Foams of linear low density polyethylene and a method for their preparation
Assignee: BP CHEMICALS FOAMS BUSINESS SA
•
Filing: 1985-07-19
•
Granted: 1988-04-19
•
Expires: 2005-07-19
Abstract
Abstract Foams are prepared from a linear low density polyethylene and, optionally, other olefinic polymers, such as a low density polyethylene using a chemical cross-linking agent. The resulting cross-linked polyethylene foams exhibit an excellent balance of properties at generally lower densities than foams prepared from low density polyethylene only.
Inventors
- 👤 John S. Cheng-Shiang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 11:17
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/0061; C08J9/04; C08J9/06; C08J9/10; C08J9/102; C08J9/103; C08J2323/00; C08J2323/02; C08J2323/04; C08J2323/06; C08J2423/00; Y; Y10; Y10S; Y10S264/00; Y10S264/18
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
157 words
A method for preparing a foam of one or more cross-linked olefin polymer(s) and optionally one or more other polymer(s) wherein the olefinic polymer or, if two or more olefinic polymers are employed, at least one of the olefinic polymers is a linear low density polyethylene wherein the method comprises mixing the linear low density polyethylene, blowing agent and other additives, if employed; preparing the mixture as a sheet material; and subsequently cross-linking and foaming the resulting sheet material characterized in that the linear low density polyethylene has a Vicat softening temperature, as measured by ASTM test method designated D-1525-75 of less than 105° C., cross-linking is affected by a chemical cross-linking agent and cross-linking agent is employed in an amount of 0.3 to 1.5 weight percent and the blowing agent is employed in an amount of from 0.1 to 30 weight percent, said weight percents being based on the total weight of the polymeric material employed.
Claim 2
Independent Claim
157 words
A method for preparing a foam of one or more cross-linked olefin polymer(s) and optionally one or more other polymer(s) wherein the olefinic polymer or, if two or more olefinic polymers are employed, at least one of the olefinic polymers is a linear low density polyethylene wherein the method comprises mixing the linear low density polyethylene, blowing agent and other additives, if employed; preparing the mixture as a sheet material; and subsequently cross-linking and foaming the resulting sheet material characterized in that the linear low density polyethylene has a Vicat softening temperature, as measured by ASTM test method designated D-1525-75 of less than 105° C., cross-linking is affected by a chemical cross-linking agent and cross-linking agent is employed in an amount of 0.3 to 1.5 weight percent and the blowing agent is employed in an amount of from 0.1 to 30 weight percent, said weight percents being based on the total weight of the polymeric material employed.
Claim 3
Dependent Claim
25 words
The method of claim 1 characterized in that the foam is prepared from a combination of a linear low density polyethylene and low density polyethylene.
Claim 4
Dependent Claim
50 words
The method of claim 2 characterized in that at least a portion of the low density polyethylene is pre-mixed with the blowing agent, the cross-linking agent and, if employed, other additives; this pre-mixture is subsequently blended with the linear low density polyethylene and the resulting foaming composition is then foamed.
Claim 5
Dependent Claim
49 words
The method of claim 3 characterized in that the pre-mixture, prior to blending with the linear low density polyethylene to form the foaming composition, is extruded at a temperature above the temperature at which the low density polyethylene is softened and the extruded mass is ground into granular form.
Claim 6
Dependent Claim
54 words
The method of claim 3 characterized in that only a portion of the low density polyethylene is employed in preparing the pre-mixture and the linear low density polyethylene is dry blended with the remainder of the low density polyethylene for subsequent blending of the dry blend with the premixture to form the foaming composition.
Claim 7
Independent Claim
39 words
The method of claims 3 characterized in that the foaming composition is prepared as a sheet by extruding the mixture of the linear low density polyethylene, low density polyethylene, blowing agent and optionally employed cross-linking agent and other additives.
Claim 8
Dependent Claim
20 words
The method of claim 6 characterized in that the sheet is foamed at temperatures between 150° C. and 275° C.
Claim 9
Dependent Claim
50 words
The method of claim 7 characterized in that a chemical cross-linking agent is employed and the sheet is subjected to two temperatures, the first temperature being from 150° C. to 250° C. and the second temperature being higher than the first temperature and being from 210° C. to 260° C.
Claim 10
Dependent Claim
18 words
The method of claim 8 wherein the blowing agent is azodicarbonamide and a chemical cross-linking agent is employed.
References Cited (Backward Citations)
US3651183A
Cited
US3608006A
Cited
US3812225A
Cited
US4048275A
Cited
US4163085A
Cited
US4166890A
Cited
US4255371A
Cited
US4338271A
Cited
US4409164A
Cited
JPS5853929A
Cited
US4519963A
Cited
US4424181A
Cited
JPS59135236A
Cited
US4552708A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-04-19 | 1991-10-19 | 1992-04-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-04-19 | 1995-10-19 | 1996-04-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-04-19 | 1999-10-19 | 2000-04-19 | $7700.00 | Window Closed / Lapsed |