Reinforcement insert for a structural member and method of making and using the same
Assignee: Henkel Corp
•
Filing: 1985-12-19
•
Granted: 1988-06-14
•
Expires: 2005-12-19
Abstract
Abstract A precast composite plastic reinforcement insert, method of making the reinforcement insert and method of reinforcing a structural member. The insert includes pellets which are formed of a mixture of a thermosetting polymeric resin and a blowing agent. Polymeric resins disclosed include a one-part epoxy with a thermal curing system or a thermoplastic polyester resin. The pellets in one embodiment are retained within a matrix of expanded polystyrene and in combination form the insert. The insert is formed in a mold cavity which receives the pellets and unexpanded polystyrene which is expanded during the process by heating the same within the mold cavity. The insert is used to reinforce a structural member by placing it in the structural member prior to a thermal paint curing operation. The insert is transformed into a lightweight, high-strength reinforcement during the paint curing operation wherein the expanded polystyrene of one embodiment is vaporized, the pellets are expanded and then cured, forming bonds between adjacent pellets and the structural member. If the pellets are not retained in a styrofoam matrix, the insert may be coated with a polymeric adhesive prior to placing it in a structural member.
Inventors
- 👤 Joseph Wycech
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 14:03
CPC Classifications
B; B62; B62D; B62D29/00; B62D29/001; B62D29/002; B29; B29C; B29C44/00; B29C44/02; B29C44/12; B29C44/18; B29C44/182; B29C44/184; B62D21/00; B62D21/09; C; C08; C08J; C08J9/00; C08J9/32; C08J9/35; Y; Y10; Y10S; Y10S264/00; Y10S264/06; Y10S264/07; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249971; Y10T428/249972; Y10T428/249986
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
124 words
A precast reinforcement insert for a structural member, comprising: a plurality of thermosetting pellets, said thermosetting pellets including a mixture of a one-part epoxy resin and a high temperature curing agent, said curing agent being present in the range of 2.0 to 5.0 percent by weight of said epoxy resin, an accelerator present in the range of 0.2 to 1.0 percent by weight of said epoxy resin, pre-expanded microspheres in the range of 2.75 to 3.5 times the resin volume, and unexpanded microspheres in the range of 0.25 to 5.0 percent by weight of resin; and expanded cellular polystyrene forming an expanded cellular polystyrene matrix for said pellets, said thermosetting pellets being partially bonded to one another and to said expanded cellular polystyrene matrix.
Claim 2
Dependent Claim
124 words
A precast reinforcement insert for a structural member, comprising: a plurality of thermosetting pellets, said thermosetting pellets including a mixture of a one-part epoxy resin and a high temperature curing agent, said curing agent being present in the range of 2.0 to 5.0 percent by weight of said epoxy resin, an accelerator present in the range of 0.2 to 1.0 percent by weight of said epoxy resin, pre-expanded microspheres in the range of 2.75 to 3.5 times the resin volume, and unexpanded microspheres in the range of 0.25 to 5.0 percent by weight of resin; and expanded cellular polystyrene forming an expanded cellular polystyrene matrix for said pellets, said thermosetting pellets being partially bonded to one another and to said expanded cellular polystyrene matrix.
Claim 3
Dependent Claim
127 words
A precast insert for use as a structural reinforcement member in a hollow structure comprising a plurality of thermosetting pellets partially bonded together, said thermosetting pellets being a mixture of a polyester resin and a high temperature curing agent in the range of 2.0 to 5.0 percent of resin weight, pre-expanded microspheres in the range of 1.5 to 4.0 times the resin volume, and a B-staged epoxy adhesive coating applied to said thermosetting pellets, said epoxy adhesive coating having a high temperature curing agent in the range of 2.0 to 5.0 percent of coating weight and an accelerator in the range of 0.2 to 1.0 percent of said coating weight, said plurality of thermosetting pellets being partially bonded together by the curing of said epoxy adhesive coating.
Claim 4
Dependent Claim
127 words
A precast insert for use as a structural reinforcement member in a hollow structure comprising a plurality of thermosetting pellets partially bonded together, said thermosetting pellets being a mixture of a polyester resin and a high temperature curing agent in the range of 2.0 to 5.0 percent of resin weight, pre-expanded microspheres in the range of 1.5 to 4.0 times the resin volume, and a B-staged epoxy adhesive coating applied to said thermosetting pellets, said epoxy adhesive coating having a high temperature curing agent in the range of 2.0 to 5.0 percent of coating weight and an accelerator in the range of 0.2 to 1.0 percent of said coating weight, said plurality of thermosetting pellets being partially bonded together by the curing of said epoxy adhesive coating.
Claim 5
Independent Claim
110 words
A method of reinforcing a hollow structural member by bonding a reinforcing insert into said structural member to provide greater strength to said structural member comprising the steps of: placing a precast composite plastic reinforcing insert in said structural member to be reinforced, said insert including a plurality of pellets formed of a thermosetting resin and unexpanded microspheres, said pellets having been heated to partially bond said pellets together to form said precast composite insert; and heating said precast composite insert sufficiently to expand said microspheres such that said pellets expand, and to cause said precast composite insert to expand and to substantially contact and bond to said structural member.
Claim 6
Independent Claim
110 words
A method of reinforcing a hollow structural member by bonding a reinforcing insert into said structural member to provide greater strength to said structural member comprising the steps of: placing a precast composite plastic reinforcing insert in said structural member to be reinforced, said insert including a plurality of pellets formed of a thermosetting resin and unexpanded microspheres, said pellets having been heated to partially bond said pellets together to form said precast composite insert; and heating said precast composite insert sufficiently to expand said microspheres such that said pellets expand, and to cause said precast composite insert to expand and to substantially contact and bond to said structural member.
Claim 7
Dependent Claim
21 words
The method of claim 1 wherein said thermosetting resin is selected from the group consisting of epoxy resin and polyurethane resin.
Claim 8
Dependent Claim
32 words
The method of reinforcing a hollow structural member recited in claim 3, wherein said pellets are embedded in a matrix of expanded polystyrene and wherein said heating step vaporizes said expanded polystyrene.
Claim 9
Dependent Claim
65 words
The method of reinforcing a structural member of claim 5 wherein said expanded polystyrene has a vaporization temperature T v and said expandable microspheres have an expansion temperature T e at which the majority of the expandable microspheres will expand; and said thermosetting resin has a curing temperature T c which is higher than the temperature at which the majority of said expandable microspheres expand.
Claim 10
Dependent Claim
91 words
The method of reinforcing a structural member of claim 5, wherein said precast composite plastic insert is formed by loading a mold cavity with a plurality of said pellets such that interstitial spaces are formed between some of said pellets; and further including the steps of filling said interstitial spaces with unexpanded polystyrene beads, said polystyrene beads being smaller than said pellets; and heating the contents of the mold cavity to heat said pellets and said beads to a temperature sufficient to expand the unexpanded polystyrene to form said expanded polystyrene.
Claim 11
Dependent Claim
49 words
The method of claim 7, wherein said pellets include epoxy resin and wherein said pellets are heated prior to said step of loading the pellets into the die cavity to a temperature at which the epoxy resin is at least partially thermally reacted beyond its A-stage to its B-stage.
Claim 12
Dependent Claim
28 words
The method of reinforcing a structural member recited in claim 3, wherein said pellets expand at a temperature lower than the temperature at which said thermosetting resin cures.
Claim 13
Dependent Claim
37 words
The method of reinforcing a structural member recited in claim 3, wherein said thermosetting resin is an epoxy resin and wherein said pellets further include an accelerator which accelerates the rate at which said thermosetting resin cures.
Claim 14
Independent Claim
97 words
A method of forming a precast composite plastic insert for use in reinforcing a hollow structural member comprising the steps of; loading a mold cavity with a mixture of pellets and unexpanded polystyrene beads, said pellets being formed of a thermosetting resin and unexpanded microspheres, said unexpanded polystyrene beads being smaller than said pellets; heating the mold cavity to heat said pellets and said unexpanded polystyrene beads to expand the unexpanded polystyrene beads to form an expanded polystyrene matrix encasing said pellets, thereby forming said precast composite plastic insert; and removing said insert from the mold cavity.
Claim 15
Independent Claim
97 words
A method of forming a precast composite plastic insert for use in reinforcing a hollow structural member comprising the steps of; loading a mold cavity with a mixture of pellets and unexpanded polystyrene beads, said pellets being formed of a thermosetting resin and unexpanded microspheres, said unexpanded polystyrene beads being smaller than said pellets; heating the mold cavity to heat said pellets and said unexpanded polystyrene beads to expand the unexpanded polystyrene beads to form an expanded polystyrene matrix encasing said pellets, thereby forming said precast composite plastic insert; and removing said insert from the mold cavity.
Claim 16
Dependent Claim
45 words
The method of claim 11, including the further step of heating the pellets prior to said step of loading the pellets into the mold cavity to a temperature at which the thermosetting resin is at least partially thermally reacted beyond its A-stage to its B-stage.
Claim 17
Independent Claim
123 words
A method of forming a precast composite plastic insert comprising the steps of: coating a plurality of thermosetting pellets with a heat curable epoxy adhesive to form epoxy-coated thermosetting pellets; loading a mold cavity with said epoxy-coated thermosetting pellets, the interior surfaces of said mold cavity being formed of a material which is non-adherent to said heat curable epoxy adhesive, and said epoxy-coated thermosetting pellets being formed of a mixture of thermosetting resin and hollow microspheres; heating the mold cavity and said epoxy-coated thermosetting pellets by circulating in the mold cavity a heated gaseous medium to cure said epoxy adhesive to partially bond the epoxy-coated thermosetting pellets together to form a precast composite plastic insert; and removing said insert from the mold cavity.
Claim 18
Independent Claim
123 words
A method of forming a precast composite plastic insert comprising the steps of: coating a plurality of thermosetting pellets with a heat curable epoxy adhesive to form epoxy-coated thermosetting pellets; loading a mold cavity with said epoxy-coated thermosetting pellets, the interior surfaces of said mold cavity being formed of a material which is non-adherent to said heat curable epoxy adhesive, and said epoxy-coated thermosetting pellets being formed of a mixture of thermosetting resin and hollow microspheres; heating the mold cavity and said epoxy-coated thermosetting pellets by circulating in the mold cavity a heated gaseous medium to cure said epoxy adhesive to partially bond the epoxy-coated thermosetting pellets together to form a precast composite plastic insert; and removing said insert from the mold cavity.
Claim 19
Dependent Claim
41 words
The method of claim 13 wherein said coating step comprises heating the epoxy-coated thermosetting pellets to a temperature at which the epoxy adhesive coating of the epoxy-coated thermosetting pellets is at least partially thermally reacted beyond its A-stage to its B-stage.
Claim 20
Independent Claim
110 words
A method for reinforcing a hollow structural member by bonding a reinforcing insert inside said structural member, said method comprising the steps of: providing a plurality of thermosetting pellets, said pellets including a thermosetting resin and a heat-activated blowing agent; placing said thermosetting pellets in a mold cavity; heating said mold cavity and said pellets sufficiently to partially bond said thermosetting pellets together to form a precast insert; removing said precast insert from said mold cavity; placing said precast insert in said structural member; and, heating said precast insert sufficiently to activate said heat-activatable blowing agent and to cause said precast insert to expand and bond to said structural member.
Claim 21
Independent Claim
110 words
A method for reinforcing a hollow structural member by bonding a reinforcing insert inside said structural member, said method comprising the steps of: providing a plurality of thermosetting pellets, said pellets including a thermosetting resin and a heat-activated blowing agent; placing said thermosetting pellets in a mold cavity; heating said mold cavity and said pellets sufficiently to partially bond said thermosetting pellets together to form a precast insert; removing said precast insert from said mold cavity; placing said precast insert in said structural member; and, heating said precast insert sufficiently to activate said heat-activatable blowing agent and to cause said precast insert to expand and bond to said structural member.
Claim 22
Dependent Claim
77 words
The method for reinforcing a hollow structural member recited in claim 15, further including the steps of providing a plurality of unexpanded polystyrene beads, mixing said polystyrene beads with said thermosetting pellets in said mold cavity before said first heating step, and wherein said first heating step expands said polystyrene beads to form a matrix of expanded polystyrene in which said thermosetting pellets are embedded and wherein said second heating step vaporizes said matrix of expanded polystyrene.
Claim 23
Dependent Claim
46 words
The method for reinforcing a structural member recited in claim 15, wherein said thermosetting resin is epoxy resin and wherein said method further includes the step of heating said pellets before said step of placing said pellets in said mold cavity to B-stage said thermosetting pellets.
References Cited (Backward Citations)
US2632922A
Cited
US3608031A
Cited
US3611583A
Cited
US3867495A
Cited
US3842020A
Cited
US3899556A
Cited
US3909058A
Cited
US4014826A
Cited
US4040165A
Cited
US4268574A
Cited
US4311541A
Cited
US4405543A
Cited
US4396565A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-06-14 | 1991-12-14 | 1992-06-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-06-14 | 1995-12-14 | 1996-06-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-06-14 | 1999-12-14 | 2000-06-14 | $7700.00 | Window Closed / Lapsed |