Crystalline 1-butene polymer composition
Assignee: Mitsui Chemicals Inc
•
Filing: 1987-02-20
•
Granted: 1988-02-23
•
Expires: 2007-02-20
Abstract
Abstract The composition of crystalline 1-butene polymer comprising: (a) a crystalline 1-butene polymer containing a 1-butene component as a main component, and (b) a radical-treated crystalline olefinic polymer having (1) a boiling p-xylene-insoluble content of 30% by weight at most and (2) the relation satisfying the following expression TcCL-TcO>/=1 wherein TcCL is the crystallization temperature ( DEG C.) of the radical-treated crystalline olefinic polymer, and TcO is the crystallization temperature of the crystalline olefinic polymer before the radical treatment, and (c) the proportion of the radical-treated crystalline olefinic polymer (b) being 0.2 to 100 parts by weight per 100 parts by weight of the crystalline 1-butene polymer (a).
Inventors
- 👤 Masaki Kohyama
- 👤 Hiroyuki Hori
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 02:02
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/02; C08L23/18; C08L23/20; Y; Y10; Y10S; Y10S525/00; Y10S525/938; Y10S526/00; Y10S526/914
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
157 words
A crystalline 1-butene polymer composition comprising: (a) a crystalline 1-butene polymer containing a 1-butene component as a main component, and (b) a radical-treated crystalline propylene polymer having the relation satisfying the following expressions: T.sub.C.sup.CL -T.sub.C.sup.0 ≧10 wherein T C CL is the crystallization temperature (°C.) of the radical-treated crystalline propylene polymer, and T C 0 is the crystallization temperature of the crystalline propylene polymer before the radical treatment, and ##EQU3## wherein MFR 0 (g/10 min) is the melt flow rate of the crystalline polymer before treatment and MFR CL (g/10 min) is the melt flow rate of the crystalline polymer after treatment, and (c) the proportion of the radical-treated crystalline propylene polymer (b) being 0.2 to 100 parts by weight of the crystalline 1-butene polymer (a), said treatment being effected in the presence of a cross linking agent and a polymerization initiator, or by irradiating light onto the crystalline polymer in the presence of a photopolymerization initiator.
Claim 2
Dependent Claim
157 words
A crystalline 1-butene polymer composition comprising: (a) a crystalline 1-butene polymer containing a 1-butene component as a main component, and (b) a radical-treated crystalline propylene polymer having the relation satisfying the following expressions: T.sub.C.sup.CL -T.sub.C.sup.0 ≧10 wherein T C CL is the crystallization temperature (°C.) of the radical-treated crystalline propylene polymer, and T C 0 is the crystallization temperature of the crystalline propylene polymer before the radical treatment, and ##EQU3## wherein MFR 0 (g/10 min) is the melt flow rate of the crystalline polymer before treatment and MFR CL (g/10 min) is the melt flow rate of the crystalline polymer after treatment, and (c) the proportion of the radical-treated crystalline propylene polymer (b) being 0.2 to 100 parts by weight of the crystalline 1-butene polymer (a), said treatment being effected in the presence of a cross linking agent and a polymerization initiator, or by irradiating light onto the crystalline polymer in the presence of a photopolymerization initiator.
Claim 3
Dependent Claim
155 words
A crystalline 1-butene polymer composition comprising: (a) a crystalline 1-butene polymer containing a 1-butene component as a main component, and (b) a radical-treated crystalline 4-methyl-1-pentene polymer having the relationship satisfying the following expressions: T.sub.C.sup.CL -T.sub.C.sup.0 ≧2 wherein T C CL is the crystallization temperature (°C.) of the radical-treated crystalline 4-methyl-1-pentene polymer, and T C 0 is the crystallization temperature of the crystalline 4-methyl-1-pentene polymer before radical treatment, and ##EQU4## wherein MFR 0 (g/10 min) is the melt flow rate of the crystalline polymer before treatment and MFR CL (g/10 min) is the melt flow rate of the crystalline polymer after treatment, and (c) the proportion of the radial-treated crystalline 4-methyl-1-pentene (b) being 0.2 to 100 parts by weight of the crystalline 1-butene polymer (a), said treatment being effected in the presence of a cross linking agent and a polymerization initiator, or by irradiating light onto the crystalline polymer in the presence of a photopolymerization initiator.
Claim 4
Dependent Claim
155 words
A crystalline 1-butene polymer composition comprising: (a) a crystalline 1-butene polymer containing a 1-butene component as a main component, and (b) a radical-treated crystalline 4-methyl-1-pentene polymer having the relationship satisfying the following expressions: T.sub.C.sup.CL -T.sub.C.sup.0 ≧2 wherein T C CL is the crystallization temperature (°C.) of the radical-treated crystalline 4-methyl-1-pentene polymer, and T C 0 is the crystallization temperature of the crystalline 4-methyl-1-pentene polymer before radical treatment, and ##EQU4## wherein MFR 0 (g/10 min) is the melt flow rate of the crystalline polymer before treatment and MFR CL (g/10 min) is the melt flow rate of the crystalline polymer after treatment, and (c) the proportion of the radial-treated crystalline 4-methyl-1-pentene (b) being 0.2 to 100 parts by weight of the crystalline 1-butene polymer (a), said treatment being effected in the presence of a cross linking agent and a polymerization initiator, or by irradiating light onto the crystalline polymer in the presence of a photopolymerization initiator.
References Cited (Backward Citations)
US4546150A
Cited
US4677025A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-02-22 | 1991-08-24 | 1992-02-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-02-22 | 1995-08-24 | 1996-02-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-02-22 | 1999-08-24 | 2000-02-23 | $7700.00 | Window Closed / Lapsed |