High performance molding compounds for shielding electromagnetic interference

Claim 2

A molding composition comprising a thermosetting resin binder and an electrically-conductive filler comprising particles of carbon black, graphite and a conductive metal, said conductive filler being present in a minimum amount sufficient to provide (a) a total conductive filler surface area of about 2×10 13 to about 2×10 14 μ 2 /cm 3 of molded composition, and (b) a shielding effectiveness of at least 20 dB of attenuation in EMI emissions over a frequency range of 0.5 to 1000 Mhz. as measured by transmission line testing, wherein the binder is selected from the group consisting of phenolic resins, epoxy resins and unsaturated polyester resins, and wherein the conductive metal particles are selected from the group consisting of steel, aluminum, copper, zinc, nickel, lead, silver, gold and mixtures thereof.

Claim 3

The composition of claim 2 having a shielding effectiveness of at least 30 dB of attenuation in EMI emissions over the frequency range of 0.5 to 1000 Mhz.

Claim 4

The composition of claim 2 wherein the binder is a phenolic resin.

Claim 5

The composition of claim 3 wherein the phenolic resin is a one-stage phenol-aldehyde resin.

Claim 6

The composition of claim 3 wherein the phenolic resin is a thermosettable two-stage phenol-aldehyde resin.

Claim 7

The composition of claim 2 wherein the conductive metal particles are flaked or fibrous aluminum.

Claim 8

The composition of claim 1 including inert fillers.

Claim 9

The composition of claim 7 including a particulate refractory ferroalloy.

Claim 10

The composition of claim 8 wherein the ferroalloy is ferrophosphorous.

Claim 11

An electrically conductive molding compound having an EMI shielding effectiveness of at least 20 dB of attenuation over a frequency range of 0.5 to 1000 Mhz. as measured by transmission line testing, said compound comprising a thermosettable resin binder and an electrically conductive filler comprising particles of carbon black, graphite and a conductive metal wherein the filler is present in a minimum amount sufficient to provide a total conductive filler surface area of about 2×10 13 to about 2×10 14 μ 2 /cm 3 of molded compound, wherein the binder is selected from the group consisting of phenolic resins, epoxy resins and unsaturated polyester resins, and wherein the conductive metal particles are selected from the group consisting of steel, aluminum, copper, zinc, nickel, lead, silver, gold and mixtures thereof.

Claim 12

An electrically conductive molding compound having an EMI shielding effectiveness of at least 20 dB of attenuation over a frequency range of 0.5 to 1000 Mhz. as measured by transmission line testing, said compound comprising a thermosettable resin binder and an electrically conductive filler comprising particles of carbon black, graphite and a conductive metal wherein the filler is present in a minimum amount sufficient to provide a total conductive filler surface area of about 2×10 13 to about 2×10 14 μ 2 /cm 3 of molded compound, wherein the binder is selected from the group consisting of phenolic resins, epoxy resins and unsaturated polyester resins, and wherein the conductive metal particles are selected from the group consisting of steel, aluminum, copper, zinc, nickel, lead, silver, gold and mixtures thereof.

Claim 13

The molding compound of claim 10 having a shielding effectiveness of at least 30 dB of attenuation to EMI emissions over a frequency range of 0.5 to 1000 Mhz.

Claim 14

The molding compound of claim 11 wherein the binder is a phenolic resin.

Claim 15

The molding compound of claim 12 wherein the phenolic resin is a one-stage phenol-aldehyde resin.

Claim 16

The molding compound of claim 12 wherein the phenolic resin is a thermosettable two-stage phenol-aldehyde resin.

Claim 17

The molding compound of claim 12 including ferrophosphorous.

Claim 18

The molding compound of claim 10 including inert filler.

Claim 19

A molded composite made from the compound of claim 10.

Claim 20

A molded composite made from a compound of claim 11.

Claim 21

A molded composite made from a compound of claim 12.

Claim 22

A molded composite made from the compound of claim 16.

Claim 23

A molding composition comprising a thermosettable resin binder and a conductive filler system comprising particles of carbon black, graphite and a conductive metal, said conductive fillers being present in minimum amounts sufficient to import to the composition at least 20 dB of constant attenuation to EMI emissions over a frequency range of 0.5 to 1000 Mhz. as measured by transmission line testing and without substantial reduction in mechanical properties, wherein the binder is selected from the group consisting of phenolic resins, epozy resins and unsaturated polyester resins, and wherein the conductive metal particles are selected from the group consisting of steel, aluminum, copper, zinc, nickel, lead, silver, gold and mixtures thereof.

Claim 24

A molding composition comprising a thermosettable resin binder and a conductive filler system comprising particles of carbon black, graphite and a conductive metal, said conductive fillers being present in minimum amounts sufficient to import to the composition at least 20 dB of constant attenuation to EMI emissions over a frequency range of 0.5 to 1000 Mhz. as measured by transmission line testing and without substantial reduction in mechanical properties, wherein the binder is selected from the group consisting of phenolic resins, epozy resins and unsaturated polyester resins, and wherein the conductive metal particles are selected from the group consisting of steel, aluminum, copper, zinc, nickel, lead, silver, gold and mixtures thereof.

Claim 25

The composition of claim 21 wherein the thermosettable resin binder is a phenolic resin and the conductive filler comprises carbon black, graphite and at least one particulate metal selected from aluminum, copper, zinc or lead, said fillers being present in minimum amounts sufficient to impart from about 30 to 70 dB of constant attenuation in EMI emission over frequencies between 0.5 to 1000 Mhz. as measured by transmission line testing.

Claim 26

The composition of claim 23 including ferrophosphorous.