Vapor phase method for making metal halide glasses
Assignee: Corning Glass Works
•
Filing: 1983-10-21
•
Granted: 1988-01-12
•
Expires: 2003-10-21
Abstract
Abstract A vapor phase method for making a metal halide material useful for the manufacture of an infrared transmitting optical waveguide fiber or other optical device, and the use of the method for making such a device, wherein a halogenated beta-diketonate of a metal to be incorporated in the device is converted to the corresponding metal halide by controlled decomposition of the halogenated diketonate, are described.
Inventors
- 👤 Joseph M. Power
- 👤 Ahmad Sarhangi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:00
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/018; C03B37/01807; C03B37/01846; C03C; C03C13/00; C03C13/04; C03C13/041; C03C13/042; C03C3/00; C03C3/32; C03C3/325; C03B2201/00; C03B2201/80; C03B2201/82; Y; Y10; Y10S; Y10S65/00; Y10S65/15; Y10S65/16
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
104 words
A method for making a metal halide product which comprises the steps of: (a) introducing into a reaction zone a reactant vapor stream which comprises vapors of a halogenated metal beta-diketonate containing the metal and the halogen to be incorporated into the metal halide product; and (b) supplying energy to the reactant vapor stream at a rate sufficient to cause the decomposition of the metal beta-diketonate and the formation of a vapor deposition product therefrom which consists essentially of the metal halide of the metal and the halogen, the metal beta-diketonate being the principal source of both metal and halogen in the metal halide.
Claim 2
Independent Claim
104 words
A method for making a metal halide product which comprises the steps of: (a) introducing into a reaction zone a reactant vapor stream which comprises vapors of a halogenated metal beta-diketonate containing the metal and the halogen to be incorporated into the metal halide product; and (b) supplying energy to the reactant vapor stream at a rate sufficient to cause the decomposition of the metal beta-diketonate and the formation of a vapor deposition product therefrom which consists essentially of the metal halide of the metal and the halogen, the metal beta-diketonate being the principal source of both metal and halogen in the metal halide.
Claim 3
Dependent Claim
46 words
A method in accordance with claim 1 wherein the metal halide product includes at least one metal selected from the group consisting of Be, MG, Pb, Zn, Al, Zr, Hf, and Ce, and wherein the halogens are selected from the group consisting of Cl and F.
Claim 4
Dependent Claim
23 words
A method in accordance with claim 2 wherein the beta-diketonate is a fluorinated beta-diketonate and the metal halide product is a metal fluoride
Claim 5
Dependent Claim
20 words
A method in accordance with claim 3 wherein the energy is supplied by thermal heating of the reactant vapor stream.
Claim 6
Dependent Claim
22 words
A method in accordance with claim 3 wherein the energy is supplied to the reactant vapor stream by a low-pressure plasma discharge.
Claim 7
Dependent Claim
92 words
In a method for forming a metal halide optical fiber preform comprising the steps of providing a substrate, flowing reactive vapors into a reaction zone adjacent the substrate, and reacting the vapors to form a metal halide precursor material which is deposited onto the substrate, the improvement characterized in that the reactive vapors comprise a halogenated beta-diketonate containing the halogen and the metal to be incorporated as a metal halide in the precursor, and in that the halogenated beta-diketonate constitutes the principal source of both metal and halogen in the metal halide.
Claim 8
Dependent Claim
92 words
In a method for forming a metal halide optical fiber preform comprising the steps of providing a substrate, flowing reactive vapors into a reaction zone adjacent the substrate, and reacting the vapors to form a metal halide precursor material which is deposited onto the substrate, the improvement characterized in that the reactive vapors comprise a halogenated beta-diketonate containing the halogen and the metal to be incorporated as a metal halide in the precursor, and in that the halogenated beta-diketonate constitutes the principal source of both metal and halogen in the metal halide.
Claim 9
Dependent Claim
45 words
A method in accordance with claim 6 wherein the metal halide includes at least one metal selected from the group consisting of Be, Mg, Pb, Zn, Al, Zr, Hf and Ce, and wherein the halogens are selected from the group consisting of Cl and F.
Claim 10
Dependent Claim
22 words
A method in accordance with claim 7 wherein the beta-diketonate is a fluorinated beta-diketonate and the metal halide is a metal fluoride.
Claim 11
Dependent Claim
24 words
A method in accordance with claim 8 wherein the precursor consists of 85-100 mole percent BeF 2 and 0-15 mole percent AlF 3 .
Claim 12
Dependent Claim
19 words
A method in accordance with claim 6 wherein the halogenated beta-diketonate incorporates beta-diketone ligands which contain 5-12 carbon atoms.
Claim 13
Dependent Claim
15 words
A method in accordance with claim 10 wherein the beta-diketone ligand is derived from hexafluoroacetylacetone.
Claim 14
Dependent Claim
22 words
A method in accordance with claim 8 wherein decomposition of the fluorinated beta-diketonate is promoted by thermal heating of the reaction zone.
Claim 15
Dependent Claim
20 words
A method in accordance with claim 8 wherein decomposition of the fluorinated beta-diketonate is promoted by a low-pressure plasma discharge.
Claim 16
Dependent Claim
19 words
A method in accordance with claim 13 wherein the low-pressure plasma discharge is a microwave or radio frequency discharge.
Claim 17
Dependent Claim
99 words
In a method for forming a metal halide optical fiber preform comprising the steps of providing a hollow tubular substrate, flowing reactive vapors into a reaction zone within the tubular substrate, and reacting the vapors to form a metal halide precursor material which is deposited onto the inner surface of the substrate, the improvement characterized in that the reactive vapors comprise a halogenated beta-diketonate containing the halogen and the metal to be incorporated as a metal halide into the precursor, and in that the halogenated beta-diketonate constitutes the principal source of both metal and halogen in the metal halide.
Claim 18
Dependent Claim
99 words
In a method for forming a metal halide optical fiber preform comprising the steps of providing a hollow tubular substrate, flowing reactive vapors into a reaction zone within the tubular substrate, and reacting the vapors to form a metal halide precursor material which is deposited onto the inner surface of the substrate, the improvement characterized in that the reactive vapors comprise a halogenated beta-diketonate containing the halogen and the metal to be incorporated as a metal halide into the precursor, and in that the halogenated beta-diketonate constitutes the principal source of both metal and halogen in the metal halide.
Claim 19
Independent Claim
57 words
A method for making a product consisting essentially of a substantially oxygen-free vapor deposited metal halide which comprises the step of decomposing a vaporized fluorinated beta-diketonate of the metal to form the corresponding metal fluoride by intramolecular fluorine transfer, such that the fluorinated beta-diketonate constitutes the principal source of metal and halogen in the metal halide product.
Claim 20
Independent Claim
57 words
A method for making a product consisting essentially of a substantially oxygen-free vapor deposited metal halide which comprises the step of decomposing a vaporized fluorinated beta-diketonate of the metal to form the corresponding metal fluoride by intramolecular fluorine transfer, such that the fluorinated beta-diketonate constitutes the principal source of metal and halogen in the metal halide product.
Claim 21
Independent Claim
83 words
A method for making a substantially oxygen-free vapor deposited metal halide which comprises the step of decomposing a fluorinated beta-diketonate of the metal to form the corresponding metal fluoride by intramolecular fluorine transfer wherein the decomposition is promoted by thermal heating of the beta-diketonate at a temperature sufficient for metal fluoride formation but below the temperature at which significant carbonization of the beta-diketonate will occur, such that the fluorinated beta-diketonate constitutes the principal source of metal and halogen in the metal halide product.
Claim 22
Independent Claim
83 words
A method for making a substantially oxygen-free vapor deposited metal halide which comprises the step of decomposing a fluorinated beta-diketonate of the metal to form the corresponding metal fluoride by intramolecular fluorine transfer wherein the decomposition is promoted by thermal heating of the beta-diketonate at a temperature sufficient for metal fluoride formation but below the temperature at which significant carbonization of the beta-diketonate will occur, such that the fluorinated beta-diketonate constitutes the principal source of metal and halogen in the metal halide product.
Claim 23
Dependent Claim
17 words
A method in accordance with claim 16 wherein the decomposition is promoted by a low-pressure plasma discharge.
References Cited (Backward Citations)
US3356527A
Cited
US3826817A
Cited
US3933302A
Cited
DE2444100A1
Cited
US4076574A
Cited
US4065280A
Cited
US4189208A
Cited
US4349373A
Cited
US4308066A
Cited
US4343638A
Cited
US4262035A
Cited
US4292063A
Cited
JPS5751146A
Cited
US4378987A
Cited
US4501602A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-01-11 | 1991-07-13 | 1992-01-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-01-11 | 1995-07-13 | 1996-01-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-01-11 | 1999-07-13 | 2000-01-12 | $7700.00 | Window Closed / Lapsed |