US4713180A — Ceramic filter and method for using same

Claim 1

Independent Claim 182 words

A ceramic filter made from a high-melting ceramic material and having an open-celled foam structure, with at least one afflux surface for filtering molten cast iron, said ceramic filter comprising an interior region surrounded by an outer region wherein the bulk density of the outer region of said ceramic filter is higher than the bulk density of the interior region of said ceramic filter, and wherein the ceramic filter has a ratio of filter surface to filter volume in the range of about 0.0003 to 9 m 2 /cm 3 , a specific filter resistance in the range of about 0.1 to 0.9 bar-cm at a fluid flow rate of 5 m 3 /hour, and a pressure loss Δp across the filter which depends on the specific resistance η of the filter, the filter length L, and the surface area of the afflux surface F in accordance with the relationship: ##EQU4## said ceramic material comprising 20-70% by weight of silicon carbide, 10-40% by weight of aluminum oxide, 2-20% by weight of silicon oxide, and 10-30% by weight of a refractory inorganic binder.

Claim 2

Dependent Claim 182 words

A ceramic filter made from a high-melting ceramic material and having an open-celled foam structure, with at least one afflux surface for filtering molten cast iron, said ceramic filter comprising an interior region surrounded by an outer region wherein the bulk density of the outer region of said ceramic filter is higher than the bulk density of the interior region of said ceramic filter, and wherein the ceramic filter has a ratio of filter surface to filter volume in the range of about 0.0003 to 9 m 2 /cm 3 , a specific filter resistance in the range of about 0.1 to 0.9 bar-cm at a fluid flow rate of 5 m 3 /hour, and a pressure loss Δp across the filter which depends on the specific resistance η of the filter, the filter length L, and the surface area of the afflux surface F in accordance with the relationship: ##EQU4## said ceramic material comprising 20-70% by weight of silicon carbide, 10-40% by weight of aluminum oxide, 2-20% by weight of silicon oxide, and 10-30% by weight of a refractory inorganic binder.

Claim 3

Dependent Claim 23 words

The ceramic filter of claim 1 wherein the refractory inorganic binder is selected from the group consisting of monoaluminum phosphate and monochromic phosphate.

Claim 4

Dependent Claim 23 words

The ceramic filter of claim 2 wherein said ceramic material comprises 30-60% by weight of silicon carbide and 10-30% by weight of alumina.

Claim 5

Dependent Claim 30 words

The ceramic filter of claim 1 wherein the ratio of the filter surface to filter volume is in the range of about 0.01 to 0.9 m 2 /cm 3 .

Claim 6

Dependent Claim 20 words

The ceramic filter of claim 1 wherein the afflux surface has a void fraction in the range of about 35-95%.

Claim 7

Dependent Claim 20 words

The ceramic filter of claim 1 wherein the afflux surface has a void fraction in the range of about 70-95%.

Claim 8

Dependent Claim 36 words

The ceramic filter of claim 1 wherein the bulk density in the outer region of the filter is about 1.2 to 10 times as great as the bulk density in the interior region of the filter.

Claim 9

Dependent Claim 27 words

The ceramic filter of claim 7 wherein the higher bulk density of the outer region of the filter is achieved by enclosing the filter within a frame.

Claim 10

Dependent Claim 29 words

The ceramic filter of claim 8 wherein the frame is made from a material selected from the group consisting of an organically set, refractory granular material and a metal.

Claim 11

Independent Claim 181 words

A method for filtering molten iron which comprises: (a) providing a flowing mass of molten iron; (b) providing a ceramic filter made from a high melting ceramic material and having an open-celled foam structure with at least one afflux surface for filtering molten cast iron, said ceramic filter comprising an interior region surrounded by an outer region wherein the bulk density of the outer region of said ceramic filter is higher than the bulk density of the interior region of said ceramic filter, said ceramic material comprising 20-70% by weight of silicon carbide, 10-40% by weight of aluminum oxide, 2-20% by weight of silicon oxide, and 10-30% by weight of a refractory inorganic binder, (c) positioning said ceramic filter in a casting system near the location where the molten iron has its highest kinetic energy; and (d) causing the mass of molten iron to flow tangentially by the afflux surface of said ceramic filter and creating turbulent flow in front of the afflux plane of said ceramic filter thereby causing the mass of molten iron to pass through said ceramic filter.

Claim 12

Independent Claim 181 words

A method for filtering molten iron which comprises: (a) providing a flowing mass of molten iron; (b) providing a ceramic filter made from a high melting ceramic material and having an open-celled foam structure with at least one afflux surface for filtering molten cast iron, said ceramic filter comprising an interior region surrounded by an outer region wherein the bulk density of the outer region of said ceramic filter is higher than the bulk density of the interior region of said ceramic filter, said ceramic material comprising 20-70% by weight of silicon carbide, 10-40% by weight of aluminum oxide, 2-20% by weight of silicon oxide, and 10-30% by weight of a refractory inorganic binder, (c) positioning said ceramic filter in a casting system near the location where the molten iron has its highest kinetic energy; and (d) causing the mass of molten iron to flow tangentially by the afflux surface of said ceramic filter and creating turbulent flow in front of the afflux plane of said ceramic filter thereby causing the mass of molten iron to pass through said ceramic filter.

Claim 13

Dependent Claim 47 words

The method of claim 10 wherein the mass of molten iron is first caused to flow tangentially by the afflux surface of the filter in a direction essentially parallel to the afflux surface and then is deflected to create turbulence directly in front of the afflux surface.

Claim 14

Dependent Claim 35 words

The method of claim 10 wherein the afflux surface is oriented at an angle which is in the range of about 0° to 90° to the direction of flow of the molten mass of iron.

Claim 15

Dependent Claim 17 words

The method of claim 12 wherein the angle of orientation is in the range of about 0°-79°.

Claim 16

Dependent Claim 13 words

The method of claim 13 wherein the angle of orientation is about 0°.

Claim 17

Dependent Claim 18 words

The method of claim 10 wherein the pressure loss across the filter during a casting process is maintained.

Claim 18

Independent Claim 221 words

A method for filtering molten iron which comprises: (a) providing a flowing mass of molten iron; (b) causing said flowing mass of molten iron to pass through a ceramic filter while creating turbulent flow in front of the ceramic filter wherein said filter is made from a high-melting ceramic material and has an open-celled foam structure, and at least one afflux surface, an outer region of said ceramic filter surrounding an interior region of said ceramic filter, the bulk density of the outer region of said ceramic filter being higher than the bulk density in the interior region of said ceramic filter, said ceramic material comprising 20-70% by weight of silicon carbide, 10-40% by weight of aluminum oxide, 2-20% by weight of silicon oxide, and 10-30% by weight of a refractory inorganic binder, said ceramic filter having a ratio of filter surface to filter volume in the volume in the range of about 0.0003 to 9 m 2 /cm 3 , a specific filter resistance in the range of about 0.1 to 0.9 bar-cm at a fluid flow rate of 5 m 3 /hour, and a pressure loss Δp across the filter which depends on the specific resistance η of the filter, the filter length L, and the surface area of the afflux plane F in accordance with the relationship ##EQU5##

Claim 19

Independent Claim 221 words

A method for filtering molten iron which comprises: (a) providing a flowing mass of molten iron; (b) causing said flowing mass of molten iron to pass through a ceramic filter while creating turbulent flow in front of the ceramic filter wherein said filter is made from a high-melting ceramic material and has an open-celled foam structure, and at least one afflux surface, an outer region of said ceramic filter surrounding an interior region of said ceramic filter, the bulk density of the outer region of said ceramic filter being higher than the bulk density in the interior region of said ceramic filter, said ceramic material comprising 20-70% by weight of silicon carbide, 10-40% by weight of aluminum oxide, 2-20% by weight of silicon oxide, and 10-30% by weight of a refractory inorganic binder, said ceramic filter having a ratio of filter surface to filter volume in the volume in the range of about 0.0003 to 9 m 2 /cm 3 , a specific filter resistance in the range of about 0.1 to 0.9 bar-cm at a fluid flow rate of 5 m 3 /hour, and a pressure loss Δp across the filter which depends on the specific resistance η of the filter, the filter length L, and the surface area of the afflux plane F in accordance with the relationship ##EQU5##

Claim 20

Dependent Claim 90 words

A ceramic filter made from a high-melting ceramic material and having an open-cell foam structure, with at least one afflux surface, said ceramic filter comprising an interior region surrounded by an outer region, wherein the bulk density of the outer region of said ceramic filter is higher than the bulk density of the interior region of said ceramic filter, said ceramic material comprising 20-70% by weight of silicon carbide, 10-40% by weight of aluminum oxide, 2-20% by weight of silicon oxide, and 10-30% by weight of a refractory inorganic binder.

Claim 21

Dependent Claim 90 words

A ceramic filter made from a high-melting ceramic material and having an open-cell foam structure, with at least one afflux surface, said ceramic filter comprising an interior region surrounded by an outer region, wherein the bulk density of the outer region of said ceramic filter is higher than the bulk density of the interior region of said ceramic filter, said ceramic material comprising 20-70% by weight of silicon carbide, 10-40% by weight of aluminum oxide, 2-20% by weight of silicon oxide, and 10-30% by weight of a refractory inorganic binder.

Claim 22

Dependent Claim 37 words

The ceramic filter of claim 17 wherein the bulk density in the outer region of said ceramic filter is about 1.2 to 10 times higher than the bulk density in the interior region of said ceramic filter.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1990-12-14	1991-06-15	1991-12-15	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1994-12-14	1995-06-15	1995-12-15	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	1998-12-14	1999-06-15	1999-12-15	$7700.00	Window Closed / Lapsed

Ceramic filter and method for using same

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag