Antistatic resin composition
Assignee: Kohjin Holdings Co Ltd
•
Filing: 1986-03-25
•
Granted: 1988-05-24
•
Expires: 2006-03-25
Abstract
Abstract An antistatic resin composition prepared by dissolving at least one of lithium nitrate and lithium chloride in cold or hot water, adding a molten surface active agent thereto, mixing them together to give a homogeneous mixture, and blending the same with a molten thermoplastic resin either before or after cooling and solidification. The composition is highly antistatic and gives a film having a high degree of transparency.
Inventors
- 👤 Naoya Yamaguchi
- 👤 Sigeyosi Koyabu
- 👤 Tomoji Mizutani
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 15:49
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/28; C08K3/16; C08K5/00; C08K5/0008; C08K5/0075
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
249 words
An antistatic resin composition which comprises a thermoplastic resin and an antistatic composition comprising lithium nitrate and a surface active agent which is at least one member selected from the group consisting of alkylamines containing an alkyl group with 8 to 22 carbon atoms and derivatives thereof, alkyldiamines containing an alkyl group with 8 to 22 carbon atoms, alkylpolyamines containing an alkyl group with 8 to 22 carbon atoms, alkylamides containing an alkyl group with 8 to 22 carbon atoms, esters of polyols with higher fatty acids containing an alkyl group with 7 to 21 carbon atoms, and higher alcohols having 7 to 21 carbon atoms; said resin composition being prepared by preparing a solution of the lithium nitrate in water wherein the amount of water is from 1.8 to 5.2 moles, inclusive of the water of crystallization of the lithium nitrate, per 1 mole of the lithium nitrate, mixing the aqueous solution of the lithium nitrate with the surface active agent in a molten state, the amount of which is from 5 to 500 parts by weight based on 100 parts by weight of the lithium nitrate as an anhydrous salt, yielding an antistatic composition in the form of a homogeneous mixture, an kneading the antistatic composition with the thermoplastic resin in a molten state in a proportion of 0.05 to 20% by weight of the antistatic composition to the resin, thereby obtaining an antistatic resin composition which contains substantially no visible coarse particles of said lithium nitrate.
Claim 2
Dependent Claim
249 words
An antistatic resin composition which comprises a thermoplastic resin and an antistatic composition comprising lithium nitrate and a surface active agent which is at least one member selected from the group consisting of alkylamines containing an alkyl group with 8 to 22 carbon atoms and derivatives thereof, alkyldiamines containing an alkyl group with 8 to 22 carbon atoms, alkylpolyamines containing an alkyl group with 8 to 22 carbon atoms, alkylamides containing an alkyl group with 8 to 22 carbon atoms, esters of polyols with higher fatty acids containing an alkyl group with 7 to 21 carbon atoms, and higher alcohols having 7 to 21 carbon atoms; said resin composition being prepared by preparing a solution of the lithium nitrate in water wherein the amount of water is from 1.8 to 5.2 moles, inclusive of the water of crystallization of the lithium nitrate, per 1 mole of the lithium nitrate, mixing the aqueous solution of the lithium nitrate with the surface active agent in a molten state, the amount of which is from 5 to 500 parts by weight based on 100 parts by weight of the lithium nitrate as an anhydrous salt, yielding an antistatic composition in the form of a homogeneous mixture, an kneading the antistatic composition with the thermoplastic resin in a molten state in a proportion of 0.05 to 20% by weight of the antistatic composition to the resin, thereby obtaining an antistatic resin composition which contains substantially no visible coarse particles of said lithium nitrate.
Claim 3
Dependent Claim
15 words
The antistatic resin composition of claim 1, wherein said thermoplastic resin is an olefin polymer.
Claim 4
Dependent Claim
57 words
The antistatic resin composition of claim 1, wherein the resin composition is in the form of a film formed either directly from the antistatic resin composition or after dilution of the antistatic resin composition with a further amount of said thermoplastic resin, said film containing 0.05 to 2.0% by weight of said antistatic composition to the resin.
Claim 5
Dependent Claim
144 words
A process for preparing an antistatic resin composition, which comprises preparing an aqueous solution of lithium nitrate wherein the amount of water is from 1.8 to 5.2 moles, inclusive of the water of crystallization of the lithium nitrate, per 1 mole of the lithium nitrate; mixing the aqueous solution of lithium nitrate with a surface active agent in a molten state, the amount of which is from 5 to 500 parts by weight based on 100 parts by weight of the lithium nitrate as an anhydrous salt, yielding an antistatic composition in the form of a homogeneous mixture; and kneading the antistatic composition with a thermoplastic resin in a molten state in a proportion of 0.05 to 20% by weight of the antistatic composition to the resin, thereby obtaining an antistatic resin composition which contains substantially no visible coarse particles of said lithium nitrate.
Claim 6
Dependent Claim
144 words
A process for preparing an antistatic resin composition, which comprises preparing an aqueous solution of lithium nitrate wherein the amount of water is from 1.8 to 5.2 moles, inclusive of the water of crystallization of the lithium nitrate, per 1 mole of the lithium nitrate; mixing the aqueous solution of lithium nitrate with a surface active agent in a molten state, the amount of which is from 5 to 500 parts by weight based on 100 parts by weight of the lithium nitrate as an anhydrous salt, yielding an antistatic composition in the form of a homogeneous mixture; and kneading the antistatic composition with a thermoplastic resin in a molten state in a proportion of 0.05 to 20% by weight of the antistatic composition to the resin, thereby obtaining an antistatic resin composition which contains substantially no visible coarse particles of said lithium nitrate.
Claim 7
Dependent Claim
94 words
The process of claim 4, wherein said surface active agent is at least one member selected from the group consisting of alkylamines containing an alkyl group with 8 to 22 carbon atoms and derivatives thereof, alkyldiamines containing an alkyl group with 8 to 22 carbon atoms, alkylpolyamines containing an alkyl group with 8 to 22 carbon atoms, alkylamides containing an alkyl group with 8 to 22 carbon atoms, esters of polyols with higher fatty acids containing an alkyl group with 7 to 21 carbon atoms, and higher alcohols having 7 to 21 carbon atoms.
Claim 8
Dependent Claim
13 words
The process of claim 4, wherein said thermoplastic resin is an olefin polymer.
Claim 9
Dependent Claim
55 words
The process of claim 4, wherein the resin composition is in the form of a film formed either directly from the antistatic resin composition or after dilution of the antistatic resin composition with a further amount of said thermoplastic resin, said film containing 0.05 to 2.0% by weight of said antistatic composition to the resin.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-05-24 | 1991-11-23 | 1992-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-05-24 | 1995-11-23 | 1996-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-05-24 | 1999-11-23 | 2000-05-24 | $7700.00 | Window Closed / Lapsed |