US4735909A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for forming a polycrystalline monolayer
Assignee: Photon Energy Inc
•
Filing: 1986-10-14
•
Granted: 1988-04-05
•
Expires: 2006-10-14
Abstract
Abstract Improved techniques are provided for forming a very thin polycrystalline layer of a semiconductor material on a glass substrate. The film material may be formed from a slurry of a semiconductor powder and a liquid carrier, and the slurry economically applied at room temperature by spraying techniques. Once dried, the film is compressed by the application of a substantial mechanical force. The compressed film is regrown in a heated atmosphere, forming a polycrystalline film comprised of large mean diameter crystals, with many crystals having a mean diameter in excess of the film thickness. A high quality cadmium sulfide polycrystalline film suitable for forming a photovoltaic cells may be inexpensively manufactured according to these techniques.
Inventors
- 👤 Scot P. Albright
- 👤 David K. Brown
- 👤 John F. Jordon
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 22:44
CPC Classifications
H; H10; H10F; H10F71/00; H10F10/00; H10F10/10; H10F10/16; H10F10/169; H10F71/125; H10F77/00; H10F77/10; H10F77/16; H10F77/162; H10F77/164; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/543; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
156 words
A method of forming an improved cadmium sulfide polycrystalline film over an electrically-conductive surface of a glass substrate, comprising: mixing a cadmium sulfide powder and a liquid carrier to form a cadmium sulfide-bearing slurry of a desired consistency; spraying the slurry while at substantially ambient temperature to form a cadmium sulfide containing layer on the electrically-conductive surface of the glass substrate; drying the applied slurry to evaporate at least substantially the entirety of the liquid carrier from the cadmium sulfide containing layer and forming a polycrystalline cadmium sulfide film comprised of relatively small-sized crystals on the glass substrate; applying compressive force to the polycrystalline film to substantially reduce the film thickness; heating the compressed polycrystalline film and substrate to form a cadmium sulfide polycrystalline film highly transmissive of light incident upon the glass substrate and comprised of relatively larger-sized crystals having a mean diameter equal to or greater than the thickness of the film after heating.
Claim 2
Independent Claim
156 words
A method of forming an improved cadmium sulfide polycrystalline film over an electrically-conductive surface of a glass substrate, comprising: mixing a cadmium sulfide powder and a liquid carrier to form a cadmium sulfide-bearing slurry of a desired consistency; spraying the slurry while at substantially ambient temperature to form a cadmium sulfide containing layer on the electrically-conductive surface of the glass substrate; drying the applied slurry to evaporate at least substantially the entirety of the liquid carrier from the cadmium sulfide containing layer and forming a polycrystalline cadmium sulfide film comprised of relatively small-sized crystals on the glass substrate; applying compressive force to the polycrystalline film to substantially reduce the film thickness; heating the compressed polycrystalline film and substrate to form a cadmium sulfide polycrystalline film highly transmissive of light incident upon the glass substrate and comprised of relatively larger-sized crystals having a mean diameter equal to or greater than the thickness of the film after heating.
Claim 3
Dependent Claim
24 words
The method as defined in claim 1 wherein the slurry is sprayed on the substrate while the substrate is in a substantially horizontal plane.
Claim 4
Dependent Claim
46 words
The method as defined in claim 2, further comprising: arranging a series of substrate panels on a horizontally moving conveyor belt; and the slurry is sprayed from one or more guns positioned above the conveyor belt and moving traversely with respect to the moving substrate panels.
Claim 5
Dependent Claim
25 words
The method as defined in claim 1, wherein the applied slurry is dried at a temperature between ambient temperature and the liquid carrier boiling point.
Claim 6
Dependent Claim
32 words
The method as defined in claim 1, wherein the step of applying a compressive force to the polycrystalline film comprises: applying a compressive force in excess of 5,000 p.s.i. to the film.
Claim 7
Dependent Claim
31 words
The method is defined in claim 5, wherein the compressive force is applied to the film by one or more rollers exerting a force perpendicular to the plane of the substrate.
Claim 8
Dependent Claim
27 words
The method as defined in claim 5, wherein the application of compressive force reduces the film thickness from approximately 50% to approximately 70% of its precompressed thickness.
Claim 9
Dependent Claim
48 words
The method as defined in claim 1, wherein the step of heating the compressed film comprises: positioning one or more glass substrates in a substantially vertical plane; and thereafter heating the substrate in an atmosphere containing an inert gas and at a temperature in excess of 480° C.
Claim 10
Dependent Claim
60 words
The method as defined in claim 8, wherein: the step of mixing the slurry includes mixing a flux material with the cadmium sulfide powder and the liquid carrier; and the step of positioning the glass substrate in a vertical plane includes positioning the polycrystalline cadmium sulfide film layers in a face-to-face relationship for maintaining a desired concentration of flux vapor.
Claim 11
Dependent Claim
14 words
The method as defined in claim 9 wherein the flux material is cadmium chloride.
Claim 12
Dependent Claim
34 words
The method as defined in claim 1, wherein the compressed film and substrate are heated to a temperature in the range of from 480° C. to 580° C. to form the relatively larger-sized crystals.
Claim 13
Dependent Claim
37 words
The method as defined in claim 11, wherein the compressed film and substrate are heated for a time period such that a majority of the relatively larger-sized crystals have a mean diameter of at least 7 microns.
Claim 14
Dependent Claim
170 words
An improved method of forming a large crystal polycrystalline film highly transmissive of light on a rigid substrate, comprising: mixing a selected powder suitable for forming the polycrystalline layer and a liquid carrier to form a slurry of a desired consistency; applying the slurry while at substantially ambient temperature to form a polycrystalline layer on the substrate; drying the applied slurry to evaporate at least substantially the entirety of the liquid carrier and forming a polycrystalline film on the substrate having relatively small diameter crystals; applying a compressive force to the polycrystalline film to reduce the film thickness to a thickness less than approximately 70% of its precompressed thickness; and heating the compressed film and substrate to a temperature sufficient to form a semiconductor film comprised of crystals having a mean diameter substantially greater than the diameter of the crystals prior to heating, such that the mean diameter of at least some of the crystals after heating is equal to or greater than the thickness of the film after heating.
Claim 15
Dependent Claim
170 words
An improved method of forming a large crystal polycrystalline film highly transmissive of light on a rigid substrate, comprising: mixing a selected powder suitable for forming the polycrystalline layer and a liquid carrier to form a slurry of a desired consistency; applying the slurry while at substantially ambient temperature to form a polycrystalline layer on the substrate; drying the applied slurry to evaporate at least substantially the entirety of the liquid carrier and forming a polycrystalline film on the substrate having relatively small diameter crystals; applying a compressive force to the polycrystalline film to reduce the film thickness to a thickness less than approximately 70% of its precompressed thickness; and heating the compressed film and substrate to a temperature sufficient to form a semiconductor film comprised of crystals having a mean diameter substantially greater than the diameter of the crystals prior to heating, such that the mean diameter of at least some of the crystals after heating is equal to or greater than the thickness of the film after heating.
Claim 16
Dependent Claim
27 words
The method as defined in claim 13, wherein the application of compressive force reduces the film thickness from approximately 50% to approximately 70% of its precompressed thickness.
Claim 17
Dependent Claim
44 words
The method as defined in claim 13, wherein the step of applying the slurry comprises: arranging a series of substrate panels on a horizontally moving conveyor belt; and spraying the slurry on the substrate panels, while the panels are in a substantially horizontal position.
Claim 18
Independent Claim
225 words
The method of forming an improved light-transmissive polycrystalline cadmium sulfide layer for a back-wall photovoltaic cell having a light-transmissive substrate, an electrically conductive light-transmissive film overlying a surface of the substrate, the cadmium sulfide layer overlying the electrically conductive film, and another polycrystalline layer overlying the cadmium sulfide layer and forming a photovoltaic heterojunction therewith, comprising: mixing a cadmium sulfide power and a liquid carrier to form a cadmium sulfide-bearing slurry of a desired consistency; applying the slurry while at a substantially ambient temperature to form a cadmium sulfide containing layer on the electrically conductive light-transmissive film overlying the surface of the glass substrate; drying the applied slurry to evaporate at least substantially the entirety of the liquid carrier from the cadmium sulfide containing layer and forming a polycrystalline cadmium sulfide layer comprised of relatively small-sized crystals on the glass substrate; applying a compressive force to the polycrystalline layer to reduce the layer thickness to a thickness less than approximately 70% of its precompressed thickness; and heating the compressed polycrystalline layer and substrate to a temperature sufficient to form a cadmium sulfide polycrystalline layer highly transmissive of light incident upon the substrate and comprised of relatively larger-sized, crystals such that the mean diameter of at least some of the crystals after heating is equal to or greater than the thickness of the film after heating.
Claim 19
Independent Claim
225 words
The method of forming an improved light-transmissive polycrystalline cadmium sulfide layer for a back-wall photovoltaic cell having a light-transmissive substrate, an electrically conductive light-transmissive film overlying a surface of the substrate, the cadmium sulfide layer overlying the electrically conductive film, and another polycrystalline layer overlying the cadmium sulfide layer and forming a photovoltaic heterojunction therewith, comprising: mixing a cadmium sulfide power and a liquid carrier to form a cadmium sulfide-bearing slurry of a desired consistency; applying the slurry while at a substantially ambient temperature to form a cadmium sulfide containing layer on the electrically conductive light-transmissive film overlying the surface of the glass substrate; drying the applied slurry to evaporate at least substantially the entirety of the liquid carrier from the cadmium sulfide containing layer and forming a polycrystalline cadmium sulfide layer comprised of relatively small-sized crystals on the glass substrate; applying a compressive force to the polycrystalline layer to reduce the layer thickness to a thickness less than approximately 70% of its precompressed thickness; and heating the compressed polycrystalline layer and substrate to a temperature sufficient to form a cadmium sulfide polycrystalline layer highly transmissive of light incident upon the substrate and comprised of relatively larger-sized, crystals such that the mean diameter of at least some of the crystals after heating is equal to or greater than the thickness of the film after heating.
Claim 20
Dependent Claim
28 words
The method as defined in claim 16, wherein the slurry is applied by spraying the slurry on the substrate while the substrate is in a substantially horizontal plane.
Claim 21
Dependent Claim
46 words
The method as defined in claim 17, further comprising: arranging a series of substrate panels on a horizontally moving conveyor belt; and the slurry is sprayed from one or more guns positioned above the conveyor belt and moving traversely with respect to the moving substrate panels.
Claim 22
Dependent Claim
66 words
The method as defined in claim 16, wherein: the step of mixing the slurry includes mixing a flux material the cadmium sulfide powder and the liquid carrier; and the step of heating the compressed film and substrate includes positioning a plurality of glass substrates in a substantially vertically plane with the polycrystalline cadmium sulfide layers in face-to-face relationship for maintaining a desired concentration of flux vapor.
Claim 23
Dependent Claim
34 words
The method as defined in claim 16, wherein the compressed film and substrate are heated to a temperature in the range of from 480° C. to 580° C. to form the relatively larger-sized crystals.
References Cited (Backward Citations)
US4362896A
Cited
US4609567A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-04-05 | 1991-10-05 | 1992-04-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-04-05 | 1995-10-05 | 1996-04-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-04-05 | 1999-10-05 | 2000-04-05 | $7700.00 | Window Closed / Lapsed |