Dielectric ceramic composition
Assignee: Taiyo Yuden Co Ltd
•
Filing: 1986-07-24
•
Granted: 1987-12-15
•
Expires: 2006-07-24
Abstract
Abstract A dielectric ceramic composition which comprises a mixture of 7 to 25 mole% of BaTiO3, 0.1 to 15 mole% of Bi2O3, 50 to 65 mole% of TiO2, 0.1 to 5 mole% of LaO3/2 and 15 to 45 mole% of NdO3/2 in a total of 100 mole%. At least one member selected from the group consisting of Y2O3, Gd2O3 and CeO2, and at least one member selected from the group consisting of Cr2O3, MnO2, NiO and CoO are further added to the mixture in amounts of from 0.1 to 5 parts by weight and from 0.01 to 1 part by weight per 100 parts by weight of the mixture, respectively.
Inventors
- 👤 Kazuo Sasazawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 16:23
CPC Classifications
H; H01; H01G; H01G4/00; H01G4/002; H01G4/258; C; C04; C04B; C04B35/00; C04B35/01; C04B35/46; C04B35/462
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
157 words
A dielectric ceramic composition which consists essentially of (A) 100 parts by weight of a mixture of 7 to 25 mole % of BaTiO 3 , 0.1 to 15 mole % of Bi 2 O 3 , 50 to 65 mole % of TiO 2 , 0.1 to 5 mole % of LaO 3/2 and 15 to 45 mole % of NdO 3/2 in a total amount of 100 mole % as main components, (B) from 0.1 to 5 parts by weight, per 100 parts by weight of the said components (A), of at least one member selected from the group consisting of Y 2 O 3 , Gd 2 O 3 and CeO 2 , and (C) from 0.01 to 1.0 part by weight, per 100 parts by weight of said main components (A), of at least one member selected from the group consisting of Cr 2 O 3 , MnO 2 , NiO and CoO.
Claim 2
Dependent Claim
157 words
A dielectric ceramic composition which consists essentially of (A) 100 parts by weight of a mixture of 7 to 25 mole % of BaTiO 3 , 0.1 to 15 mole % of Bi 2 O 3 , 50 to 65 mole % of TiO 2 , 0.1 to 5 mole % of LaO 3/2 and 15 to 45 mole % of NdO 3/2 in a total amount of 100 mole % as main components, (B) from 0.1 to 5 parts by weight, per 100 parts by weight of the said components (A), of at least one member selected from the group consisting of Y 2 O 3 , Gd 2 O 3 and CeO 2 , and (C) from 0.01 to 1.0 part by weight, per 100 parts by weight of said main components (A), of at least one member selected from the group consisting of Cr 2 O 3 , MnO 2 , NiO and CoO.
Claim 3
Dependent Claim
171 words
In a ceramic capacitor having a dielectric layer made of a ceramic composition, the improvement comprising: said ceramic composition consists essentially of (A) 100 parts by weight of a mixture of 7 to 25 mole % of BaTiO 3 , 0.1 to 15 mole % of Bi 2 O 3 , 50 to 65 mole % of TiO 2 , 0.1 to 5 mole % of LaO 3/2 and 15 to 45 mole % of NdO 3/2 in a total amount of 100 mole % as main components, (B) from 0.1 to 5 parts by weight, per 100 parts by weight of said main components (A), of at least one member selected from the group consisting of Y 2 O 3 , Gd 2 O 3 and CeO 2 , and (C) from 0.01 to 1.0 part by weight, per 100 parts by weight of said main components (A), of at least one member selected from the group consisting of Cr 2 O 3 , MnO 2 , NiO and CoO.
Claim 4
Dependent Claim
171 words
In a ceramic capacitor having a dielectric layer made of a ceramic composition, the improvement comprising: said ceramic composition consists essentially of (A) 100 parts by weight of a mixture of 7 to 25 mole % of BaTiO 3 , 0.1 to 15 mole % of Bi 2 O 3 , 50 to 65 mole % of TiO 2 , 0.1 to 5 mole % of LaO 3/2 and 15 to 45 mole % of NdO 3/2 in a total amount of 100 mole % as main components, (B) from 0.1 to 5 parts by weight, per 100 parts by weight of said main components (A), of at least one member selected from the group consisting of Y 2 O 3 , Gd 2 O 3 and CeO 2 , and (C) from 0.01 to 1.0 part by weight, per 100 parts by weight of said main components (A), of at least one member selected from the group consisting of Cr 2 O 3 , MnO 2 , NiO and CoO.
Claim 5
Dependent Claim
53 words
The dielectric ceramic composition of claim 1 wherein at least one member selected from the group consisting of Cr 2 O 3 , MnO 2 , NiO and CoO is present in said ceramic composition in an amount of about 0.1 parts by weigth per 100 parts by weight of said main components.
Claim 6
Dependent Claim
53 words
The dielectric ceramic composition of claim 1 wherein at least one member selected from the group consisting of Cr 2 O 3 , MnO 2 , NiO and CoO is present in said ceramic composition in an amount of about 1.0 parts by weight per 100 parts by weight of the main components.
References Cited (Backward Citations)
US4054531A
Cited
JPS5374298A
Cited
JPS5525690A
Cited
JPS56165204A
Cited
US4338403A
Cited
JPS5761667A
Cited
JPS5780603A
Cited
JPS5780604A
Cited
US4394456A
Cited
US4500942A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-12-14 | 1991-06-15 | 1991-12-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-12-14 | 1995-06-15 | 1995-12-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-12-14 | 1999-06-15 | 1999-12-15 | $7700.00 | Window Closed / Lapsed |