Emulsion-char method for making fine ceramic powders
Assignee: MRA Laboratories Inc
•
Filing: 1986-12-29
•
Granted: 1988-06-07
•
Expires: 2006-12-29
Abstract
Abstract Water soluble precursors of ceramic compounds are emulsified in an organic fluid containing an organic surfactant. The emulsion is subsequently mildly heated at a pressure of about 0.05 atmospheres to remove the free water from the emulsion droplets. The resulting sludge consists of particles deriving from the dehydrated emulsion droplets. These particles may only be bound by the surfactant, all or most of the original organic fluid having been boiling off under low pressure. This sludge is then heated in a standard air atmosphere to char the surfactant, which char is to maintain the separation between the dried droplet-derived particles to prevent forming sintered or fused agglomerates thereof. With continued heating the transient char is subsequently burned off and the particles are calcined to controllably and simply produce a fine ceramic powder of spherical particles having a narrow size distribution and an average size in the particularly useful range of 0.1 micron to 1.0 micron.
Inventors
- 👤 Sidney D. Ross
- 👤 Galeb H. Maher
- 👤 Clinton E. Hutchins
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 19:28
CPC Classifications
C; C01; C01B; C01B13/00; C01B13/14; C01B13/32; C01B13/328; C01G; C01G23/00; C01G23/003; C01G23/006; C01G25/00; C01G33/00; C01G45/00; C01G45/02; C01G45/026; C04; C04B; C04B35/00; C04B35/622; C04B35/626; C01P; C01P2004/00; C01P2004/30; C01P2004/32; C01P2004/51; C01P2004/52; C01P2004/60; C01P2004/61; C01P2004/62
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
248 words
A ceramic powder-making method comprising: (a) preparing water soluble precursor compounds of a desired ceramic powder product, forming an aqueous solution of said compounds, and forming an emulsion comprised of a water-immiscible-organic fluid, an organic surfactant, and a suspension of droplets of said aqueous solution in said water-immiscible organic fluid; (b) heating said emulsion at a temperature up to approximately 100° C. and at a pressure of less than 0.25 standard atmospheres (190 mm Hg), to evaporate and remove free water from said droplets, to evaporate and remove a major portion and leave no more than a minor portion of said organic fluid and to leave essentially all of said surfactant, to produce a sludge of dehydrated emulsion-droplet-derived particles bound in said surfactant and said remaining minor portion of said organic fluid, and to render the weight of the carbon in all the organic material portion of said sludge that includes the remaining portions respectively of said organic fluid, of said surfactant and of the organic ones of said ceramic precursor compounds, and that is capable of surviving heating to 300° C., less than twice the weight of said desired product; and (c) heating and raising the temperature of said sludge in a standard air atmosphere to decompose said surfactant to form a transient carbon-char matrix containing said particles and to calcine and transform said particles to said desired ceramic; and continuing to heat to oxidize and remove said carbon-char matrix to leave only said ceramic powder product.
Claim 2
Dependent Claim
248 words
A ceramic powder-making method comprising: (a) preparing water soluble precursor compounds of a desired ceramic powder product, forming an aqueous solution of said compounds, and forming an emulsion comprised of a water-immiscible-organic fluid, an organic surfactant, and a suspension of droplets of said aqueous solution in said water-immiscible organic fluid; (b) heating said emulsion at a temperature up to approximately 100° C. and at a pressure of less than 0.25 standard atmospheres (190 mm Hg), to evaporate and remove free water from said droplets, to evaporate and remove a major portion and leave no more than a minor portion of said organic fluid and to leave essentially all of said surfactant, to produce a sludge of dehydrated emulsion-droplet-derived particles bound in said surfactant and said remaining minor portion of said organic fluid, and to render the weight of the carbon in all the organic material portion of said sludge that includes the remaining portions respectively of said organic fluid, of said surfactant and of the organic ones of said ceramic precursor compounds, and that is capable of surviving heating to 300° C., less than twice the weight of said desired product; and (c) heating and raising the temperature of said sludge in a standard air atmosphere to decompose said surfactant to form a transient carbon-char matrix containing said particles and to calcine and transform said particles to said desired ceramic; and continuing to heat to oxidize and remove said carbon-char matrix to leave only said ceramic powder product.
Claim 3
Dependent Claim
29 words
The method of claim 1 wherein at said pressure of said emulsion-heating step said temperature of said emulsion heating step is less than the decomposition temperature of said surfactant.
Claim 4
Dependent Claim
22 words
The method of claim 1 wherein said pressure of said emulsion-heating step is within the range of 20 to 190 mm Hg.
Claim 5
Dependent Claim
28 words
The method of claim 1 wherein said organic fluid is composed of a hydrocarbon having a characteristic boiling temperature within the range from 120° C. to 200° C.
Claim 6
Dependent Claim
40 words
The method of claim 4 wherein said emulsion heating is stopped only after essentially all of said organic fluid is boiled off and removed, and said weight of said carbon is less than 1.0 times that of said ceramic product.
Claim 7
Dependent Claim
43 words
The method of claim 4 wherein said emulsion heating is stopped after about 85% of said organic fluid, said major portion, has boiled away to leave about 15% of said organic fluid, said minor portion, in said sludge to render said sludge pumpable.
Claim 8
Dependent Claim
72 words
The method of claim 1 wherein said water immiscible organic fluid is composed of a low boiling hydrocarbon having a boiling temperature between 120° C. and 200° C. and of up to 15 weight percent of a high boiling hydrocarbon having a boiling temperature greater than 200° C., and wherein said low boiling hydrocarbon is said major portion and said high boiling hydrocarbon is said minor portion to render said sludge pumpable.
Claim 9
Dependent Claim
26 words
The method of claim 1 wherein said organic surfactant has a minimum decomposition temperature that is substantially greater than the peak temperature at said emulsion heating.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-06-07 | 1991-12-07 | 1992-06-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-06-07 | 1995-12-07 | 1996-06-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-06-07 | 1999-12-07 | 2000-06-07 | $7700.00 | Window Closed / Lapsed |