US4735854A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Polymeric article for transfer to a substrate
Assignee: JACOB SCHLAEPFER AND CO AG
•
Filing: 1984-02-15
•
Granted: 1988-04-05
•
Expires: 2004-02-15
Abstract
Abstract The invention relates to a method of applying polymeric materials to the surface of a substrate by providing a layer of polymeric material on a release sheet and then subsequently transferring the polymeric material from the release sheet by the application of heat and pressure sufficient to effect adhesion of the polymeric material to the substrate and thereafter peeling the release sheet from the polymeric material. The invention is particularly concerned with the application of polymeric materials being capable of a secondary reaction at the time of application to the substrate or subsequent thereto.
Inventors
- 👤 Alfred E. Lauchenauer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 21:34
CPC Classifications
D; D06; D06M; D06M23/00; Y; Y10; Y10S; Y10S428/00; Y10S428/914; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/28; Y10T428/2813; Y10T428/2817
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
118 words
A polymeric article adapted for heat and pressure transfer to a substrate, said article comprising a layer of composite polymeric material having temporarily adhered thereto a sheet material adapted to act as a release sheet, said composite polymeric material being adapted to be secured to a substrate on application of heat and pressure sufficient to tackify said material and allow the release sheet to be removed; wherein components of said composite polymeric material are capable of undergoing an interraction which modifies its chemical structure when a temperature significantly higher than the tackifying temperature is applied in the absense of pressure and after the article has been secured to the substrate and the sheet material removed from the article.
Claim 2
Dependent Claim
118 words
A polymeric article adapted for heat and pressure transfer to a substrate, said article comprising a layer of composite polymeric material having temporarily adhered thereto a sheet material adapted to act as a release sheet, said composite polymeric material being adapted to be secured to a substrate on application of heat and pressure sufficient to tackify said material and allow the release sheet to be removed; wherein components of said composite polymeric material are capable of undergoing an interraction which modifies its chemical structure when a temperature significantly higher than the tackifying temperature is applied in the absense of pressure and after the article has been secured to the substrate and the sheet material removed from the article.
Claim 3
Dependent Claim
32 words
An article according to claim 1, wherein the inter-reaction is such as to increase intermolecular cohesion, and in that the temperature selected is 10 to 100° C. higher than the tackifying temperature.
Claim 4
Dependent Claim
25 words
An article according to claim 1 when said composite polymeric material comprises two or more layers which chemically or physiochemically inter-react above the tackifying temperature.
Claim 5
Dependent Claim
28 words
An article as claimed in claim 1 wherein the interreaction is a blowing reaction and the temperature selected from 10° to 100° C. higher than the tackifying temperature.
Claim 6
Dependent Claim
40 words
An article as claimed in claim 1 wherein said composite polymeric material includes a proportion of an acrylate containing a blowing agent, polyethlene powder, a polyacrylate thickener, ammonia, water, a fatty amid softener, a silicone antifoaming agent and a pigment.
Claim 7
Dependent Claim
50 words
An article as claimed in claim 1 wherein said composite polymeric material includes 24 parts acrylate containing a blowing agent, 20 parts polyethylene powder, 10parts polyacrylate thickener, 2 parts 20% solution of ammonia, 28 parts water, 4 parts fatty amid softener, 3 parts silicone antifoaming agent, and 0.10 parts pigment.
Claim 8
Dependent Claim
50 words
An article as claimed in claim 1 wherein said composite polymeric material includes: 100 parts cross linkable polyacrylate, 20 parts acrylate containing a blowing agent, 5 parts melamine formaldehyde percondensate, 0.10 part pigment, 2 parts silicone antifoaming agent, 5 parts acrylic copolymer thickening agent, 20 parts methyl cellulose (4% solution).
References Cited (Backward Citations)
US2559649A
Cited
US2644262A
Cited
US3523846A
Cited
GB1215914A
Cited
GB1469955A
Cited
US4171398A
Cited
US4151319A
Cited
US4275106A
Cited
US4219596A
Cited
US4326005A
Cited
US4388137A
Cited
US4322461A
Cited
GB2090193A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-04-05 | 1991-10-05 | 1992-04-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-04-05 | 1995-10-05 | 1996-04-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-04-05 | 1999-10-05 | 2000-04-05 | $7700.00 | Window Closed / Lapsed |