Glass fibers for reinforcing polymers
Assignee: PPG Industries Inc
•
Filing: 1986-05-07
•
Granted: 1988-03-01
•
Expires: 2006-05-07
Abstract
Abstract Glass fibers are prepared with a chemical treatment resulting in chemically treated glass fibers having utility in reinforcing thermoplastic polymers such as polyolefins. The chemically treated glass fibers have a dried residue of an aqueous chemical treating composition having one or more amino organo coupling agents, an aqueous emulsion of an acid or anhydride modified polyolefin having one or more surfactants, wherein the polyolefin is neutralized with an organic or inorganic base with a basicity less than the basicity of the amino moiety of the coupling agent, a binder stabilizer, one or more film forming polymers, and water. The aqueous chemical treating composition is essentially free of cationic lubricants that are amidated fatty acids and polyvinyl acetate homopolymer. The chemically treated glass fibers can be prepared in a wet chop or dry chop process, wherein the chopped glass fiber strands eventually have a moisture content of less than 20 weight percent prior to volatilization of the formed moisture. The chemically treated glass fibers are used to reinforce thermoplastic polymers such as polyolefins and particularly polypropylene in any molding operation to produce glass fiber reinforced thermoplastic articles.
Inventors
- 👤 Chester S. Temple
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 02:19
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/04; C08J5/06; C08J5/08; C03; C03C; C03C25/00; C03C25/10; C03C25/24; C03C25/26; C08J2323/00; C08J2323/02; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2938; Y10T428/2962; Y10T428/2964
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
256 words
Glass fibers having an aqueous chemical treating composition on a substantial portion of the fibers in the strands, wherein the aqueous chemical treating composition comprises: a. one or more amino organo coupling agents present in an effective coupling agent amount and having a primary amine with a basicity greater than diethyl ethanolamine, b. an aqueous emulsion of acid or anhydride modified polyolefin having one or more surfactants, wherein the polyolefin is neutralized with diethyl ethanolamine and wherein the polyolefin emulsion is present in an amount to result in a predominant amount of the solids of the aqueous chemical treating composition being polyolefin, c. a binder stabilzier, d. an aqueous dispersion of a film forming polymer selected from the group consisting of water soluble, dispersible or emulsifiable polyurethanes, epoxies, polyesters, and copolymers formed from the monomers used in preheating these homopolymers and blends of the homopolymers or copolymers, wherein the film forming polymer is free of polyvinyl acetate homopolymer and wherein the film forming polymer is present in the aqueous chemical treating composition in an amount less than the polyolefin emulsion, and e. water in an amount to give a total solids for the aqueous chemical treating composition in the range of about 1 to about 25 weight percent and a viscosity so that the aqueous chemical treating composition can be applied to glass fibers as they are formed, wherein the aqueous chemical treating composition is essentially free of cationic lubricants that are formed from amidated fatty acids formed by the reaction of fatty acids and polyamines.
Claim 2
Dependent Claim
256 words
Glass fibers having an aqueous chemical treating composition on a substantial portion of the fibers in the strands, wherein the aqueous chemical treating composition comprises: a. one or more amino organo coupling agents present in an effective coupling agent amount and having a primary amine with a basicity greater than diethyl ethanolamine, b. an aqueous emulsion of acid or anhydride modified polyolefin having one or more surfactants, wherein the polyolefin is neutralized with diethyl ethanolamine and wherein the polyolefin emulsion is present in an amount to result in a predominant amount of the solids of the aqueous chemical treating composition being polyolefin, c. a binder stabilzier, d. an aqueous dispersion of a film forming polymer selected from the group consisting of water soluble, dispersible or emulsifiable polyurethanes, epoxies, polyesters, and copolymers formed from the monomers used in preheating these homopolymers and blends of the homopolymers or copolymers, wherein the film forming polymer is free of polyvinyl acetate homopolymer and wherein the film forming polymer is present in the aqueous chemical treating composition in an amount less than the polyolefin emulsion, and e. water in an amount to give a total solids for the aqueous chemical treating composition in the range of about 1 to about 25 weight percent and a viscosity so that the aqueous chemical treating composition can be applied to glass fibers as they are formed, wherein the aqueous chemical treating composition is essentially free of cationic lubricants that are formed from amidated fatty acids formed by the reaction of fatty acids and polyamines.
Claim 3
Dependent Claim
32 words
Glass fibers of claim 1, wherein the moisture content of the glass fiber prior to drying is in the range of about 8 to about 14 weight percent of the glass fibers.
Claim 4
Dependent Claim
13 words
Glass fibers of claim 2, having a percent LOI of less than 2.
Claim 5
Dependent Claim
16 words
Glass fibers of claim 2, having a percent LOI in the range of 0.6 to 0.9.
Claim 6
Dependent Claim
42 words
Glass fibers of claim 1, wherein the acid neutralized polyolefin is selected from the group consisting of maleonated amorphous polypropylene, maleonated isotactic polypropylene, blends of maleonated polypropylene and polyethylene with the polyethylene present up to about 25 weight percent of the blend.
Claim 7
Dependent Claim
23 words
Glass fibers of claim 1, wherein the pH of the aqueous chemical treating composition is in the range of about 7.5 to 8.5.
Claim 8
Dependent Claim
26 words
Glass fibers of claim 1, wherein the solids content of the aqueous chemical treating composition is in the range of about 5 to 6 weight percent.
Claim 9
Dependent Claim
24 words
Glass fibers of claim 1, wherein the amino organo coupling agent is an amino organo functional silane selected from monoamino silanes and diamino silanes.
Claim 10
Dependent Claim
32 words
Glass fibers of claim 1 that are chopped glass fiber strands, wherein the binder stabilizer is selected from the group consisting of organic dicarboxlic acids that are saturated, unsaturated, aliphatic or aromatic.
Claim 11
Dependent Claim
27 words
Glass fiber strands of claim 11, wherein the glass fibers before drying have a moisture content in the range of about 8 to about 14 weight percent.
Claim 12
Dependent Claim
25 words
Glass fiber strands of claim 9, having an LOI of the aqueous chemical treating composition in the range of about less than 2 percent LOI.
Claim 13
Dependent Claim
32 words
Glass fiber strands claim 11, wherein the film forming polymer in the aqueous chemical treating composition is a blend of an aqueous dispersion of an epoxy polyurethane polymer and a polyurethane polymer.
Claim 14
Dependent Claim
43 words
Glass fiber strands of claim 11, wherein the acid neutralized polyolefin is selected from the group consisting of maleonated amorphous polypropylene, maleonated isotactic polypropylene, blends of maleonated polypropylene and polyethylene with the polythylene present up to about 5 weight percent of the blend.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-03-01 | 1991-08-31 | 1992-03-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-03-01 | 1995-08-31 | 1996-03-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-03-01 | 1999-08-31 | 2000-03-01 | $7700.00 | Window Closed / Lapsed |