Glass fibers and capillaries with high temperature resistant coatings
Assignee: U S Holding Co Inc
•
Filing: 1986-03-10
•
Granted: 1988-06-14
•
Expires: 2006-03-10
Abstract
Abstract Solid fibers or capillaries are coated with a metal, alloy or dielectric capable of withstanding temperatures in excess of 300° C. and preferably 500° C. The coating is deposited by a heterogeneous nucleation thermochemical deposition process occurring on the surface of the fiber.
Inventors
- 👤 Dipak R. Biswas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 07:05
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/44; G02B6/4401; G02B6/4429; G02B6/4436; C; C03; C03C; C03C25/00; C03C25/10; C03C25/104; C03C25/106; C03C25/1061; C03C25/1063; G01; G01N; G01N30/00; G01N30/02; G01N30/60; G01N30/6052; G01N30/6073; G01N30/6078; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/294; Y10T428/2956
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
89 words
A combination, comprising a glass fiber having an outer surface and a single high temperature resistant coating on said outer surface for enabling said combination to be employed in environments having temperatures exceeding 300° C. without any additional coatings thereon, said single high temperature resistant coating being formed of a material having a melting temperature in excess of 300° C. selected from the group consisting of metal, metal alloy or a dielectric material, said high temperature resistant coating deposited on said surface by a heterogeneous nucleation thermochemical deposition process.
Claim 2
Dependent Claim
89 words
A combination, comprising a glass fiber having an outer surface and a single high temperature resistant coating on said outer surface for enabling said combination to be employed in environments having temperatures exceeding 300° C. without any additional coatings thereon, said single high temperature resistant coating being formed of a material having a melting temperature in excess of 300° C. selected from the group consisting of metal, metal alloy or a dielectric material, said high temperature resistant coating deposited on said surface by a heterogeneous nucleation thermochemical deposition process.
Claim 3
Dependent Claim
40 words
The combination recited in claim 1, wherein said material is selected from the group consisting of aluminum, nickel, silicon, titanium, copper, tungsten, molybdenum, tin oxide, silicon nitride, boron nitride, titanium oxide, aluminum oxide, silicon oxynitride, silicon carbide and boron carbide.
Claim 4
Dependent Claim
16 words
The combination recited in claim 1, wherein said melting temperature is in excess of 500° C.
Claim 5
Dependent Claim
15 words
The combination recited in claim 1, wherein said dielectric includes metal oxides, nitrides and carbides.
Claim 6
Dependent Claim
17 words
The combination recited in claim 1, wherein said coating has a fine grained structure without growth cones.
Claim 7
Dependent Claim
89 words
A combination, comprising a glass capillary having an outer surface and a single high temperature resistant coating on said outer surface for enabling said combination to be employed in environments having temperatures exceeding 300° C. without any additional coatings thereon, said single high temperature resistant coating being formed of a material having a melting temperature in excess of 300° C. selected from the group consisting of metal, metal alloy, or a dielectric material, said high temperature resistant coating deposited on said surface by a heterogeneous nucleation thermochemical deposition process.
Claim 8
Dependent Claim
89 words
A combination, comprising a glass capillary having an outer surface and a single high temperature resistant coating on said outer surface for enabling said combination to be employed in environments having temperatures exceeding 300° C. without any additional coatings thereon, said single high temperature resistant coating being formed of a material having a melting temperature in excess of 300° C. selected from the group consisting of metal, metal alloy, or a dielectric material, said high temperature resistant coating deposited on said surface by a heterogeneous nucleation thermochemical deposition process.
Claim 9
Dependent Claim
40 words
The combination recited in claim 6, wherein said material is selected from the group consisting of aluminum, nickel, silicon, titanium, copper, tungsten, molybdenum, tin oxide, silicon nitride, boron nitride, titanium oxide, aluminum oxide, silicon oxynitride, silicon carbon and boron carbide.
Claim 10
Dependent Claim
16 words
The combination recited in claim 6, wherein said melting temperature is in excess of 500° C.
Claim 11
Dependent Claim
15 words
The combination recited in claim 6, wherein the dielectric includes metal oxides, nitrides and carbides.
Claim 12
Dependent Claim
18 words
The combination as recited in claim 6, wherein said coating has a fine grained structure without growth cones.
References Cited (Backward Citations)
US3436141A
Cited
US4028080A
Cited
JPS5612602A
Cited
WO1982001543A1
Cited
US4418984A
Cited
JPS5858502A
Cited
JPS5858501A
Cited
US4512629A
Cited
US4518628A
Cited
US4468294A
Cited
US4592932A
Cited
US4575463A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-06-14 | 1991-12-14 | 1992-06-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-06-14 | 1995-12-14 | 1996-06-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-06-14 | 1999-12-14 | 2000-06-14 | $7700.00 | Window Closed / Lapsed |