Coating for EMI shielding

Claim 2

An electrically conductive water based, air dried, paint having a cured surface resistivity of less than about 10 Ω/square comprising: metallic flake selected from a group consisting of copper, silver, iron phosphide, gold, nickel, mixtures thereof, and substrates coated therewith, the flakes having a thickness of not more than about 3 microns and a long dimension of at least about 10 microns but not intended for applying the paint; polymeric latex, the polymer having a molecular weight of at least about 90,000, a backbone, and pendant acidic functional moieties in the backbone in sufficient quantity to provide the polymer with an acid number of at least about 7 but not more than about 195, the latex being present in the paint in a ratio of about 15% by weight to about 100% by weight (Polymer basis) of the retallic flake present in the paint; an air drying, co-solvent having a boiling point greater than water and being capable of agglomerating particles of the latex polymer to form a coherent coating upon a surface being painted in a quantity of at least 2% by weight and 20% by weight of polymer in the latex; a pH adjusting compound in a quantity sufficient to adjust the pH of the paint to between about 5 and 11; and at least one non-silicone, non-silicate based film forming enhancer in a quantity of between about 1% by weight and 5% by weight of the metallic flake present in the paint.

Claim 3

The paint of claim 1 including an anti-foaming agent in a quantity not exceeding about 1% by weight of the nickel in the paint.

Claim 4

The paint of claim 1 including finely divided carbon black or colloidal silica in an amount not exceeding about 5% by weight of the nickel in the paint.

Claim 5

The paint of claim 1, the co-solvent being selected from a group consisting of: ester alcohols having a molecular weight exceeding about 118, mono ethers of ethylene, propylene or butylene glycols, and acetates thereof, or methyl or ethyl esters thereof, 4-hydroxy-4 methyl-2 pentanone, and mixtures thereof.

Claim 6

The paint of claim 1, the latex being partially crosslinked, having pendant carboxylate based moieties, and having a latex particle size of between about 170 and 500 nanometers.

Claim 7

The paint of claim 1, pH adjusting compound being a fugitive amine selected from a group consisting of primary and secondary amines of C 1 -C 5 and ammonia.

Claim 8

The paint of claim 1, the film forming enhancer having a salt of at least one fatty acid, the salt having an iodine value of at least about 85 but not more than about 250 and including an unsaturate selected from a group consisting of palmitoleic, oleic, linoleic, eleostearic, sterculic, arachidonic, ricinoleic, cetoleic, erucic, nervonic, mycolipenic, linolenic acids and mixtures thereof in a proportion of at least about 25% by weight of the fatty acid salt.

Claim 9

The paint of claim 7, the unsaturate comprising at least about 50% by weight of the fatty acid salt.

Claim 10

An electrically conductive water based air dried paint having a cured surface resistivity of less than about 10 Ω/square comprising: nickel flake, the flake having a thickness of not more than about 3 microns and a long dimension of at least about 10 microns but not greater than passable through a spray nozzle intended for applying the paint; polymeric latex, the polymer having a molecular weight of at least about 90,000, a backbone, and carboxylate based functional moieties pendant from a backbone thereof in a quantity sufficient to provide the polymer with an acid number of at least about 10 but not more than about 195, the latex being present in the paint in a ratio of about 15% by weight to about 100% by weight (polymer basis) of the weight of nickel present in the paint; an air drying, water soluable, co-solvent selected from a group consisting of: ester alcohols having a molecular weight exceeding about 118, elevated molecular weight alcohols, monoethers of ethylene, propylene, or methylene glycols, and acetates thereof or methyl or ethyl ethers thereof, and 4-hydroxy-4 methyl-2 pentanone, and mixtures thereof; a pH adjusting compound selected from a group consisting of primary tertiary and secondary amines of C 1 -C 5 and ammonia in a quantity sufficient to adjust the pH of the paint to between about 5 and about 11; and film forming enhancer of non-silicone, non-silicate base, present in the paint in a quantity of about 1% by weight and about 5% by weight of the nickel present in the paint.

Claim 11

An electrically conductive water based air dried paint having a cured surface resistivity of less than about 10 Ω/square comprising: nickel flake, the flake having a thickness of not more than about 3 microns and a long dimension of at least about 10 microns but not greater than passable through a spray nozzle intended for applying the paint; polymeric latex, the polymer having a molecular weight of at least about 90,000, a backbone, and carboxylate based functional moieties pendant from a backbone thereof in a quantity sufficient to provide the polymer with an acid number of at least about 10 but not more than about 195, the latex being present in the paint in a ratio of about 15% by weight to about 100% by weight (polymer basis) of the weight of nickel present in the paint; an air drying, water soluable, co-solvent selected from a group consisting of: ester alcohols having a molecular weight exceeding about 118, elevated molecular weight alcohols, monoethers of ethylene, propylene, or methylene glycols, and acetates thereof or methyl or ethyl ethers thereof, and 4-hydroxy-4 methyl-2 pentanone, and mixtures thereof; a pH adjusting compound selected from a group consisting of primary tertiary and secondary amines of C 1 -C 5 and ammonia in a quantity sufficient to adjust the pH of the paint to between about 5 and about 11; and film forming enhancer of non-silicone, non-silicate base, present in the paint in a quantity of about 1% by weight and about 5% by weight of the nickel present in the paint.

Claim 12

The paint of claim 9, the latex including a copolymer of at lesat two monomers selected from a group consisting of styrene, acrylic esters having between about 5 and about 12 carbon atoms, acrylonitrile, methacrylonitrile, vinyl acetates, multifunctional acrylates, multifunctional methacrylates, vinyl or vinylidene chloride, and acrylamides, at least one of the monomers being a mono or dicarboxylic acid.

Claim 13

The paint of claim 10, the pH being adjusted to be between about 6 and 9.

Claim 14

The paint of claim 11, the film forming enhancer being a salt of at least one fatty acid, the salt having an iodine number of at least 7 but not more than about 195, and the fatty acid including an unsaturate selected from a group consisting of palmitoleic, oleic, linoleic, eleostearic, sterculic, arachidonic, ricinoleic, cetoleic, erucic, nervonic, mycolipenic, linolenic acids and mixtures thereof in a proportion of at least about 25% by weight of the fatty acid.

Claim 15

The paint of claim 12 including an anti-foaming agent in a quantity not exceeding about 1% by weight of the nickel in the paint.

Claim 16

The paint of claim 12 including finely divided carbon black or a colloidal silica in an amount not exceeding about 5% by weight of the nickel in the paint.

Claim 17

The paint of claim 12, the unsaturate comprising at least about 50% by weight of the fatty acid.

Claim 18

The paint of claim 5, the latex being a co-polymer of at least two monomers selected from a group consisting of: an unsaturated carboxylic acid containing monomer, 0.5-15% by weight; styrene 0.5-65% by weight; acrylate or methacrylate esters, 35-90% by weight; acrylonitrile or methacrylonitrile, 0-20% by weight; an acrylamide or N-substituted acrylamide, 0-15% by weight; and a multi-functional acrylate selected from a group consisting of ethylene glycol, dimethylacrylate, trimethyl propane, and trimethylacrylate, 0-5% by weight.

Claim 19

The paint of claim 16, the metallic flake being one of nickel or a nickel coated substrate.

Claim 20

The paint of claim 1, the polymer forming the polymeric latex being a core-shell structure having a substantial majority proportion of backbone pendant acidic functionality present in the structure present in the shell.

Claim 21

The paint of claim 9, the polymer forming the polymeric latex being a core-shell structure having a substantial majority proportion of backbone pendant acidic functionality present in the structure present in the shell.

Claim 22

The paint of claim 1, the paint being aged at least about 1 week after formation.

Claim 23

The paint of claim 1, the paint being aged at least about 1 month after formation.

Claim 24

The paint of claim 9, the paint being aged at least about 1 week after formation.

Claim 25

The paint of claim 5, the latex being a co-polymer of at least two monomers selected from a group consisting of: an unsaturated carboxylic acid containing monomer, 0.5-15% by weight; styrene, 0.5-65% by weight; acrylate or methacrylate esters, 35-90% by weight; acrylonitrile or methacrylonitrile, 0-20% by weight; an acrylamide, 0-15% by weight; and a multifunctional acrylate or methacrylate selected from a group consisting of ethylene glycol dimethacrylate, and trimethylol propane trimethacrylate, 0-5% by weight.