Process for the preparation of water absorptive composite material
Assignee: Unicharm Corp
•
Filing: 1987-07-01
•
Granted: 1988-04-19
•
Expires: 2007-07-01
Abstract
Abstract Aqueous solution of alkali or ammonium acrylate is applied to a prefabricated fibrous substrate, and the acrylate is subjected to polymerization in two steps, namely the first step in which the acrylate is polymerized by means of a radical polymerization initiator and the second step which is subsequent to the first step and in which the unpolymerized acrylate is polymerized by means of irradiation with electromagnetic radiation or corpuscular ionizing radiation.
Inventors
- 👤 Kiichi Itoh
- 👤 Takeshi Shibano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 18:15
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/04; D; D06; D06M; D06M14/00; D06M14/08; D06M14/10; D06M14/02; D06M14/04; D06M14/12; D06M14/14; D06M14/16; D06M14/18; D06M14/20; D06M14/22; D06M14/26; D06M14/28; D06M14/30; D06M14/32; D06M14/34
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
124 words
A process for preparing a water absorptive composite material, which comprises the combination of the following steps of: (A) applying an aqueous solution of a polymerizable monomer comprising as a main component acrylic acid, of which 20% or more of the carboxyl groups have been neutralized to its alkali metal salt or ammonium salt, to a prefabricated fibrous substrate; (B) polymerizing the polymerizable monomers applied to said fibrous substrate by means of a water-soluble radical polymerization initiator to form a composite of a polymer derived from said polymerizable monomer and said fibrous substrate; and (C) irradiating said composite with electromagnetic radiation or corpuscular ionizing radiation to obtain a water absorptive composite of which the water absorption velocity is enhanced as compared with said composite.
Claim 2
Dependent Claim
124 words
A process for preparing a water absorptive composite material, which comprises the combination of the following steps of: (A) applying an aqueous solution of a polymerizable monomer comprising as a main component acrylic acid, of which 20% or more of the carboxyl groups have been neutralized to its alkali metal salt or ammonium salt, to a prefabricated fibrous substrate; (B) polymerizing the polymerizable monomers applied to said fibrous substrate by means of a water-soluble radical polymerization initiator to form a composite of a polymer derived from said polymerizable monomer and said fibrous substrate; and (C) irradiating said composite with electromagnetic radiation or corpuscular ionizing radiation to obtain a water absorptive composite of which the water absorption velocity is enhanced as compared with said composite.
Claim 3
Dependent Claim
33 words
A process according to claim 1, wherein the polymerizable monomer comprises acrylic acid of which 20% or more of the carboxyl groups have been neutralized to its alkali metal salt or ammonium salt.
Claim 4
Dependent Claim
79 words
A process according to claim 1, wherein the polymerizable monomer contains up to 20 mol % of at least one of the monomers selected from the group consisting of 2-acrylamide-2-methylpropanesulfonic acid, 2-acryloylethanesulfonic acid, 2-acryloylpropanesulfonic acid, methacrylic acid and alkali metal salts or ammonium salts thereof, acrylamide, methacrylamide, N,N-dimethylamide, N,N-dimethylmethacrylamide, 2-hydroxyethyl acrylamide, 2-hydroxyethyl methacrylamide, 2-vinylpyridine, 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl acrylate, 2-hydroxypropyl methacrylate, polyethylene glycol monoacrylate, polyethylene gylcol monomethacrylate, N,N'-methylene bisacrylamide, N,N'-methylene bismethacrylamide, polyethylene glycol diacrylate and polyethylene glycol dimethacrylate.
Claim 5
Dependent Claim
27 words
A process according to claim 1, wherein the fibrous substrate formed in step (A) comprises as a main component a cellulose fiber or/and a polyester type fiber.
Claim 6
Dependent Claim
38 words
A process according to claim 1, wherein the fibrous substrate formed in step (A) is a pad of loose fabric, a carded web, an air-laid web, a paper, a nonwoven fabric, a woven fabric or a knitted fabric.
Claim 7
Dependent Claim
47 words
A process according to claim 1, wherein the stage of applying the aqueous solution of the polymerizable monomer in the step (A) to the prefabricated fibrous substrate comprises spraying of said aqueous solution to said fibrous substrate or impregnation of said fibrous substrate with said aqueous solution.
Claim 8
Dependent Claim
40 words
A process according to claim 1, wherein the amount of the polymerizable monomer applied to the fibrous substrate in the step (A) is in a proportion of 1-10,000 parts by weight per 100 parts by weight of the fibrous substrate.
Claim 9
Dependent Claim
18 words
A process according to claim 1, wherein the polymerization initiator in the steps (B) comprises a redox type.
Claim 10
Dependent Claim
64 words
A process according to claim 1, wherein the stage of polymerizing the polymerizable monomer in the step (B) by means of the radical polymerization initiator involes the decomposition of said polymerization initiator while it is previously dissolved in the aqueous solution of the monomer for polymerization, or the spraying of said polymerization initiator in a solution form to the fibrous substrate before decomposition thereof.
Claim 11
Dependent Claim
39 words
A process according to claim 1, wherein the composite to be irradiated in the step (C) does not contain water in a proportion of 40 parts by weight or more per 1 part by weight of the fibrous substrate.
Claim 12
Dependent Claim
17 words
A process according to claim 1, wherein the irradiation dose in the step (C) is 0.01-100 Mrad.
Claim 13
Dependent Claim
24 words
A process according to claim 1, wherein the amount of residual monomers is further reduced by heating the resulting composite after the step (C).
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-04-19 | 1991-10-19 | 1992-04-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-04-19 | 1995-10-19 | 1996-04-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-04-19 | 1999-10-19 | 2000-04-19 | $7700.00 | Window Closed / Lapsed |