.0; and subjecting said raw material mixture to a desiliconizing heat treatment in a nonoxidizing atmosphere of which the presence is not higher than 0.6 atm, said desiliconizing heat treatment being a combination of a first-stage heat treatment which is performed at a temperature in the range from 1200° to 1550° C. for separating silica from said zircon powder and a second-stage heat treatment which is performed at a higher temperature in the range from above 1550° C. to 2000° C. for completely converting silica in the mixture under heat treatment into gaseous SiO and dissipating the gaseous SiO, wherein said raw material mixture is subjected to said desiliconizing heat treatment in the form of at least one lump whose bulk density is in the range from 0.7 to 2.0.
Claim 2
Independent Claim
207 words
A method of producing a zirconia powder from zirconia containing SiO 2 , comprising the steps of: preparing a raw material mixture comprising said zircon powder containing said SiO 2 and a powdery carbon-containing material such that the mole ratio of C, which is contained in said carbon-containing material and does not gasify at temperatures below 1000° C. in a nonoxidizing atmosphere, to SiO 2 contained in said zircon powder is in the range from 0.4 to 2.0; and subjecting said raw material mixture to a desiliconizing heat treatment in a nonoxidizing atmosphere of which the presence is not higher than 0.6 atm, said desiliconizing heat treatment being a combination of a first-stage heat treatment which is performed at a temperature in the range from 1200° to 1550° C. for separating silica from said zircon powder and a second-stage heat treatment which is performed at a higher temperature in the range from above 1550° C. to 2000° C. for completely converting silica in the mixture under heat treatment into gaseous SiO and dissipating the gaseous SiO, wherein said raw material mixture is subjected to said desiliconizing heat treatment in the form of at least one lump whose bulk density is in the range from 0.7 to 2.0.
Claim 3
Dependent Claim
15 words
The method defined in claim 1, wherein said pressure is not higher than 0.1 atm.
Claim 4
Dependent Claim
48 words
The method defined in claim 1, wherein said first-stage heat treatment is performed at a temperature in the range from about 1300° C. to about 1500° C. and said second-stage heat treatment is performed at a temperature in the range from about 1600° C. to about 1800° C.
Claim 5
Dependent Claim
23 words
The method defined in claim 1, wherein said mole ratio of C to SiO 2 is in the range from 0.6 to 1.6.
Claim 6
Dependent Claim
57 words
The method defined in claim 1, further comprising the step of heating zirconia powder containing another zirconium compound selected from the group consisting of ZrC and ZrO as the product of said desiliconizing heat treatment in an oxidizing atmosphere at a temperature in the range from 600° to 1400° C. to thereby oxidize said other zirconium compound.
Claim 7
Dependent Claim
60 words
The method defined in claim 1, wherein said raw material mixture further comprises at least one metal oxide which can form a solid solution with zirconia and serves as a stabilizer for zirconia or metal salt which can be converted into said metal oxide by thermal decomposition at a temperature not higher than the temperature of said first-stage heat treatment.
Claim 8
Dependent Claim
30 words
The method defined in claim 6, wherein said at least one metal oxide is selected from the group consisting of CaO, MgO, Y 2 O 3 and CeO 2 .
Claim 9
Dependent Claim
34 words
A method defined in claim 7, wherein the total amount of said at least one metal oxide is in the range from 0.5 to 20 mole% of ZrO 2 contained in said zircon powder.
Claim 10
Dependent Claim
33 words
A method defined in claim 1, wherein said carbon-containing material is selected from the group consisting of carbon black, petroleum coke, coal coke, petroleum pitch, coal pitch, phenolic resin, polyvinyl alcohol and polyethylene.
References Cited (Backward Citations)
CA632447A
Cited
CA657746A
Cited
DE543675C
Cited
US2072889A
Cited
GB535011A
Cited
US3849532A
Cited
US4118464A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-07-05 | 1992-01-04 | 1992-07-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-07-05 | 1996-01-04 | 1996-07-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-07-05 | 2000-01-04 | 2000-07-05 | $7700.00 | Window Closed / Lapsed |