Oxide resistor
Assignee: Asahi Kasei Corp
•
Filing: 1985-06-24
•
Granted: 1988-04-05
•
Expires: 2005-06-24
Abstract
Abstract A composite sintered oxide resistor comprising crystal grains of zinc oxide and crystal grains of a zinc oxide compound of other metal or semi-metal element than zinc, and a grain boundary layer having an electric resistance equal to or lower than that of the crystal grains and which of zinc oxide between the individual crystal grains has a very large withstanding capacity against switch surge, a small non-linear coefficient of voltage in the voltage-current characteristics, a positive, smaller resistance-temperature coefficient, and a small percent change in resistivity after heat treatment at 500 DEG C. in the atmosphere.
Inventors
- 👤 Takeo Yamazaki
- 👤 Satoru Ogihara
- 👤 Tetsuo Kosugi
- 👤 Shingo Shirakawa
- 👤 Shinichi Owada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 17:16
CPC Classifications
H; H01; H01C; H01C7/00; H01C7/001; H01C17/00; H01C17/30; H01C7/10; H01C7/105; H01C7/108; H01C7/112; H01H; H01H9/00; H01H9/30; H01H9/42
Claims Analysis
Total Claims: 43
Claim 1
Independent Claim
110 words
A composite sintered oxide resistor, obtained by sintering a powdery oxide mixture of zinc oxide as the main component and other oxide of metal or semi-metal other than zinc oxide, free from bismuth oxide, so as to form crystal grains of zinc oxide and crystal grains having an electric resistance of 200 Ω to 3×10 13 Ω, free from a grain boundary layer having a higher electric resistance than that of the crystal grains of zinc oxide, the resistor being in a plate form and having electrodes at both end surfaces, and having a non-linear coefficient of voltage of 1.0 to 1.3 at 3×10 -3 to 80 A/cm 2 .
Claim 2
Dependent Claim
110 words
A composite sintered oxide resistor, obtained by sintering a powdery oxide mixture of zinc oxide as the main component and other oxide of metal or semi-metal other than zinc oxide, free from bismuth oxide, so as to form crystal grains of zinc oxide and crystal grains having an electric resistance of 200 Ω to 3×10 13 Ω, free from a grain boundary layer having a higher electric resistance than that of the crystal grains of zinc oxide, the resistor being in a plate form and having electrodes at both end surfaces, and having a non-linear coefficient of voltage of 1.0 to 1.3 at 3×10 -3 to 80 A/cm 2 .
Claim 3
Dependent Claim
93 words
A composite sintered oxide resistor, obtained by sintering a powdery oxide mixture of zinc oxide as a major component and other oxide of metal or semi-metal than zinc oxide, free from bismuth oxide powder, the resistor having a resistance-temperature coefficient of 5×10 -4 Ω/°C. to -5×10 -4 Ω/°C. at 20° l to 500° C., a resistivity of 100 to 4,000 Ω at 20° C., a withstanding capacity against switching surge of 500 to 800 J/cc, and a non-linear coefficient of voltage of 1.0 to 1.3 at 3×10 -3 to 80 A/cm 2 .
Claim 4
Dependent Claim
93 words
A composite sintered oxide resistor, obtained by sintering a powdery oxide mixture of zinc oxide as a major component and other oxide of metal or semi-metal than zinc oxide, free from bismuth oxide powder, the resistor having a resistance-temperature coefficient of 5×10 -4 Ω/°C. to -5×10 -4 Ω/°C. at 20° l to 500° C., a resistivity of 100 to 4,000 Ω at 20° C., a withstanding capacity against switching surge of 500 to 800 J/cc, and a non-linear coefficient of voltage of 1.0 to 1.3 at 3×10 -3 to 80 A/cm 2 .
Claim 5
Dependent Claim
101 words
A composite sintered oxide resistor, which is obtained by sintering a powdery oxide mixture containing 0.1 to 10% by mole of magnesium oxide, 0.1 to 20% by mole of at least one of yttrium oxide, aluminum oxide, gallium oxide, lanthanum oxide and indium oxide, and the balance being zinc oxide, free of bismuth oxide, having zinc oxide grains and a grain boundary layer having a lower electric resistance than that of said zinc oxide grains being formed between crystal grains, and the resistor having a non-linear coefficient of voltage of 1.0 to 1.3 at 3×10 -3 to 80 A/cm 2 .
Claim 6
Dependent Claim
101 words
A composite sintered oxide resistor, which is obtained by sintering a powdery oxide mixture containing 0.1 to 10% by mole of magnesium oxide, 0.1 to 20% by mole of at least one of yttrium oxide, aluminum oxide, gallium oxide, lanthanum oxide and indium oxide, and the balance being zinc oxide, free of bismuth oxide, having zinc oxide grains and a grain boundary layer having a lower electric resistance than that of said zinc oxide grains being formed between crystal grains, and the resistor having a non-linear coefficient of voltage of 1.0 to 1.3 at 3×10 -3 to 80 A/cm 2 .
Claim 7
Dependent Claim
40 words
A composite sintered oxide resistor according to claim 3, wherein the powdery oxide mixture comprises 70 to 92% by mole of zinc oxide, 3 to 10% by mole of magnesium oxide, and 5 to 15% by mole of aluminum oxide.
Claim 8
Dependent Claim
104 words
A composite sintered oxde resistor, which is obtained by sintering a powdery oxide mixture containing 68 to 90% by mole of zinc oxide, 3 to 10% by mole of magnesium oxide, 5 to 15% by mole of aluminum oxide and 1 to 2% by mole of silicon oxide, free from bismuth oxide, having crystal grains of zinc oxide and a grain boundary layer having a lower electric resistance than that of said crystal grains of zinc oxide being formed between the crystal grains, and the resistor having a non-linear coefficient of voltage of 1.0 to 1.3 at 3×10 -3 to 80 A/cm 2 .
Claim 9
Dependent Claim
104 words
A composite sintered oxde resistor, which is obtained by sintering a powdery oxide mixture containing 68 to 90% by mole of zinc oxide, 3 to 10% by mole of magnesium oxide, 5 to 15% by mole of aluminum oxide and 1 to 2% by mole of silicon oxide, free from bismuth oxide, having crystal grains of zinc oxide and a grain boundary layer having a lower electric resistance than that of said crystal grains of zinc oxide being formed between the crystal grains, and the resistor having a non-linear coefficient of voltage of 1.0 to 1.3 at 3×10 -3 to 80 A/cm 2 .
Claim 10
Dependent Claim
45 words
A gas circuit breaker with an oxide resistor, which comprises an oxide resistor being a composite sintered oxide resistor according to any one of claims 1 to 5 and having a column or cylindrical form and electrodes on both end surfaces excluding the side surface.
Claim 11
Dependent Claim
24 words
A gas circuit breaker according to claim 6, wherein an insulating glass is provided by baking on the entire side surface of the resistor.
Claim 12
Dependent Claim
47 words
An SF 6 gas-insulated neutral grounding with an oxide resistor, which comprises an oxide resistor being a composite sintered oxide resistor according to any one of claims 1 to 5 and having a column or cylindrical form and electrodes on both end surfaces excluding the side surface.
Claim 13
Dependent Claim
23 words
An SF 6 gas-insulated neutral grounding according to claim 8, wherein the electrodes are formed at inner positions than the peripheral side surface.
Claim 14
Dependent Claim
89 words
A composite sintered oxide resistor which comprises individual crystal grains including zinc oxide grains, obtained by sintering a powdery oxide mixture of zinc oxide as the main component and other oxide of metal or semi-metal than zinc oxide, free from bismuth oxide, and a grain boundary layer having an electric resistance equal to or lower than that of said zinc oxide grains being present between said individual crystal grains, the resistor having a non-linear coefficient of voltage of 1.0 to 1.3 at 3×10 -3 to 80 A/cm 2 .
Claim 15
Dependent Claim
89 words
A composite sintered oxide resistor which comprises individual crystal grains including zinc oxide grains, obtained by sintering a powdery oxide mixture of zinc oxide as the main component and other oxide of metal or semi-metal than zinc oxide, free from bismuth oxide, and a grain boundary layer having an electric resistance equal to or lower than that of said zinc oxide grains being present between said individual crystal grains, the resistor having a non-linear coefficient of voltage of 1.0 to 1.3 at 3×10 -3 to 80 A/cm 2 .
Claim 16
Dependent Claim
33 words
A composite sintered oxide resistor according to claim 10, wherein the grain boundary layer between the individual crystal grains has an electric resistance equal to that of the crystal grains of zinc oxide.
Claim 17
Dependent Claim
27 words
A composite sintered oxide resistor according to claim 10, wherein a void exists at the position corresponding to the grain boundary layer between the individual crystal grains.
Claim 18
Dependent Claim
23 words
A composite sintered oxide resistor according to claim 10, wherein the metal or the semi-metal element is titanium, silicon, antimony, zirconium, or tin.
Claim 19
Dependent Claim
49 words
A composite sintered oxide resistor according to claim 10, wherein the individual crystal grains further comprise grains having the following chemical formula: Zn 2 TiO 4 , Zn 2 SiO 4 , Zn 7 Sb 2 O 12 , Zn 2 ZrO 4 or Zn 2 SnO 4 .
Claim 20
Dependent Claim
34 words
A composite sintered oxide resistor according to claim 10, wherein the resistor comprises crystal grains of zinc oxide and crystal grains of a zinc oxide compound of other metal or semi-metal element than zinc.
Claim 21
Dependent Claim
43 words
A composite sintered oxide resistor according to claim 15, wherein said powdery oxide mixture contains zinc oxide as the main component and at least one oxide selected from the group consisting of titanium oxide, silicon oxide, antimony oxide, zirconium oxide and tin oxide.
Claim 22
Dependent Claim
26 words
A composite sintered oxide resistor according to claim 15, wherein said powdery oxide mixture contains zinc oxide as the main component, titanium oxide and magnesium oxide.
Claim 23
Dependent Claim
35 words
A composite sintered oxide resistor according to claim 17, wherein said powdery oxide mixture further contains at least one element selected from the group consisting of antimony oxide, silicon oxide, zirconium oxide and tin oxide.
Claim 24
Dependent Claim
45 words
A composite sintered oxide resistor according to claim 17, wherein said powdery oxide mixture contains zinc oxide as the main component, magnesium oxide and at least one oxide selected from the group consisting of aluminum oxide, gallium oxide, lanthanum oxide, indium oxide and yttrium oxide.
Claim 25
Dependent Claim
18 words
A composite sintered oxide resistor according to claim 19, wherein said powdery oxide mixture further contains silicon oxide.
Claim 26
Dependent Claim
100 words
A composite sintered oxide resistor which is obtained by sintering a powdery oxide mixture consisting essentially of 0.1 to 10% by mole of magnesium oxide and 0.1 to 20% by mole of at least one yttrium oxide, gallium oxide, lanthanum oxide and indium oxide, the balance being zinc oxide, having crystal grains of zinc oxide and a grain boundary layer having a lower electric resistance than that of said crystal grains of zinc oxide being formed between crystal grains, and the resistor having a non-linear coefficient of voltage of 1.0 to 1.3 at 3×10 -3 to 80 A/cm 2 .
Claim 27
Dependent Claim
100 words
A composite sintered oxide resistor which is obtained by sintering a powdery oxide mixture consisting essentially of 0.1 to 10% by mole of magnesium oxide and 0.1 to 20% by mole of at least one yttrium oxide, gallium oxide, lanthanum oxide and indium oxide, the balance being zinc oxide, having crystal grains of zinc oxide and a grain boundary layer having a lower electric resistance than that of said crystal grains of zinc oxide being formed between crystal grains, and the resistor having a non-linear coefficient of voltage of 1.0 to 1.3 at 3×10 -3 to 80 A/cm 2 .
Claim 28
Dependent Claim
102 words
A composite sintered oxide resistor which is obtained by sintering a powdery oxide mixture consisting essentially of 68 to 90% by mole of zinc oxide, 3 to 10% by mole of magnesium oxide powder, 5 to 15% by mole of aluminum oxide and 1 to 2% by mole of silicon oxide, having crystal grains of zinc oxide and a grain boundary layer having a lower electric resistance than that of said crystal grains of zinc oxide being formed between crystal grains, and the resistor having a non-linear coefficient of voltage of 1.0 to 1.3 at 3×10 -3 to 80 A/cm 2 .
Claim 29
Dependent Claim
102 words
A composite sintered oxide resistor which is obtained by sintering a powdery oxide mixture consisting essentially of 68 to 90% by mole of zinc oxide, 3 to 10% by mole of magnesium oxide powder, 5 to 15% by mole of aluminum oxide and 1 to 2% by mole of silicon oxide, having crystal grains of zinc oxide and a grain boundary layer having a lower electric resistance than that of said crystal grains of zinc oxide being formed between crystal grains, and the resistor having a non-linear coefficient of voltage of 1.0 to 1.3 at 3×10 -3 to 80 A/cm 2 .
Claim 30
Dependent Claim
93 words
A composite sintered oxide resistor which is obtained by sintering a powdery oxide mixture consisting essentially of 70 to 92% by mole of zinc oxide, 3 to 10% by mole of magnesium oxide and 5 to 15% by mole of aluminum oxide, having crystal grains of zinc oxide and a grain boundary layer having a lower electric resistance than that of said crystal grains of zinc oxide being formed between crystal grains, and the resistor having a non-linear coefficient of voltage of 1.0 to 1.3 at 3×10 -3 to 80 A/cm 2 .
Claim 31
Dependent Claim
93 words
A composite sintered oxide resistor which is obtained by sintering a powdery oxide mixture consisting essentially of 70 to 92% by mole of zinc oxide, 3 to 10% by mole of magnesium oxide and 5 to 15% by mole of aluminum oxide, having crystal grains of zinc oxide and a grain boundary layer having a lower electric resistance than that of said crystal grains of zinc oxide being formed between crystal grains, and the resistor having a non-linear coefficient of voltage of 1.0 to 1.3 at 3×10 -3 to 80 A/cm 2 .
Claim 32
Dependent Claim
59 words
A composite sintered oxide resistor which is obtained by sintering a powdery oxide mixture containing zinc oxide, magnesium oxide, aluminum oxide, and silicon oxide, free of bismuth oxide, and having crystal grains of zinc oxide and a grain boundary layer having a lower electric resistance than that of said crystal grains of zinc oxide being formed between crystal grains.
Claim 33
Dependent Claim
59 words
A composite sintered oxide resistor which is obtained by sintering a powdery oxide mixture containing zinc oxide, magnesium oxide, aluminum oxide, and silicon oxide, free of bismuth oxide, and having crystal grains of zinc oxide and a grain boundary layer having a lower electric resistance than that of said crystal grains of zinc oxide being formed between crystal grains.
Claim 34
Dependent Claim
97 words
A composite sintered oxide resistor which is obtained by sintering a powdery oxide mixture consisting essentially of 65 to 94.8% by mole of zinc oxide, 0.2 to 154% by mole of magnesium oxide powder and 5 to 20% by mole of titanium oxide, having crystal grains of zinc oxide and a grain boundary layer having an electric resistance equal to or lower than that of said crystal grains of zinc oxide being formed between crystal grains, and the resistor having a non-linear coefficient of voltage of 1.0 to 1.3 at 3×10 -3 to 80 A/cm 2 .
Claim 35
Dependent Claim
97 words
A composite sintered oxide resistor which is obtained by sintering a powdery oxide mixture consisting essentially of 65 to 94.8% by mole of zinc oxide, 0.2 to 154% by mole of magnesium oxide powder and 5 to 20% by mole of titanium oxide, having crystal grains of zinc oxide and a grain boundary layer having an electric resistance equal to or lower than that of said crystal grains of zinc oxide being formed between crystal grains, and the resistor having a non-linear coefficient of voltage of 1.0 to 1.3 at 3×10 -3 to 80 A/cm 2 .
Claim 36
Dependent Claim
120 words
A composite sintered oxide resistor which is obtained by sintering a powdery oxide mixture containing 5 to 20% by mole of titanium oxide, 0.2 to 15% by mole of magnesium oxide, and 0.2 to 15% by weight of at least one oxide selected from the group consisting of antimony oxide, silicon oxide, zirconium oxide and tin oxide, the balance being zinc oxide, free from bismuth oxide, having crystal grains of zinc oxide and a grain boundary layer having an electric resistance equal to or lower than that of said crystal grains of zinc oxide being formed between crystal grains, and the resistor having a non-linear coefficient of voltage of 1.0 to 1.3 at 3×10 -3 to 80 A/cm 2 .
Claim 37
Dependent Claim
120 words
A composite sintered oxide resistor which is obtained by sintering a powdery oxide mixture containing 5 to 20% by mole of titanium oxide, 0.2 to 15% by mole of magnesium oxide, and 0.2 to 15% by weight of at least one oxide selected from the group consisting of antimony oxide, silicon oxide, zirconium oxide and tin oxide, the balance being zinc oxide, free from bismuth oxide, having crystal grains of zinc oxide and a grain boundary layer having an electric resistance equal to or lower than that of said crystal grains of zinc oxide being formed between crystal grains, and the resistor having a non-linear coefficient of voltage of 1.0 to 1.3 at 3×10 -3 to 80 A/cm 2 .
Claim 38
Dependent Claim
74 words
A composite sintered oxide resistor according to claim 26, wherein said powdery oxide mixture consists essentially of 65 to 94.8% by mole of zinc oxide, 5 to 20% by mole of titanium oxide, 0.2 to 15% by mole of magnesium oxide, 0.05 to 5% by mole of antimony oxide, 0.2 to 23% by mole of silicon oxide, 0.1 to 7% by mole of zirconium oxide, and 0.1 to 6% by mole of tin oxide.
Claim 39
Dependent Claim
40 words
A gas circuit breaker with an oxide resistor which comprises an oxide resistor being a composite sintered oxide resistor according to claim 10 and having a column or cylindrical form and electrodes on both end surfaces excluding the side surface.
Claim 40
Dependent Claim
24 words
A gas circuit breaker according to claim 28, wherein an insulating glass is provided by baking on the entire side surface of the resistor.
Claim 41
Dependent Claim
42 words
An SF 6 gas-insulated neutral grounding with an oxide resistor, which comprises an oxide resistor being a composite sintered oxide resistor according to claim 10 and having a column or cylindrical form and electrodes on both end surfaces excluding the side surface.
Claim 42
Dependent Claim
24 words
An SF 6 gas-insulated neutral grounding according to claim 30, wherein the electrodes are formed at inner positions other than the peripheral side surface.
Claim 43
Dependent Claim
18 words
A composite sintered oxide resistor according to claim 10, wherein said powdery oxide mixture further contains magnesium oxide.
References Cited (Backward Citations)
US4386021A
Cited
US4439651A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-04-05 | 1991-10-05 | 1992-04-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-04-05 | 1995-10-05 | 1996-04-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-04-05 | 1999-10-05 | 2000-04-05 | $7700.00 | Window Closed / Lapsed |