Method for producing air-tight, heat-resistant plate
Assignee: Mitsubishi Electric Corp
•
Filing: 1987-01-27
•
Granted: 1988-05-24
•
Expires: 2007-01-27
Abstract
Abstract A method for producing an air-tight, heat-resistant plate for a particular use in manufacturing bulbous fluorescent lamp, which comprises: preparing a shaping material by mixing an inorganic filler composed of alumina powder and silica powder in a specified compositional ratio, and glass powder having a thermal expansion coefficient of 8.5 to 11.5x10-6/ DEG C., both inorganic filler and glass material being blended at a predetermined ratio then, forming the shaping material into a shaped product of any desired configuration by a known shaping method; thereafter heating this shaped body to a temperature, at which the glass powder used becomes molten and fused, thereby rendering it to be a burned body.
Inventors
- 👤 Tadaki Murakami
- 👤 Kiyoshi Takata
- 👤 Kazuharu Kato
- 👤 Kazuo Okahashi
- 👤 Hitoshi Yamazaki
- 👤 Takao Takeda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 16:58
CPC Classifications
H; H01; H01J; H01J61/00; H01J61/02; H01J61/30; H01J61/32; H01J61/327; C; C03; C03C; C03C14/00; C03C14/004; C03C2214/00; C03C2214/04
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
126 words
A method for producing an air-tight, heat-resistant plate which comprises steps of: (a) preparing a shaping material by mixing 25 to 45% by weight of an inorganic filler consisting essentially of 100 parts by weight of alumina powder and 15 to 50 parts by weight of silica powder; and 55 to 75% by weight of glass powder having a glass transition point of 500° C. or above and a thermal expansion coefficient of from 8.5×10 -6 /° C. to 11.5×10 -6 /° C.; (b) forming said shaping material into a shaped body of a desired configuration by an ordinary forming method; and (c) heating to burn said shaped body at a temperature, at which said glass powder becomes molten and fused, thereby obtaining a burned body.
Claim 2
Independent Claim
126 words
A method for producing an air-tight, heat-resistant plate which comprises steps of: (a) preparing a shaping material by mixing 25 to 45% by weight of an inorganic filler consisting essentially of 100 parts by weight of alumina powder and 15 to 50 parts by weight of silica powder; and 55 to 75% by weight of glass powder having a glass transition point of 500° C. or above and a thermal expansion coefficient of from 8.5×10 -6 /° C. to 11.5×10 -6 /° C.; (b) forming said shaping material into a shaped body of a desired configuration by an ordinary forming method; and (c) heating to burn said shaped body at a temperature, at which said glass powder becomes molten and fused, thereby obtaining a burned body.
Claim 3
Dependent Claim
53 words
The method for producing an air-tight, heat-resistant plate according to claim 1, wherein a coloring matter selected from the group consisting of titanium oxide and zinc oxide in powder form is added in a quantity of not more than 5 parts by weight relative to 100 parts by weight of said shaping material.
Claim 4
Dependent Claim
33 words
The method for producing an air-tight, heat-resistant plate according to claim 1, wherein each of the alumina powder, silica powder and glass powder has an average particle size of 10 μm or below.
References Cited (Backward Citations)
US2912340A
Cited
US3051589A
Cited
US3228548A
Cited
US3374076A
Cited
US3881904A
Cited
US4002799A
Cited
JPS53141915A
Cited
US4585972A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-05-24 | 1991-11-23 | 1992-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-05-24 | 1995-11-23 | 1996-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-05-24 | 1999-11-23 | 2000-05-24 | $7700.00 | Window Closed / Lapsed |