Strengthened glass articles and method for making
Assignee: Corning Glass Works
•
Filing: 1985-06-10
•
Granted: 1988-02-23
•
Expires: 2005-06-10
Abstract
Abstract This invention is directed to the production of unitary, transparent glass articles demonstrating exceptionally high flexural and impact strengths composed of an interior portion and an integral surface compression layer. The articles are prepared by contacting glass bodies consisting essentially, in mole percent, of 14-24% R 2 O, wherein R 2 O consists of 0-5% Li 2 O, 0-5% K 2 O, and the remainder Na 2 O, 17-21% Al 2 o 3 , 45-60% SiO 2 , 3-6% TiO 2 and/or ZrO 2 , and 0-2% P 2 O 5 , the sum of those components constituting at least 85% of the total composition, at a temperature above the annealing point of the glass with a source of Li + ions to replace at least part of the Na + ions and, if present, K + ions in a surface layer with a corresponding amount of Li + ions and to react the Li + ions with Al 2 O 3 and SiO 2 in the surface layer to form crystallites of beta-quartz solid solution nucleated by the TiO 2 and/or ZrO 2 .
Inventors
- 👤 Joseph E. Pierson
- 👤 Stanley D. Stookey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 23:34
CPC Classifications
C; C03; C03C; C03C3/00; C03C3/04; C03C3/076; C03C3/083; C03C21/00; C03C21/001; C03C21/002; C03C10/00; C03C10/0018; C03C10/0027; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
192 words
A unitary glass article which is transparent, translucent, or opaque exhibiting exceptionally high flexural and impact strengths composed of an interior glass portion and an integral surface compression layer having a depth of at least 0.001", said surface layer containing crystallites of beta-quartz solid solution which have a coefficient of thermal expansion substantially lower than that of said interior glass portion, said interior portion consisting essentially, expressed in terms of mole percent on the oxide basis, of about 14-24% R 2 O, wherein R 2 O consists of the sum of 0-5% Li 2 O+0-5% K 2 O+the remainder Na 2 O, 17-21% Al 2 O 3 , 45-60% SiO 2 , 3-6% total of at least one oxide selected from the group consisting of TiO 2 and ZrO 2 , and 0-2% P 2 O 5 , the sum of R 2 O+Al 2 O 3 +SiO 2 +TiO 2 +ZrO 2 +P 2 O 5 constituting at least 85% of the total composition, and said surface layer containing Li + ions in greater amount than in said interior portion with a corresponding decrease in Na + and K + ions.
Claim 2
Dependent Claim
192 words
A unitary glass article which is transparent, translucent, or opaque exhibiting exceptionally high flexural and impact strengths composed of an interior glass portion and an integral surface compression layer having a depth of at least 0.001", said surface layer containing crystallites of beta-quartz solid solution which have a coefficient of thermal expansion substantially lower than that of said interior glass portion, said interior portion consisting essentially, expressed in terms of mole percent on the oxide basis, of about 14-24% R 2 O, wherein R 2 O consists of the sum of 0-5% Li 2 O+0-5% K 2 O+the remainder Na 2 O, 17-21% Al 2 O 3 , 45-60% SiO 2 , 3-6% total of at least one oxide selected from the group consisting of TiO 2 and ZrO 2 , and 0-2% P 2 O 5 , the sum of R 2 O+Al 2 O 3 +SiO 2 +TiO 2 +ZrO 2 +P 2 O 5 constituting at least 85% of the total composition, and said surface layer containing Li + ions in greater amount than in said interior portion with a corresponding decrease in Na + and K + ions.
Claim 3
Dependent Claim
32 words
A glass article according to claim 1 exhibiting transparency wherein the mole ratio Al 2 O 3 +P 2 O 5 :R 2 O is greater than 0.8 but less than 1.2.
Claim 4
Dependent Claim
33 words
Transparent, thin walled, lightweight glass articles having the structure of and the composition of a glass according to claim 2 selected from the group of containers, drinkware, and faceplates for motor vehicle headlights.
Claim 5
Dependent Claim
58 words
A glass article according to claim 1 also containing up to 15% total of at least one component in the indicated proportion selected from the group consisting of up to about 5% ZnO, up to about 10% CaO, up to about 10% MgO, up to about 2% F, and up to about 2% B 2 O 3 .
Claim 6
Dependent Claim
88 words
A glass article according to claim 1 consisting essentially of about 14-16% R 2 O, wherein R 2 O consists of Li 2 O, K 2 O, and Na 2 O in the indicated proportions of 0-3% Li 2 O, 0-3% K 2 O, and the remainder Na 2 O, 5-10% MgO, 17-20% Al 2 O 3 , 50-60% SiO 2 , 3-6% total of at least one oxide selected from the group consisting of TiO 2 and ZrO 2 , and 0-2% P 2 O 5 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-02-22 | 1991-08-24 | 1992-02-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-02-22 | 1995-08-24 | 1996-02-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-02-22 | 1999-08-24 | 2000-02-23 | $7700.00 | Window Closed / Lapsed |