Method for the production of silver halide emulsion
Assignee: Konica Minolta Inc
•
Filing: 1986-05-22
•
Granted: 1988-03-01
•
Expires: 2006-05-22
Abstract
Abstract The present invention is to provide a method for uniforming a group of silver halide particles of a silver halide emulsion to be used in a silver halide photographic light-sensitive material into a group of particles which is monodispersive and whose crystal habit is tetradecahedral or octahedral so that the complication and instabilization of the conventional particles can be reduced to be processed. Namely, in a process for growing particles in which a water-soluble silver salt is added to a core emulsion and a silver halide is produced to add to the core, this method is to adjust the pAg values of an emulsion being applied to the abovementioned process to increase by not less than 0.3 multistepwise or continuously.
Inventors
- 👤 Toshihiko Yagi
- 👤 Toshifumi Iijima
- 👤 Syoji Matsuzaka
- 👤 Hisashi Yamaguchi
- 👤 Mikio Miura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 17:00
CPC Classifications
G; G03; G03C; G03C1/00; G03C1/005; G03C1/015; G03C1/035; G03C2001/03535; G03C2001/0357
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
109 words
A method of preparing a silver halide emulsion comprising the steps of: (a) producing monodispersed silver halide particles of cubic and/or tetradecahedral shape in an aqueous hydrophilic colloidal solution, the silver halide particles consisting essentially of silver iodobromide, silver chloroiodobromide or a mixture therefore containing from 0.5 to 10 mole % of silver iodide; (b) increasing the pAg value of the aqueous hydrophilic colloidal solution by not less than 0.3 either stepwise involving not less than three steps or continuously by adding an aqueous water-soluble silver salt solution and an aqueous water-soluble halide solution to the hydrophilic coloidal solution to form silver halide particles of octahedronal and/or tetradecahedronal shape.
Claim 2
Independent Claim
109 words
A method of preparing a silver halide emulsion comprising the steps of: (a) producing monodispersed silver halide particles of cubic and/or tetradecahedral shape in an aqueous hydrophilic colloidal solution, the silver halide particles consisting essentially of silver iodobromide, silver chloroiodobromide or a mixture therefore containing from 0.5 to 10 mole % of silver iodide; (b) increasing the pAg value of the aqueous hydrophilic colloidal solution by not less than 0.3 either stepwise involving not less than three steps or continuously by adding an aqueous water-soluble silver salt solution and an aqueous water-soluble halide solution to the hydrophilic coloidal solution to form silver halide particles of octahedronal and/or tetradecahedronal shape.
Claim 3
Dependent Claim
28 words
A method according to claim 1, wherein said method is for the production of a silver halide emulsion comprising silver halide particles consisting essentially of a silver iodobromide.
Claim 4
Dependent Claim
17 words
A method according to claim 1, wherein said method comprises a step of using a seed emulsion.
Claim 5
Dependent Claim
54 words
A method according to claim 1, wherein silver halide particles of cubic shape are made present in said hydrophilic colloid solution at the time of initiation of said pAg-increasing step and silver halide particles present in said hydrophilic solution at the time of completion of said pAg-increasing step are in the form of octahedron.
Claim 6
Dependent Claim
17 words
A method according to claim 2, wherein said silver halide particles are core/shell type silver halide particles.
Claim 7
Dependent Claim
21 words
A method according to claim 5, wherein said core/shell type silver halide particles have a thickness from 0.01 to 0.3 μm.
Claim 8
Dependent Claim
30 words
The method of claim 1, further comprising the step of decreasing the size of the silver halide particles after step (a) and before step (b) by decreasing the pAg value.
References Cited (Backward Citations)
US3000739A
Cited
US3598593A
Cited
US3736144A
Cited
US3821002A
Cited
US4063951A
Cited
US4309501A
Cited
US4242445A
Cited
US4433048A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-03-01 | 1991-08-31 | 1992-03-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-03-01 | 1995-08-31 | 1996-03-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-03-01 | 1999-08-31 | 2000-03-01 | $7700.00 | Window Closed / Lapsed |