Thermionic cathode of high emissive power for an electric tube, and process for its manufacture
Assignee: BBC Brown Boveri AG Switzerland
•
Filing: 1987-03-05
•
Granted: 1988-06-21
•
Expires: 2007-03-05
Abstract
Abstract A reactionless thermionic cathode for electronic tubes consists of a metallic or ceramic support and an alloy, preferably an intermetallic compound, containing the actual emission-promoting element, with a metal from the group comprising those of the VIIIth vertical row of the periodic table and rhenium. The preferred activation substances are platinides of the elements having a low electron work function, predominantly Ba and La. The cathode is manufactured by wet-mechanical, cataphoretic or electroplating application of the activation substance to the support or by infiltration of the porous support having a pore volume of at least 10%. High emission current densities are obtained at relatively low operating temperatures.
Inventors
- 👤 Charley Buxbaum
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 19:49
CPC Classifications
H; H01; H01J; H01J9/00; H01J9/02; H01J9/04; H01J9/042; H01J1/00; H01J1/02; H01J1/13; H01J1/14
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
115 words
A thermionic cathode of high emissive power for an electronic tube, consisting of a heat-resisting metallic or ceramic body serving as a support and of a metallic activation substance which promotes the emission of electrons, said activation substance consisting of at least one alloy, intermetallic compound, or mixtures thereof of a metal selected from the group consisting of the metals of the VIII vertical row of the Periodic Table and rhenium, and of an element selected from the group consisting of Ba, Ca, La, Y, Gd, Ce, Th, and U, and that the activation substance covers the entire surface of the support and fills at least 10% of the total volume of the cathode body.
Claim 2
Dependent Claim
115 words
A thermionic cathode of high emissive power for an electronic tube, consisting of a heat-resisting metallic or ceramic body serving as a support and of a metallic activation substance which promotes the emission of electrons, said activation substance consisting of at least one alloy, intermetallic compound, or mixtures thereof of a metal selected from the group consisting of the metals of the VIII vertical row of the Periodic Table and rhenium, and of an element selected from the group consisting of Ba, Ca, La, Y, Gd, Ce, Th, and U, and that the activation substance covers the entire surface of the support and fills at least 10% of the total volume of the cathode body.
Claim 3
Dependent Claim
32 words
The thermionic cathode of claim 1, wherein said support consists of a coherent porous structure having a pore volume of 10-50%, the pores of which are completely filled with the activation substance.
Claim 4
Dependent Claim
36 words
The thermionic cathode of claim 1, wherein the activation substance contains at least one intermetallic compound of a platinum metal with at least one of the elements selected from the group consisting of barium and lanthanum.
Claim 5
Dependent Claim
27 words
The thermionic cathode of claim 3, wherein the activation substance contains a platinide of a metal selected from the group consisting of barium, lanthanum, and mixtures thereof.
Claim 6
Dependent Claim
19 words
The thermionic cathode of claim 4, wherein said activation substance contains BaPt 5 , BaPt 2 and mixtures thereof.
Claim 7
Dependent Claim
30 words
The thermionic cathode of claim 4, wherein said activation substance contains a composition selected from the group consisting of LaPt 5 , LaPt 3 , LaPt 2 and mixtures thereof.
Claim 8
Dependent Claim
27 words
The thermionic cathode of claim 1, wherein the support consists of at least one refractory metal selected from the group consisting of W, Mo, Ta and Nb.
Claim 9
Dependent Claim
12 words
The thermionic cathode of claim 7, wherein said support consists of tungsten.
Claim 10
Dependent Claim
20 words
The thermionic cathode of claim 1, wherein the support consists of ZrO 2 stabilized with Y 2 O 3 .
Claim 11
Dependent Claim
109 words
A process for the manufacture of a thermionic cathode of high emissive power for an electron tube of a structure in which a heat-resisting metallic or ceramic body serves as a support and a metallic activation substance is provided thereon, comprising: applying to or introducing onto said support at least one alloy, intermetallic compound or combination thereof of a metal selected from the group consisting of the metal elements of the group VIII vertical row of the Periodic Table and rhenium and an element selected from the group consisting of Ba, Ca, La, Y, Gd, Ce, Th, and U, said alloy or intermetallic compounds serving as said activation substance.
Claim 12
Dependent Claim
109 words
A process for the manufacture of a thermionic cathode of high emissive power for an electron tube of a structure in which a heat-resisting metallic or ceramic body serves as a support and a metallic activation substance is provided thereon, comprising: applying to or introducing onto said support at least one alloy, intermetallic compound or combination thereof of a metal selected from the group consisting of the metal elements of the group VIII vertical row of the Periodic Table and rhenium and an element selected from the group consisting of Ba, Ca, La, Y, Gd, Ce, Th, and U, said alloy or intermetallic compounds serving as said activation substance.
Claim 13
Dependent Claim
22 words
The process of claim 10, wherein said activation substance is applied to said support by a wet-mechanical, chemical, electroplating or fusion-metallurgical process.
Claim 14
Dependent Claim
23 words
The process of claim 10, wherein said activation substance is applied to a compact body serving as said support by brushing or cataphoresis.
Claim 15
Dependent Claim
32 words
The process of claim 10, wherein said activation substance as a liquid infiltrates the open-pored body which serves as the support and forms a structure which has a pore volume of 10-50%.
Claim 16
Dependent Claim
19 words
The process of claim 13, wherein said infiltrated body is subjected to hot-forming by extrusion, swaging, drawing or rolling.
Claim 17
Dependent Claim
57 words
The process of claim 10, wherein said heat-resisting body, serving as the support, is produced from at least one refractory metal selected from the group consisting of W, Mo, Ta and Nb, or from an alloy of at least two of said refractory metals, and said activation substance is prepared from a platinide of barium or lanthanum.
References Cited (Backward Citations)
US3684912A
Cited
US4019081A
Cited
US4274030A
Cited
US4291252A
Cited
US4429250A
Cited
US4310777A
Cited
JPS5624982A
Cited
US4393328A
Cited
US4533852A
Cited
JPS58133739A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-06-21 | 1991-12-21 | 1992-06-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-06-21 | 1995-12-21 | 1996-06-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-06-21 | 1999-12-21 | 2000-06-21 | $7700.00 | Window Closed / Lapsed |