Immobilization of biological cells in polytetrafluoroethylene matrix

Claim 3

The method according to claim 1 wherein said viable cells range in size from 0.1 to 25 micrometers.

Claim 4

The method according to claim 1 wherein said viable cells range in size from 0.3 to 15 micrometers.

Claim 5

The method according to claim 1 wherein said calendering rolls are maintained at a temperature in the range of 30° to 40° C.

Claim 6

The method according to claim 1 wherein said mixing in (c) takes place at a temperature in the range of 20° to 40° C.

Claim 7

The method according to claim 1 wherein said viable cells are Achrombacter guttatus, Azotobacter aqilis, Candida tropicalis, Clostridium butyricum, Eschericia coli, Micrococcus denitrificans, Pseudomonas mephitica var. lipolytica, Saccharomyces cerevisiae, Streptococcus faecalis, Tetrahymena pyriformis, Aspergillus niger, Bacillus thuringiensis or mammalian cells.

Claim 8

The method according to claim 1 wherein said composite structure further consists essentially of a cell nutrient which is added in step (a).

Claim 9

The method according to claim 1 wherein said composite structure further consists essentially of at least one processing aid selected from the group consisting of calcium carbonate, starch, polyethylene, zeolite, chiten, Sephadex, cellulosics, vermiculite and clay which is added in step (a).

Claim 10

The method according to claim 1 further comprising the step of drying the resultant composite structure from step (d).

Claim 11

A composite structure consisting essentially of a polytetrafluoroethylene fibril matrix having entrapped therein 0.005 to 15 parts of viable cells per part of polytetrafluoroethylene by weight, said viable cells being capable of their usual and continuous biochemical and biological performances, said composite having been prepared by a process comprising the steps of: (a) providing a blend consisting essentially of viable cells and surfactant-and soap-free polytetrafluoroethylene as an aqueous dispersion in the form of a damp paste. (b) adding sufficient water as a lubricant to exceed the absorptive capacity of the viable cells yet maintain a stiff dough consistency, (c) intensively mixing said stiff dough at a temperature in the range of 5° to 70° C. to fibrillate said polytetrafluoroethylene, and (d) biaxially calendering the resultant mass between calendering rolls at a temperature in the range of 5° to 70° C. and a pressure in the range of 1000 to 3000 MPa to cause further fibrillation of said polytetrafluoroethylene to provide said composite structure, said heating being controlled to preserve the viability of the cells.

Claim 12

A composite structure consisting essentially of a polytetrafluoroethylene fibril matrix having entrapped therein 0.005 to 15 parts of viable cells per part of polytetrafluoroethylene by weight, said viable cells being capable of their usual and continuous biochemical and biological performances, said composite having been prepared by a process comprising the steps of: (a) providing a blend consisting essentially of viable cells and surfactant-and soap-free polytetrafluoroethylene as an aqueous dispersion in the form of a damp paste. (b) adding sufficient water as a lubricant to exceed the absorptive capacity of the viable cells yet maintain a stiff dough consistency, (c) intensively mixing said stiff dough at a temperature in the range of 5° to 70° C. to fibrillate said polytetrafluoroethylene, and (d) biaxially calendering the resultant mass between calendering rolls at a temperature in the range of 5° to 70° C. and a pressure in the range of 1000 to 3000 MPa to cause further fibrillation of said polytetrafluoroethylene to provide said composite structure, said heating being controlled to preserve the viability of the cells.

Claim 13

The composite structure according to claim 10 further consisting essentially of a cell nutrient which has been added in step (a).

Claim 14

The composite structure according to claim 10 further consisting essentially of at least one processing aid selected from the group consisting of calcium carbonate, starch, polyethylene, zeolite, chiten, Sephadex, cellulosics, vermiculite and clay which has been added in step (a).

Claim 15

The composite structure according to claim 10 further comprising the step of drying the resultant composite structure from step (d).