Alveolar bone grafting process with controlled surface active ceramics
Assignee: Individual
•
Filing: 1985-08-15
•
Granted: 1988-02-16
•
Expires: 2005-08-15
Abstract
Abstract Materials and dental procedures are disclosed for the treatment of resorbed or diseased periodontal and alveolar bone tissues. Biocompatible nonresorbable ceramic mixtures and compounds containing silicon, calcium, phosphorous, and sodium oxides and flurides are prepared as powders or spheres and applied to defects or areas where it is desired to recontour the bone structure. This technique permits an improved method for corrective peridontal procedures and for alveolar ridge augmentation.
Inventors
- 👤 Edwin C. Ethridge
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 06:46
CPC Classifications
A; A61; A61C; A61C17/00
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
225 words
A method of treatment of general bone resorption and bone damage adjacent to teeth, which is caused by periodontal disease comprising: making a sulcular incision around one of said diseased teeth to free any soft tissue attachment; making modified vertical buccal and lingual incisions to some distance from the implant site: raising full thickness mucoperiosteal flaps with internally beveled incisions reflected to expose the defect; removing epithelialized granulation tissue; thinning bulky gingiva while preserving the vertical dimension of the flap and papilla such that adequate closure is possible; preparing the root surface and the bony defect to receive the implant; planning of the root in order to accomplish complete debridement of granulomatous tissue and cementum containing exdotoxins from the exposed cementum; scaling and planning the exposed root using sharp curettes until the root is hard, smooth and clean; curretting the bony socket site to remove all granulomatous and collagenous tissue over the osseous defect, thus exposing the root surface and osseous walls and removing all transseptal collagen fibers; performing decortication of the bone lining of the defect with intramarrow penetration, thus removing the dense cortical bone barrier; inserting controlled surface active ceramic implant granules into the implant site; lightly packing said granules into the defect, to restore a natural physiologic contour without overfilling; closing the wound at the implant site; and applying a periodontal dressing.
Claim 2
Independent Claim
225 words
A method of treatment of general bone resorption and bone damage adjacent to teeth, which is caused by periodontal disease comprising: making a sulcular incision around one of said diseased teeth to free any soft tissue attachment; making modified vertical buccal and lingual incisions to some distance from the implant site: raising full thickness mucoperiosteal flaps with internally beveled incisions reflected to expose the defect; removing epithelialized granulation tissue; thinning bulky gingiva while preserving the vertical dimension of the flap and papilla such that adequate closure is possible; preparing the root surface and the bony defect to receive the implant; planning of the root in order to accomplish complete debridement of granulomatous tissue and cementum containing exdotoxins from the exposed cementum; scaling and planning the exposed root using sharp curettes until the root is hard, smooth and clean; curretting the bony socket site to remove all granulomatous and collagenous tissue over the osseous defect, thus exposing the root surface and osseous walls and removing all transseptal collagen fibers; performing decortication of the bone lining of the defect with intramarrow penetration, thus removing the dense cortical bone barrier; inserting controlled surface active ceramic implant granules into the implant site; lightly packing said granules into the defect, to restore a natural physiologic contour without overfilling; closing the wound at the implant site; and applying a periodontal dressing.
Claim 3
Dependent Claim
31 words
The method of treatment of general bone resorption and bone damage adjacent to teeth of claim 1 comprising the preliminary steps of doing scaling, root planning and occulusal equilibration when necessary.
Claim 4
Dependent Claim
43 words
The method of treatment of general bone resorption and bone damage adjacent to teeth of claim 1 comprising the step of inducing bleeding to cover the implant site with a clot, after the insertion of the ceramic implant granules into the implant site.
Claim 5
Independent Claim
104 words
A method of regenerative therapy for treating and repairing bone defects comprising: preparing a discontinuous mass containing a physiologically compatible and insoluable surface active ceramic; and positioning said discontinuous mass adjacent to surgically prepared calcified tissues; wherein said surface active ceramic consists of particles having weight proportions in the compositional ranges as follows: silicon dioxide (SiO 2 ), 10 to 60 percent; calcium oxide (CaO) and phosphorus pentoxide (P 2 O 5 ), in the ratio of 4:1 to 8:1 comprising 50 to 95 percent; sodium oxide (Na 2 0), 0 to 25 percent; and potassium oxide (K 2 O), 0 to 10 percent.
Claim 6
Independent Claim
104 words
A method of regenerative therapy for treating and repairing bone defects comprising: preparing a discontinuous mass containing a physiologically compatible and insoluable surface active ceramic; and positioning said discontinuous mass adjacent to surgically prepared calcified tissues; wherein said surface active ceramic consists of particles having weight proportions in the compositional ranges as follows: silicon dioxide (SiO 2 ), 10 to 60 percent; calcium oxide (CaO) and phosphorus pentoxide (P 2 O 5 ), in the ratio of 4:1 to 8:1 comprising 50 to 95 percent; sodium oxide (Na 2 0), 0 to 25 percent; and potassium oxide (K 2 O), 0 to 10 percent.
Claim 7
Dependent Claim
39 words
A method according to claim 4 for treating and repairing bone defects wherein said discontinuous mass consists of surface active ceramic grains mixed with one or more of demineralized bone, bone morphogenic protein, resorbable calcium phosphate mineral, or collagen.
Claim 8
Dependent Claim
22 words
A method according to claim 5 for treating and repairing bone defects comprising mixing a sterile aqueous solution with said ceramic grains.
Claim 9
Dependent Claim
23 words
A method according to claim 4 for treating and repairing bone defects comprising delivering said discontinuous mass to the tissues using a syringe.
Claim 10
Dependent Claim
33 words
A method according to claim 4 for treating and repairing bone defects wherein 5 to 15 percent of said calcium oxide is replaced by an equal portion of calcium fluoride (CaF 2 ).
Claim 11
Dependent Claim
64 words
A method according to claim 4 for treating and repairing bone defects wherein the method for forming said particles comprises: casting said molten mixture; grinding the resulting casting of said mixture into a mixture having granular form; and passing said granular mixture through a sieve device sized and configured to achieve individual grains of the mixture having the range from 0.1 to 1 mm.
Claim 12
Dependent Claim
25 words
A method according to claim 4 for treating and repairing bone defects wherein said particles are larger than will pass through U.S. mesh size 60.
Claim 13
Dependent Claim
38 words
The method according to claim 10 for treating and repairing bone defects comprising the additional step of polishing said grains with abrasive polishing grains, in order to remove irregular edges from the individual grains of surface active ceramic.
Claim 14
Dependent Claim
35 words
The method according to claim 10 for treating and repairing bone defects comprising the additional step of heat treating said grains, in order to remove irregular edges from the individual grains of surface active ceramic.
Claim 15
Dependent Claim
53 words
A method according to claim 4 for treating and repairing bone defects wherein the method for casting and forming said particles comprises: extruding molten droplets of said mixture from an orifice in said crucible, whereby said droplets solidify as they fall through the air; and collecting the solid droplets in a sample holder.
Claim 16
Dependent Claim
39 words
The method according to claim 13 for treating and repairing bone defects wherein said extruding is accomplished by allowing the force of gravity to act on the molten ceramic material and cause separation of the droplets from the orifice.
Claim 17
Dependent Claim
45 words
The method according to claim 14 for treating and repairing bone defects wherein said extruding is accomplished by the use of a pneumatic ejection system to rapidly extrude a molten stream from the orifice to break down into droplets by the action of surface tension.
Claim 18
Dependent Claim
64 words
A method according to claim 4 for treating and repairing bone defects wherein said method more particularly comprises repairing defects in alveolar bone and said process is the filling of sockets in alveolar bone caused by the extraction of teeth comprising: insertion of the said discontinuous mass containing physiologically compatible and insoluble surface active ceramic into the fresh socket; and surgically closing said tissues.
Claim 19
Independent Claim
78 words
A method of regenerative therapy for treating and repairing bone defects comprising: preparing a discontinuous mass containing a physiologically compatible and insoluable surface active ceramic; and positioning said discontinuous mass adjacent to surgically prepared calcified tissues; wherein said surface active ceramic consists of particles having weight percentages as follows: silicon dioxide (SiO 2 ), 45 percent; calcium oxide (CaO), 24.5 percent; sodium oxide (Na 2 O), 24.5 percent; and phosphorus pentoxide (P 2 O 5 ), 6 percent.
Claim 20
Independent Claim
78 words
A method of regenerative therapy for treating and repairing bone defects comprising: preparing a discontinuous mass containing a physiologically compatible and insoluable surface active ceramic; and positioning said discontinuous mass adjacent to surgically prepared calcified tissues; wherein said surface active ceramic consists of particles having weight percentages as follows: silicon dioxide (SiO 2 ), 45 percent; calcium oxide (CaO), 24.5 percent; sodium oxide (Na 2 O), 24.5 percent; and phosphorus pentoxide (P 2 O 5 ), 6 percent.
Claim 21
Dependent Claim
32 words
A method according to claim 17 for treating and repairing bone defects wherein 5 to 15 percent of calcium oxide is replaced by an equal portion of calcium fluoride (CaF 2 ).
Claim 22
Dependent Claim
31 words
A method according to claim 4 for treating and repairing bone defects wherein said defects are defects in alveolar bone; whereby said treatment of alveolar bone defects comprises alveolar ridge augmentation.
Claim 23
Dependent Claim
85 words
A method according to claim 19 for treating and repairing bone defects wherein said defects in alveolar bone are repaired by the insertion of the said discontinuous mass containing physiologically compatible and insoluble surface active ceramic into the bone defect comprising: making an incision in the soft tissue above the alveolar bone that is to be augmented; inserting an instrument under the tissues; separating said tissues from said alveolar bone; inserting said mass into the available space in the tissues; and surgically closing said tissues.
Claim 24
Dependent Claim
32 words
A method according to claim 20 for treating and repairing bone defects comprising the step of performing decortication of the bone after the step of separating said tissues from said alveolar bone.
Claim 25
Dependent Claim
26 words
A method according to claim 19 for treating and repairing bone defects wherein said available space in the tissues is also adjacent to a dental implant.
Claim 26
Dependent Claim
25 words
A method according to claim 17 for treating and repairing bone defects wherein said particles are larger than will pass through U.S. mesh size 60.
Claim 27
Dependent Claim
31 words
A method according to claim 17 for treating and repairing bone defects wherein said defects are defects in alveolar bone; whereby said treatment of alveolar bone defects comprises alveolar ridge augmentation.
Claim 28
Dependent Claim
85 words
A method according to claim 24 for treating and repairing bone defects wherein said defects in alveolar bone are repaired by the insertion of the said discontinuous mass containing physiologically compatible and insoluble surface active ceramic into the bone defect comprising: making an incision in the soft tissue above the alveolar bone that is to be augmented; inserting an instrument under the tissues; separating said tissues from said alveolar bone; inserting said mass into the available space in the tissues; and surgically closing said tissues.
Claim 29
Dependent Claim
22 words
A method according to claim 24 for treating and repairing bone defects wherein said defects are also adjacent to a dental implant.
Claim 30
Dependent Claim
64 words
A method according to claim 17 for treating and repairing bone defects wherein said method more particularly comprises repairing defects in alveolar bone and said process is the filling of sockets in alveolar bone caused by the extraction of teeth comprising: insertion of the said discontinuous mass containing physiologically compatible and insoluble surface active ceramic into the fresh socket; and surgically closing said tissues.
Claim 31
Independent Claim
258 words
A method of regenerative therapy for treating and repairing bone defects comprising: preparing a discontinuous mass containing a physiologically compatible and insoluable surface active ceramic; and positioning said discontinuous mass adjacent to surgically prepared calcified tissues; wherein said defects are defects in alveolar bone and said method more particularly comprises repairing periodontal pockets adjacent diseased teeth comprising: making a sulcular incision around one of said diseased teeth to free any soft tissue attachment; making modified vertical buccal and lingual incisions to some distance from the implant site; raising full thickness mucoperiosteal flaps with internally beveled incisions reflected to expose the defect; removing epithelialized granulation tissue; thinning bulky gingiva while preserving the vertical dimension of the flap and papilla such that adequate closure is possible; preparing the root surface and the bony defect to receive the implant; planning of the root in order to accomplish complete debridement of granulomatous tissue and cementum containing exdotoxins from the exposed cementum; scaling and planning the exposed root using sharp curettes until the root is hard, smooth and clean; curretting the bony socket site to remove all granulomatous and collagenous tissue over the osseous defect, thus exposing the root surface and osseous walls and removing all transseptal collagen fibers; performing decortication of the bone lining of the defect with intramarrow penetration, thus removing the dense cortical bone barrier; inserting said discontinuous mass containing said surface active ceramic into the implant site; lightly packing said discontinuous mass into the defect, to restore a natural physiologic contour; and closing the wound at the implant site.
Claim 32
Independent Claim
258 words
A method of regenerative therapy for treating and repairing bone defects comprising: preparing a discontinuous mass containing a physiologically compatible and insoluable surface active ceramic; and positioning said discontinuous mass adjacent to surgically prepared calcified tissues; wherein said defects are defects in alveolar bone and said method more particularly comprises repairing periodontal pockets adjacent diseased teeth comprising: making a sulcular incision around one of said diseased teeth to free any soft tissue attachment; making modified vertical buccal and lingual incisions to some distance from the implant site; raising full thickness mucoperiosteal flaps with internally beveled incisions reflected to expose the defect; removing epithelialized granulation tissue; thinning bulky gingiva while preserving the vertical dimension of the flap and papilla such that adequate closure is possible; preparing the root surface and the bony defect to receive the implant; planning of the root in order to accomplish complete debridement of granulomatous tissue and cementum containing exdotoxins from the exposed cementum; scaling and planning the exposed root using sharp curettes until the root is hard, smooth and clean; curretting the bony socket site to remove all granulomatous and collagenous tissue over the osseous defect, thus exposing the root surface and osseous walls and removing all transseptal collagen fibers; performing decortication of the bone lining of the defect with intramarrow penetration, thus removing the dense cortical bone barrier; inserting said discontinuous mass containing said surface active ceramic into the implant site; lightly packing said discontinuous mass into the defect, to restore a natural physiologic contour; and closing the wound at the implant site.
Claim 33
Dependent Claim
26 words
The method according to claim 28 of treating and repairing bone defects comprising the preliminary steps of doing scaling, root planning and occulusal equilibration when necessary.
Claim 34
Dependent Claim
38 words
The method according to claim 24 of treating and repairing bone defects comprising the step of inducing bleeding to cover the implant site with a clot, after the insertion of the said discontinuous mass into the implant site.
References Cited (Backward Citations)
US4024639A
Cited
US4308064A
Cited
US4599085A
Cited
US4356572A
Cited
US4548959A
Cited
US4497075A
Cited
US4472840A
Cited
US4629464A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-02-15 | 1991-08-17 | 1992-02-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-02-15 | 1995-08-17 | 1996-02-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-02-15 | 1999-08-17 | 2000-02-16 | $7700.00 | Window Closed / Lapsed |