Zirconia porcelain
Assignee: NGK Insulators Ltd
•
Filing: 1986-11-28
•
Granted: 1988-02-02
•
Expires: 2006-11-28
Abstract
Abstract Disclosed herein is a high durability zirconia porcelain which is high in thermal stability and free from degradation phenomena such as profile change and strength reduction, and is characterized in that change in length after the zirconia porcelain being maintained in hot water at 250 DEG C. for 50 hours is not more than 0.05%.
Inventors
- 👤 Takao Soma
- 👤 Minoru Matsui
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 11:43
CPC Classifications
H; H01; H01M; H01M8/00; H01M8/10; H01M8/12; H01M8/124; H01M8/1246; H01M8/1253; C; C04; C04B; C04B35/00; C04B35/01; C04B35/48; C04B35/486; F; F02; F02F; F02F7/00; F02F7/0085; F02F7/0087; F05; F05C; F05C2203/00; F05C2203/08; F05C2203/0865; F05C2203/0895; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
149 words
A zirconia porcelain consisting essentially of: zirconia, wherein at least 5% by volume of the zirconia is tetragonal zirconia, and wherein the average particle size of the tetragonal zirconia is 2 μm or less; and 2 to 10% by weight of yttria is added to the zirconia as a stabilizer thereof, said yttria being dispersed in the zirconia such that tetragonal zirconia grains which contain not more than 2% by weight of the yttria are not more than 10% by volume of all the tetragonal zirconia grains, the zirconia porcelain having a closed porosity of 7% or less, such that when the zirconia porcelain is exposed to water at a temperature of approximately 250° C. for a period of time of about 50 hours, the change in length of the zirconia porcelain is not more than 0.05%, said zirconia porcelain having a strength of not less than 500 MPa.
Claim 2
Dependent Claim
149 words
A zirconia porcelain consisting essentially of: zirconia, wherein at least 5% by volume of the zirconia is tetragonal zirconia, and wherein the average particle size of the tetragonal zirconia is 2 μm or less; and 2 to 10% by weight of yttria is added to the zirconia as a stabilizer thereof, said yttria being dispersed in the zirconia such that tetragonal zirconia grains which contain not more than 2% by weight of the yttria are not more than 10% by volume of all the tetragonal zirconia grains, the zirconia porcelain having a closed porosity of 7% or less, such that when the zirconia porcelain is exposed to water at a temperature of approximately 250° C. for a period of time of about 50 hours, the change in length of the zirconia porcelain is not more than 0.05%, said zirconia porcelain having a strength of not less than 500 MPa.
Claim 3
Dependent Claim
18 words
A zirconia porcelain according to claim 1, which contains not less than 50% by volume of tetragonal zirconia.
Claim 4
Dependent Claim
25 words
A zirconia porcelain according to claim 1, further comprising 1.3% by weight of SiO 2 and 0.7% by weight of Al 2 O 3 .
Claim 5
Dependent Claim
15 words
A zirconia porcelain according to claim 1, wherein said closed porosity is 3% or less.
Claim 6
Dependent Claim
21 words
A zirconia porcelain according to claim 1, wherein said average particle size of the tetragonal zirconia is less than 0.3 μm.
Claim 7
Dependent Claim
158 words
A zirconia porcelain comprising: at least 89.4% by weight of zirconia, said zirconia containing crystal grains of tetragonal zirconia in an amount not less than 45% by volume, wherein the tetragonal zirconia grains have an average particle size of 2 μm or less; and 2 to 10% by weight of yttria is added to the zirconia as a stabilizer thereof, said yttria being dispersed in the zirconia such that tetragonal zirconia grains which contain not more than 2% by weight of the yttria are not more than 10% by volume of all the tetragonal zirconia grains, the zirconia porcelain having a closed porosity of 7% or less, such that when the zirconia porcelain is exposed to water at a temperature of approximately 250° C. for a period of time of about 50 hours, the change in length of the zirconia porcelain is not more than 0.05%, said zirconia porcelain having a strength of not less than 500 MPa.
Claim 8
Dependent Claim
158 words
A zirconia porcelain comprising: at least 89.4% by weight of zirconia, said zirconia containing crystal grains of tetragonal zirconia in an amount not less than 45% by volume, wherein the tetragonal zirconia grains have an average particle size of 2 μm or less; and 2 to 10% by weight of yttria is added to the zirconia as a stabilizer thereof, said yttria being dispersed in the zirconia such that tetragonal zirconia grains which contain not more than 2% by weight of the yttria are not more than 10% by volume of all the tetragonal zirconia grains, the zirconia porcelain having a closed porosity of 7% or less, such that when the zirconia porcelain is exposed to water at a temperature of approximately 250° C. for a period of time of about 50 hours, the change in length of the zirconia porcelain is not more than 0.05%, said zirconia porcelain having a strength of not less than 500 MPa.
Claim 9
Dependent Claim
19 words
A zirconia porcelain according to claim 6, wherein said volume % of tetragonal zirconia is not less than 80%.
Claim 10
Dependent Claim
25 words
A zirconia porcelain according to claim 6, further comprising 1.3% by weight of SiO 2 and 0.7% by weight of Al 2 O 3 .
Claim 11
Dependent Claim
15 words
A zirconia porcelain according to claim 6, wherein said closed porosity is 39% or less.
Claim 12
Dependent Claim
21 words
A zirconia porcelain according to claim 6, wherein said average particle size of the tetragonal zirconia is less than 0.3 μm.
Claim 13
Dependent Claim
178 words
A zirconia porcelain consisting essentially of: at least 89.4% by weight of zirconia, said zirconia containing crystal grains of tetragonal zirconia in an amount not less than 60% by volume, wherein the crystal grains of tetragonal zirconia have an average particle size of 2 μm or less; 1.3% by weight of SiO 2 ; 0.7% by weight of Al 2 O 3 ; and 2 to 10% by weight of yttria is added to the zirconia as a stabilizer thereof, said yttria being dispersed in the zirconia such that tetragonal zirconia grains which contain not more than 2% by weight of the yttria are not more than 10% by volume of all the tetragonal zirconia grains, the zirconia porcelain having a closed porosity of 3% or less, such that when the zirconia porcelain is exposed to water at a temperature of approximately 250° C. for a period of time of about 50 hours, the change in length of the zirconia porcelain is not more than 0.05%, said zirconia porcelain having a strength of not less than 500 MPa.
Claim 14
Dependent Claim
178 words
A zirconia porcelain consisting essentially of: at least 89.4% by weight of zirconia, said zirconia containing crystal grains of tetragonal zirconia in an amount not less than 60% by volume, wherein the crystal grains of tetragonal zirconia have an average particle size of 2 μm or less; 1.3% by weight of SiO 2 ; 0.7% by weight of Al 2 O 3 ; and 2 to 10% by weight of yttria is added to the zirconia as a stabilizer thereof, said yttria being dispersed in the zirconia such that tetragonal zirconia grains which contain not more than 2% by weight of the yttria are not more than 10% by volume of all the tetragonal zirconia grains, the zirconia porcelain having a closed porosity of 3% or less, such that when the zirconia porcelain is exposed to water at a temperature of approximately 250° C. for a period of time of about 50 hours, the change in length of the zirconia porcelain is not more than 0.05%, said zirconia porcelain having a strength of not less than 500 MPa.
Claim 15
Dependent Claim
19 words
A zirconia porcelain according to claim 11, wherein said volume % of tetragonal zirconia is not less than 80%.
Claim 16
Dependent Claim
21 words
A zirconia porcelain according to claim 12, wherein said average particle size of the tetragonal zirconia is less than 0.3 μm.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-02-01 | 1991-08-03 | 1992-02-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-02-01 | 1995-08-03 | 1996-02-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-02-01 | 1999-08-03 | 2000-02-02 | $7700.00 | Window Closed / Lapsed |