Method of evaluating the peel strength of the plastic sliding layer of a laminate for sliding surface bearings
Assignee: Kolbenschmidt AG
•
Filing: 1986-07-03
•
Granted: 1988-01-05
•
Expires: 2006-07-03
Abstract
Abstract For an evaluation of the peel strength of a plastic sliding layer of a laminate for sliding surface bearings, which laminate comprises a steel backing, a porous sintered bronze layer on said steel backing, and a mixture of polytetrafluoroethylene which fills the pores of the bronze layer and constitutes a sliding layer on the bronze layer, the surface of the sliding layer of a sample that has been blanked from the laminate for sliding surface bearings is activated and adhesively joined to the end face of a testing bar of a testing apparatus in accordance with ISO Standard 4624. The ultimate tensile stress is then determined.
Inventors
- 👤 Hans-Paul Baureis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 17:43
CPC Classifications
G; G01; G01N; G01N19/00; G01N19/04; F; F16; F16C; F16C33/00; F16C33/02; G01N2203/00; G01N2203/0058; G01N2203/0091
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
242 words
A method of evaluating the pell strength of a plastic sliding layer of a laminate for sliding surface bearings, which comprises a metallic backing layer, a sintered or sprayed-on porous bronze layer having a thickness of 0.1 to 1.0 mm and containing a rolled-in pore filler and on said bronze layer a sliding layer having a thickness of 0.005 to 1.0 mm and made of perfluoro polymers, which may contain one or more first additives for improving the emergency running properties, said first additives selected from the group consisting of lead, graphite and molybdenum disulfide, individually or in combination, and, if desired, also one or more second additives for improving the wear resistance and the load-carrying capacity, said second additives selected from the group consisting of glass fibers, carbon fibers and glass beads, individually or in combination, the method comprising the steps of: first mechanically and then, chemically activating with a solution the surface of the sliding layer of a sample punched from the laminate for sliding surface bearings; subsequently drying the sample; adhesively joining the sample to a mechanically roughened end face of a testing steel cylinder of a testing apparatus in accordance with ISO Standard 4624; and when the adhesive has cured, severing the sliding layer at the outside periphery of the testing cylinder as far as to the bronze layer, and determining the ultimate tensile stress of a joint comprising the sliding layer in accordance with ISO Standard 4624.
Claim 2
Independent Claim
242 words
A method of evaluating the pell strength of a plastic sliding layer of a laminate for sliding surface bearings, which comprises a metallic backing layer, a sintered or sprayed-on porous bronze layer having a thickness of 0.1 to 1.0 mm and containing a rolled-in pore filler and on said bronze layer a sliding layer having a thickness of 0.005 to 1.0 mm and made of perfluoro polymers, which may contain one or more first additives for improving the emergency running properties, said first additives selected from the group consisting of lead, graphite and molybdenum disulfide, individually or in combination, and, if desired, also one or more second additives for improving the wear resistance and the load-carrying capacity, said second additives selected from the group consisting of glass fibers, carbon fibers and glass beads, individually or in combination, the method comprising the steps of: first mechanically and then, chemically activating with a solution the surface of the sliding layer of a sample punched from the laminate for sliding surface bearings; subsequently drying the sample; adhesively joining the sample to a mechanically roughened end face of a testing steel cylinder of a testing apparatus in accordance with ISO Standard 4624; and when the adhesive has cured, severing the sliding layer at the outside periphery of the testing cylinder as far as to the bronze layer, and determining the ultimate tensile stress of a joint comprising the sliding layer in accordance with ISO Standard 4624.
Claim 3
Dependent Claim
49 words
The method according to claim 1, wherein the surface of the sliding layer of the sample is roughened wherein an abrasive is applied to said surface under a light pressure and is reciprocated on said surface a plurality of times in two directions at right angles to each other.
Claim 4
Dependent Claim
15 words
The method according to claim 2, wherein the abrasive is reciprocated three to ten times.
Claim 5
Dependent Claim
39 words
The method according to claim 1 or 2, wherein the surface of the sliding layer of the sample is activated by dipping the sample for 0.5 to 5 minutes into an etching solution which is suitable for perfluoro polymers.
Claim 6
Dependent Claim
29 words
The method according to claim 4, wherein the etching solution comprises one of a solution of liquid ammonia and sodium and a solution of tetrahydrofurane with naphthalene and sodium.
Claim 7
Dependent Claim
35 words
The method according to claim 1 or 2, for a metal-containing sliding layer, wherein the surface of the sample is demetallized by dipping the sample into an aqueous solution of acetic acid and hydrogen peroxide.
Claim 8
Dependent Claim
22 words
The method according to claim 1, wherein the ultimate tensile stress is determined at a stressing speed of 0.05 to 0.5 mm/s.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-01-04 | 1991-07-06 | 1992-01-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-01-04 | 1995-07-06 | 1996-01-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-01-04 | 1999-07-06 | 2000-01-05 | $7700.00 | Window Closed / Lapsed |