Method for diffusing aluminum
Assignee: BBC Brown Boveri AG Switzerland
•
Filing: 1986-04-11
•
Granted: 1988-01-19
•
Expires: 2006-04-11
Abstract
Abstract For the p-type doping of silicon, particularly for power semiconductor components, aluminum from an Al target is precipitated by cathode sputtering in an argon plasma on a major face (2) of a silicon wafer (1) by which means a comparatively high purity of the deposited aluminum is achieved. Before the aluminum deposition, the silicon water (1) is bombarded with argon ions for 10 min at an argon pressure of 20 μbar which guarantees a uniform fusion of the aluminum with the silicon during later heating and, in particular, prevents the formation of droplets of the aluminum on the major face (2). The Al layer formed in this manner is photo-lithographically preferably structured in such a manner that several aluminum sources spaced apart from each other are allocated to one aluminum-doped zone (10). The subsequent diffusion occurs for 300 min at 1250° C. in a gas mixture of nitrogen or argon (1 l/min) and oxygen (20 ml/min). During this process, the aluminum-doped zone (10) is produced. Subsequently, photoresist (13,14) is applied to the non-diffused regions. Residues (11') of the aluminum sources are then laterally etched by a silicon etchant and, as a result, removed. Following this, the photoresist (13,14) is removed.
Inventors
- 👤 Helmut Keser
- 👤 Jan Voboril
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 15:01
CPC Classifications
H; H10; H10P; H10P32/00; H10P32/10; H10P32/17; H10P32/171; H10P32/14; H10P32/1408; Y; Y10; Y10S; Y10S438/00; Y10S438/914; Y10S438/92; Y10S438/974
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
135 words
A method for producing a semiconductor device with at least one deep, laterally limited p + -type doped zone comprising the following steps: (a) bombarding a major face of a silicon wafer with rare gas ions, thereby enhancing the adhesion of a subsequently deposited aluminum layer on said major face, (b) depositing an aluminum layer on said major face by cathode sputtering in a non-corroding gas plasma, (c) structuring said aluminum layer according to a predeterminable pattern for the purpose of generating at least one deep, laterally limited p + -type doped zone, and (d) heating silicon wafer coated with said aluminum layer in an oxygen containing atmosphere to a diffusion temperature for a time sufficient to diffuse aluminum from the aluminum layer into the silicon wafer to produce said p + -type doped zone.
Claim 2
Independent Claim
135 words
A method for producing a semiconductor device with at least one deep, laterally limited p + -type doped zone comprising the following steps: (a) bombarding a major face of a silicon wafer with rare gas ions, thereby enhancing the adhesion of a subsequently deposited aluminum layer on said major face, (b) depositing an aluminum layer on said major face by cathode sputtering in a non-corroding gas plasma, (c) structuring said aluminum layer according to a predeterminable pattern for the purpose of generating at least one deep, laterally limited p + -type doped zone, and (d) heating silicon wafer coated with said aluminum layer in an oxygen containing atmosphere to a diffusion temperature for a time sufficient to diffuse aluminum from the aluminum layer into the silicon wafer to produce said p + -type doped zone.
Claim 3
Dependent Claim
25 words
The method according to claim 1 wherein the structuring of the aluminum layer divides the aluminum layer up into a plurality of separate aluminum sources.
Claim 4
Dependent Claim
46 words
The method according to claim 2, further comprising (e) removing a residue of the aluminum sources by isotropically etching said major face inbetween the residues of the aluminum sources by a silicon etchant, so as to remove the support of the residues of the aluminum sources.
Claim 5
Dependent Claim
24 words
The method according to claim 3, wherein said rare gas ions are argon ions and wherein said non-corroding gas plasma is an argon plasma.
Claim 6
Dependent Claim
29 words
The method according to claim 4, further comprising tempering said silicon wafer coated with aluminum sources at a temperature between 480° C. and 500° C. before said heating step.
Claim 7
Dependent Claim
51 words
The method according to claim 5, wherein said heating step comprises (a) raising the temperature at a rate of about 3° K./min to a diffusion temperature of 1250° C., (b) keeping the temperature at 1250° C. for about 300 min, and (c) lowering the temperature at a rate of 1° K./min.
Claim 8
Dependent Claim
33 words
The method according to claim 6 further comprising the additional step of covering the whole silicon wafer except for the p + -type doped zones with a photoresist coating before said removing step.
Claim 9
Dependent Claim
43 words
The method according to claim 7, wherein the silicon etchant to remove the residue of the aluminum sources consists of 23% by volume HF 47% by volume HNO 3 20% by volume CH 3 COOH 10% by volume H 3 PO 4 .
Claim 10
Independent Claim
149 words
A method for producing a semiconductor device with at least one deep, laterally limited p + -type doped zone comprising the following steps: (a) bombarding a major face of a silicon wafer with rare gas ions, thereby enhancing the adhesion of a subsequently deposited aluminum layer on said major face, (b) depositing an aluminum layer on said major face by cathode sputtering in a non-corroding gas plasma, (c) structuring said aluminum layer for the purpose of generating at least one deep, laterally limited, p + -type doped zone according to a predeterminable pattern whereby said aluminum layer is divided up into a plurality of separate sources, and (d) heating the silicon wafer coated with said aluminum sources in an oxygen containing atmosphere to a diffusion temperature for a time sufficient to diffuse aluminum from the aluminum sources into the silicon wafer to produce said p + -type doped zone.
Claim 11
Independent Claim
149 words
A method for producing a semiconductor device with at least one deep, laterally limited p + -type doped zone comprising the following steps: (a) bombarding a major face of a silicon wafer with rare gas ions, thereby enhancing the adhesion of a subsequently deposited aluminum layer on said major face, (b) depositing an aluminum layer on said major face by cathode sputtering in a non-corroding gas plasma, (c) structuring said aluminum layer for the purpose of generating at least one deep, laterally limited, p + -type doped zone according to a predeterminable pattern whereby said aluminum layer is divided up into a plurality of separate sources, and (d) heating the silicon wafer coated with said aluminum sources in an oxygen containing atmosphere to a diffusion temperature for a time sufficient to diffuse aluminum from the aluminum sources into the silicon wafer to produce said p + -type doped zone.
Claim 12
Dependent Claim
50 words
The method according to claim 9, further comprising (e) removing a residue of the aluminum sources by etching the major face of the diffused silicon wafer inbetween the residues of the aluminum sources by a silicon etchant, so as to remove the support of the residues of the aluminum sources.
Claim 13
Dependent Claim
24 words
The method according to claim 10, wherein said rare gas ions are argon ions and wherein said non-corroding gas plasma is an argon plasma.
Claim 14
Dependent Claim
32 words
The method according to claim 11, further comprising tempering said silicon wafer coated with aluminum sources at a temperature between 480° C. and 500° C. before heating it to said diffusion temperature.
Claim 15
Dependent Claim
51 words
The method according to claim 12, wherein said heating step comprises (a) raising the temperature at a rate of about 3° K./min to a diffusion temperature of 1250° C., (b) keeping the temperature at 1250° C. for about 300 min, and (c) lowering the temperature at a rate of 1° K./min.
Claim 16
Dependent Claim
29 words
The method according to claim 3 further comprising covering the whole silicon wafer except for the p + -type doped zones with a photoresist coating before said removing step.
Claim 17
Independent Claim
196 words
A method for producing a semiconductor device with at least one deep, laterally limited p + -type doped zone comprising the following steps: (a) bombarding a major face of a silicon wafer with rare gas ions, thereby enhancing the adhesion of a subsequently deposited aluminum layer on said major face, (b) depositing an aluminum layer on said major face by cathode sputtering in a non-corroding gas plasma, (c) structuring said aluminum layer for the purpose of generating at least one deep, laterally limited, p + -type doped zone according to a predeterminable pattern, whereby said aluminum layer is divided up into a plurality of separate aluminum sources, (d) heating the silicon wafer coated with said aluminum sources in an oxygen containing atmosphere to a diffusion temperature for a time sufficient to diffuse aluminum from the aluminum sources into the silicon wafer to produce said p + -type doped zone, and (e) removing a residue of the aluminum sources by isotropically etching said major face after the diffusion treatment of the silicon wafer inbetween the residues of the aluminum sources by a silicon etchant, so as to remove the support of the residues of the aluminum sources.
Claim 18
Independent Claim
196 words
A method for producing a semiconductor device with at least one deep, laterally limited p + -type doped zone comprising the following steps: (a) bombarding a major face of a silicon wafer with rare gas ions, thereby enhancing the adhesion of a subsequently deposited aluminum layer on said major face, (b) depositing an aluminum layer on said major face by cathode sputtering in a non-corroding gas plasma, (c) structuring said aluminum layer for the purpose of generating at least one deep, laterally limited, p + -type doped zone according to a predeterminable pattern, whereby said aluminum layer is divided up into a plurality of separate aluminum sources, (d) heating the silicon wafer coated with said aluminum sources in an oxygen containing atmosphere to a diffusion temperature for a time sufficient to diffuse aluminum from the aluminum sources into the silicon wafer to produce said p + -type doped zone, and (e) removing a residue of the aluminum sources by isotropically etching said major face after the diffusion treatment of the silicon wafer inbetween the residues of the aluminum sources by a silicon etchant, so as to remove the support of the residues of the aluminum sources.
Claim 19
Dependent Claim
24 words
The method according to claim 15, wherein said rare gas ions are argon ions and wherein said non-corroding gas plasma is an argon plasma.
Claim 20
Dependent Claim
29 words
The method according to claim 16, further comprising tempering said silicon wafer coated with aluminum sources at a temperature between 480° C. and 500° C. before said heating step.
Claim 21
Dependent Claim
51 words
The method according to claim 17, wherein said heating step comprises (a) raising the temperature at a rate of about 3° K./min to a diffusion temperature of 1250° C., (b) keeping the temperature at 1250° C. for about 300 min, and (c) lowering the temperature at a rate of 1° K./min.
Claim 22
Dependent Claim
33 words
The method according to claim 18 further comprising the additional step of covering the whole silicon wafer except for the p + -type doped zones with a photoresist coating before said removing step.
References Cited (Backward Citations)
US2989385A
Cited
US3718502A
Cited
US4290830A
Cited
US4199386A
Cited
US4348254A
Cited
US4354307A
Cited
US4381957A
Cited
US4565588A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-01-18 | 1991-07-20 | 1992-01-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-01-18 | 1995-07-20 | 1996-01-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-01-18 | 1999-07-20 | 2000-01-19 | $7700.00 | Window Closed / Lapsed |