Method and apparatus for applying metal cladding on surfaces and products formed thereby
Assignee: Individual
•
Filing: 1986-02-13
•
Granted: 1987-12-22
•
Expires: 2006-02-13
Abstract
Abstract Small, preferably micronsized hollow glass or ceramic or carbon spheres (or a mix thereof) sprayed into a uncured or wet resin material which is formed into a layer and after curing of the resin layer, it is abraded, sand or grit blasted so as to rupture the outermost layer of spheres or voids to provide a plurality of anchor sites undercuts or nooks and crannies. A thermally sprayed metal, such as copper, becomes embedded into the undercuts, nooks and crannies, such that the bond or adherent strength is greatly improved. This micronsized glass, ceramic carbon spheres and/or pores greatly increases the bond strength by providing better undercuts in the surface to be sprayed by molten metal and provide the capability of depositing thicker layers without jeopardizing the bond.
Inventors
- 👤 Louis M. Riccio
- 👤 Alexander A. Bosna
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 13:45
CPC Classifications
C; C23; C23C; C23C4/00; C23C4/02; C23C4/04; F; F28; F28F; F28F1/00; F28F1/10; F28F1/12; F28F1/24; F28F1/30; F28F21/00; F28F2275/00; F28F2275/02; F28F2275/025
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
128 words
In a method of applying an antifouling coating to a marine surface of a metal selected from the group comprising copper and/or copper alloys--such as copper-nickel, the improvement comprising the steps of: (1) coating said marine surface with a curable adhesive resin, (2) spraying a layer of inorganic hollow spheres in the size range of greater than 10 microns onto said adhesive resin prior to curing of same, (3) curing said curable layer, (4) after step (3), abrading said layer of hollow inorganic spheres to fracture same and produce a matrix of anchor sites, undercuts, nooks and crannies in the surface thereof, and (5) thermally spraying molten metal particles on said matrix to fill said undercuts, nooks and crannies with said metal in one or more passes thereof.
Claim 2
Dependent Claim
128 words
In a method of applying an antifouling coating to a marine surface of a metal selected from the group comprising copper and/or copper alloys--such as copper-nickel, the improvement comprising the steps of: (1) coating said marine surface with a curable adhesive resin, (2) spraying a layer of inorganic hollow spheres in the size range of greater than 10 microns onto said adhesive resin prior to curing of same, (3) curing said curable layer, (4) after step (3), abrading said layer of hollow inorganic spheres to fracture same and produce a matrix of anchor sites, undercuts, nooks and crannies in the surface thereof, and (5) thermally spraying molten metal particles on said matrix to fill said undercuts, nooks and crannies with said metal in one or more passes thereof.
Claim 3
Dependent Claim
44 words
The method and system of applying an antifouling coating as defined in claim 1 wherein the step of (2) spraying includes placing an electric charge on each inorganic hollow sphere, and electrically attracting the charged hollow spheres to the surface of said curable layer.
Claim 4
Dependent Claim
45 words
The invention defined in claim 1 wherein step (2) spraying said resin adhesive with a layer of inorganic hollow spheres is carried out by spraying said spheres upon said adhesive resin in a size range of about 10 to 300 microns to fill said resin.
Claim 5
Dependent Claim
40 words
The invention defined in claim 1 including spraying said hollow spheres onto said curable adhesive resin until said uncured adhesive has a dull matte like finish, and recycling of sprayed hollow spheres which did not adhere to said adhesive resin.
Claim 6
Dependent Claim
28 words
The invention defined in claim 1 wherein in step (1) the adhesive is a U.V. sensitive resin and including subjecting same to U.V. to cure prior to abrading.
Claim 7
Dependent Claim
19 words
The invention defined in claim 1 wherein said hollow spheres are in a proportion of 100-250 percent by volume.
Claim 8
Dependent Claim
29 words
The invention defined in claim 1 wherein in step (1), the hollow spheres are glass or ceramic and are in a size range of about 10 to 300 microns.
Claim 9
Dependent Claim
14 words
The invention defined in claim 7 wherein said hollow spheres are of different sizes.
Claim 10
Dependent Claim
14 words
A marine surface formed by any one of the methods defined in claims 1-8.
Claim 11
Independent Claim
105 words
A method of rigidly securing a metal layer to a substrate surface comprising: (1) applying a curable adhesive layer to said substrate surface; (2) spraying at least a layer of hollow beads in a selected size range to said curable adhesive layer; (3) then curing said curable adhesive layer; (4) fracturing at least the ones of said hollow spheres secured on the exposed surface by abrading away at least a portion of the hollow bead surface to form an exposed matrix of undercuts, nooks and crannies in said matrix; (5) spraying molten metal into said exposed undercuts, nooks and crannies to form said metal layer.
Claim 12
Independent Claim
105 words
A method of rigidly securing a metal layer to a substrate surface comprising: (1) applying a curable adhesive layer to said substrate surface; (2) spraying at least a layer of hollow beads in a selected size range to said curable adhesive layer; (3) then curing said curable adhesive layer; (4) fracturing at least the ones of said hollow spheres secured on the exposed surface by abrading away at least a portion of the hollow bead surface to form an exposed matrix of undercuts, nooks and crannies in said matrix; (5) spraying molten metal into said exposed undercuts, nooks and crannies to form said metal layer.
Claim 13
Dependent Claim
19 words
The invention defined in claim 10 wherein said hollow beads range in size from about 10 to 300 microns.
Claim 14
Dependent Claim
21 words
The invention defined in claim 11 wherein said hollow beads comprise 100-250 percent by volume of said matrix system when applied.
Claim 15
Dependent Claim
37 words
The invention defined in claim 10 wherein said matrix comprises an epoxy resin and a plurality of ruptured micronsized beads selected from the group consisting of hollow glass or ceramic or ceramic beads or a mix thereof.
Claim 16
Dependent Claim
19 words
A substrate surface having a metal layer formed according to any one of the methods defined in claims 10-13.
Claim 17
Independent Claim
85 words
A method of improving the mechanical adherence between two materials, comprising: (1) spraying a plurality of small sized frangible hollow beads in one of said materials, while said one of said materials is in a liquid state; (2) solidifying said one of said materials; (3) rupturing the surface ones of said frangible hollow beads to form undercuts, nooks and crannies; (4) flowing the other of said materials in a molten state into said undercuts, nooks and crannies; and (5) solidifying said other of said materials.
Claim 18
Independent Claim
85 words
A method of improving the mechanical adherence between two materials, comprising: (1) spraying a plurality of small sized frangible hollow beads in one of said materials, while said one of said materials is in a liquid state; (2) solidifying said one of said materials; (3) rupturing the surface ones of said frangible hollow beads to form undercuts, nooks and crannies; (4) flowing the other of said materials in a molten state into said undercuts, nooks and crannies; and (5) solidifying said other of said materials.
Claim 19
Dependent Claim
65 words
The method defined in claim 15 wherein the first one of said materials is sprayed upon a forming surface, said frangible hollow beads are selected from the group consisting of glass and, ceramic or carbon and are ruptured by abrading, and said other of said materials is a molten metal that is sprayed upon said one of said materials and said undercuts, nooks and crannies.
Claim 20
Independent Claim
103 words
A method of metal cladding a surface comprising; (1) applying an adhesive layer to said surface; (2) spraying a layer of hollow glass or ceramic or carbon micron size spheres or a mix thereof to said adhesive layer; (3) curing said adhesive layer after spraying on of said spheres; (4) rupturing at least the surface ones of said spheres to produce a matrix of undercuts uniformly over said surface; and (5) thermally spraying metal in molten particle form applying upon said matrix to fill said undercuts, nooks and crannies with molten metal which flows into and conforms to the surfaces of said undercuts.
Claim 21
Independent Claim
103 words
A method of metal cladding a surface comprising; (1) applying an adhesive layer to said surface; (2) spraying a layer of hollow glass or ceramic or carbon micron size spheres or a mix thereof to said adhesive layer; (3) curing said adhesive layer after spraying on of said spheres; (4) rupturing at least the surface ones of said spheres to produce a matrix of undercuts uniformly over said surface; and (5) thermally spraying metal in molten particle form applying upon said matrix to fill said undercuts, nooks and crannies with molten metal which flows into and conforms to the surfaces of said undercuts.
Claim 22
Dependent Claim
26 words
The method defined in claim 17 wherein in step (2), said spheres are sprayed until said uncured adhesive has a dull matte like and unshinny apperance.
Claim 23
Dependent Claim
18 words
A building structure having a metal cladding applied according to the invention defined in claim 17 or 18.
Claim 24
Dependent Claim
15 words
A sculpture having a metal cladding applied according to one of claim 17 or 18.
Claim 25
Dependent Claim
16 words
A composite panel having a metal cladding applied according to one of claims 17 or 18.
Claim 26
Dependent Claim
54 words
The method of metal cladding a surface as defined in claim 17 wherein the step of (2) spraying a layer of hollow glass or ceramic or carbon micronsize spheres includes placing an electric charge on each sphere and electrically attracting the charged spheres to the surface of said adhesive layer prior to step (3).
References Cited (Backward Citations)
US819125A
Cited
US3144349A
Cited
US3325303A
Cited
US3179531A
Cited
US3097932A
Cited
US3476577A
Cited
US3775157A
Cited
JPS5322110A
Cited
JPS54135851A
Cited
US4182641A
Cited
US4226906A
Cited
US4303730A
Cited
JPS5633485A
Cited
US4307142A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-12-21 | 1991-06-22 | 1991-12-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-12-21 | 1995-06-22 | 1995-12-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-12-21 | 1999-06-22 | 1999-12-22 | $7700.00 | Window Closed / Lapsed |