Emulsion composition and method for use in treating glass fibers

Claim 2

An aqueous emulsion composition for use in a size composition for application to glass fibers, comprising: isotatic carboxylated polypropylene, amorphous carboxylated polyproplene, where both the isotactic and amorphous carboxylated polypropylene are prepared by modifying isotactic and amorphous polypropylene with ethylenically substituted polycarboxylic acid or anhydride, amide, or lower alkyl ester thereof, a base, a surfactant selected from the group consisting of cationic, anionic and nonionic, and water in amounts sufficient to make a composition having about 20 to about 40 percent solids by weight.

Claim 3

An aqueous emulsion of claim 1 wherein a portion of the amorphous carboxylated polypropylene is substituted with carboxylated polyethylene.

Claim 4

An aqueous emulsion of claim 1 wherein the amount of base used is in the range to produce an equivalent alkalinity to that of an amount of potassium hydroxide sufficient to provide a residual content of hydroxides ranging from about 16 to about 24 mg of hydroxide per gram of emulsion.

Claim 5

Aqueous emulsion of claim 1 wherein the base is potassium hydroxide in an amount sufficient to provide a residual content of hydroxides ranging from about 16 to about 24 mg of hydroxide per gram.

Claim 6

Aqueous emulsion of claim 1 wherein the surfactant is in an amount of about 2 to about 12 weight percent of the composition.

Claim 7

Aqueous emulsion of claim 1 wherein the surfactant is a nonionic ethoxylated phenol surfactant.

Claim 8

Aqueous emulsion of claim 1 wherein the ratio of amount of isotactic polypropylene polymer to the amount of amorphous carboxylated polypropylene is about 1 - about 1 to about 1 - about 4 parts by weight.

Claim 9

Aqueous emulsion of claim 1 wherein the base is an alkali or alkaline earth metal hydroxide.

Claim 10

Aqueous emulsion of claim 8 wherein the base is potassium hydroxide.

Claim 11

Aqueous emulsion of claim 1 wherein the base is an alkali metal salt of a strong base and weak acid.

Claim 12

Aqueous emulsion of claim 10 wherein the base is an alkali metal borate.

Claim 13

Aqueous emulsion of claim 11 wherein the base is sodium tetraborate decahydrate.

Claim 14

Aqueous emulsion of claim 1 wherein the base is an organic base.

Claim 15

Aqueous emulsion of claim 13 wherein the base is 2-aminomethylpropanol.

Claim 16

method of preparing an aqueous emulsion composition for facile emulsification if isotactic carboxylated polypropylene or a mixture of isotactic carboxylated polypropylene and isotactic carboxylated polyethylene, comprising: (1) melting the isotactic carboxylated polypropylene with the amorphous carboxylated polypropylene, both of which are prepared by modifying isotactic and amorphous polypropylene with ethylenically substituted polycarboxylic acid or anhydride, amide, or lower alkyl ester thereof; (2) adding to the melted mixture a base selected from the group consisting of alkali metal hydroxides, borax and 2-aminomethylpropanol and surfactants selected from cationic, anionic, and nonionic, (3) adding sufficient amount of water to make an emulsion having about 20 to about 40 percent solids by weight.

Claim 17

method of preparing an aqueous emulsion composition for facile emulsification if isotactic carboxylated polypropylene or a mixture of isotactic carboxylated polypropylene and isotactic carboxylated polyethylene, comprising: (1) melting the isotactic carboxylated polypropylene with the amorphous carboxylated polypropylene, both of which are prepared by modifying isotactic and amorphous polypropylene with ethylenically substituted polycarboxylic acid or anhydride, amide, or lower alkyl ester thereof; (2) adding to the melted mixture a base selected from the group consisting of alkali metal hydroxides, borax and 2-aminomethylpropanol and surfactants selected from cationic, anionic, and nonionic, (3) adding sufficient amount of water to make an emulsion having about 20 to about 40 percent solids by weight.

Claim 18

Method of claim 15 wherein the ratio of amount of isotactic carboxylated polypropylene to amount of amorphous carboxylated polypropylene is in the range of about 1: about 1 to about 1: about 4.

Claim 19

Method of claim 15 wherein the amount of base is in the range to produce an equivalent alkalinity to using an amount of potassium hydroxide sufficient to provide a residual content of hydroxides ranging from about 16 to about 24 mg of hydroxide per gram emulsion.

Claim 20

Method of claim 15 wherein the amount of surfactant is in the range of about 2 to about 12 percent by weight of the emulsion.

Claim 21

Aqueous emulsion composition of claim 1 wherein an amount of carboxylated polyethylene is present in addition to the amount of amorphous carboxylated polypropylene in an amount not exceeding about 75 weight percent of the olefin content in the blend of isotactic carboxylated polypropylene and amorphous carboxylated polypropylene.

Claim 22

An aqueous composition of claim 1 having a pH in the range of 8 to 9.5.

Claim 23

Method of claim 15 wherein an amount not exceeding about 75 weight percent of the olefin content of isotactic carboxylated polypropylene and amorphous carboxylated polypropylene or carboxylated polyethylene may be present in addition to the amount of amorphous carboxylated polypropylene.

Claim 24

Method of claim 15 wherein the emulsion having about 20 to about 40 percent solids has a pH in the range of 8 to 9.5.

Claim 25

Method of claim 15 wherein the melting is performed at a termperature in the range of about 106° C. to about 185° C.

Claim 26

An aqueous emulsion composition having emulsified isotactic carboxylated polypropylene, comprising: (a) a blend of isotactic carboxylated polypropylene and amorphous carboxylated polypropylene in amounts in a ratio in the range of about 1 part by weight of isotactic carboxylated polypropylene to about 1 part by weight of the amorphous carboxylated polypropylene to a ratio of 1 part of the isotactic carboxylated polypropylene to about 4 parts of the amorphous carboxylated polypropylene, where both the isotactic and amorphous carboxylated polypropylene are prepared by modifying isotactic and amorphous polypropeylene with ethylenically substituted polycarboxylic acid or anhydride, amide, or lower alkylester thereof, (b) a base in an amount of the range to produce an equivalent alkalinity to that of an amount of potassium hydroxide sufficient to provide a residual content of hydroxides ranging from about 16 to about 24 milligrams of hydroxide per gram of emulsion, (c) a surfactant selected from the group consisting of cationic, anionic, and nonionic in an amount in the range of about 2 to about 12 weight percent of the solids of the composition, and (d) water in amounts sufficient to make an emulsion composition having about 20 to about 40 percent solids wherein the pH is in the range of about 8 to 9.5.

Claim 27

An aqueous emulsion composition having emulsified isotactic carboxylated polypropylene, comprising: (a) a blend of isotactic carboxylated polypropylene and amorphous carboxylated polypropylene in amounts in a ratio in the range of about 1 part by weight of isotactic carboxylated polypropylene to about 1 part by weight of the amorphous carboxylated polypropylene to a ratio of 1 part of the isotactic carboxylated polypropylene to about 4 parts of the amorphous carboxylated polypropylene, where both the isotactic and amorphous carboxylated polypropylene are prepared by modifying isotactic and amorphous polypropeylene with ethylenically substituted polycarboxylic acid or anhydride, amide, or lower alkylester thereof, (b) a base in an amount of the range to produce an equivalent alkalinity to that of an amount of potassium hydroxide sufficient to provide a residual content of hydroxides ranging from about 16 to about 24 milligrams of hydroxide per gram of emulsion, (c) a surfactant selected from the group consisting of cationic, anionic, and nonionic in an amount in the range of about 2 to about 12 weight percent of the solids of the composition, and (d) water in amounts sufficient to make an emulsion composition having about 20 to about 40 percent solids wherein the pH is in the range of about 8 to 9.5.

Claim 28

Glass fibers sized with the dried residue of an aqueous sizing composition having a percent by weight of the aqueous sizing composition, comprising: a. about 2 to about 15 percent of an aqueous emulsion having:

Claim 29

Glass fibers sized with the dried residue of an aqueous sizing composition having a percent by weight of the aqueous sizing composition, comprising: a. about 2 to about 15 percent of an aqueous emulsion having:

Claim 30

isotactic carboxylated polypropylene, 2. amorphous carboxylated polyproylene, 3. a base, 4. a surfactant selected from the group consisting of cationic, anionic and nonionic, 5. water in amount sufficient to make an aqueous emulsion having about 20 to about 40 percent solids; b. about 0.1 to about 2 percent of a silane coupling agent; c. about 0.4 to about 12 percent of a film former; d. about 0.2 to about 4 percent of a lubricant; e. the remaining amount being water to give a total solids content in the range of about 2 to about 20 weight percent.

Claim 31

isotactic carboxylated polypropylene, 2. amorphous carboxylated polyproylene, 3. a base, 4. a surfactant selected from the group consisting of cationic, anionic and nonionic, 5. water in amount sufficient to make an aqueous emulsion having about 20 to about 40 percent solids; b. about 0.1 to about 2 percent of a silane coupling agent; c. about 0.4 to about 12 percent of a film former; d. about 0.2 to about 4 percent of a lubricant; e. the remaining amount being water to give a total solids content in the range of about 2 to about 20 weight percent.

Claim 32

Glass fibers of claim 25 wherein the coupling agent in the sizing composition is an aminosilane.

Claim 33

Glass fibers of claim 25 wherein the film former is selected from the group consisting of homopolymers and copolymers of vinyl acetates, epoxies, polyesters, polyurethenes, acrylic polymers and coreaction products thereof.

Claim 34

Glass fibers of claim 25 wherein the dried residue of the aqueous sizing composition has present polypropylene which was present in the aqueous emulsion in the amount of 0.5 to about 75 percent by weight when the blend of isotactic carboxylated polypropylene and amorphous carboxylated polypropylene was present in an amount of 25 to 99.5 percent by weight.

Claim 35

Laminate of glass fiber reinforced polyolefin having the glass fibers of claim 25.