Method of producing blown thermoplastic foil with low thickness tolerances
Assignee: Reifenhauser KG
•
Filing: 1986-05-20
•
Granted: 1987-12-08
•
Expires: 2006-05-20
Abstract
Abstract A method of producing a thermoplastic foil with reduced thickness tolerances in which close to the head the temperatures of the mass flow emerging from the heat at various regions corresponding to tempering sectors are detected, the temperature measurements are averaged and the averages are used to form a set point value with which the individual averages are compared and the comparison used to generate a correction signal which is applied to the temperature controller of the respective sector.
Inventors
- 👤 Hartmut Halter
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 15:56
CPC Classifications
B; B29; B29C; B29C48/00; B29C48/25; B29C48/78; B29C48/86; B29C48/87; B29C48/03; B29C48/09; B29C48/10; B29C48/30; B29C48/32; B29C48/325; B29C48/865; B29C48/92; B29C2948/00; B29C2948/92; B29C2948/92504; B29C2948/92609; B29C2948/92647; B29C2948/92704; B29C2948/92819; B29C2948/92857; B29C2948/92904
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
213 words
A method of producing a thermoplastic synthetic resin foil with reduced thickness tolerances, comprising the steps of: extruding a tubular stream of hot thermoplastic synthetic resin through an annular nozzle of a foil blowing head; blowing the tubular stream emerging from said nozzle to expand said stream into a thin-wall foil tube and thereafter cooling said tube to stabilize the resulting foil; subdividing said nozzle into a plurality of independently temperature controllable sectors around the periphery of said stream and the temperatures of which control at least in part the thickness of said foil tube in corresponding regions; detecting the temperature of a mass flow of the hot thermoplastic synthetic resin emerging from said annular nozzle around the periphery of said mass flow and at a location upstream of complete expansion of said tubular stream; averaging said temperature of said mass flow for specific regions thereof corresponding to said sectors to form respective average values; forming a set point value from at least one of said average values; comparing each of said average values with said set point value and generating a respective control signal for each sector upon deviation of said average values from said set point value; and controlling the temperature of each of said sectors with the respective control signals.
Claim 2
Independent Claim
213 words
A method of producing a thermoplastic synthetic resin foil with reduced thickness tolerances, comprising the steps of: extruding a tubular stream of hot thermoplastic synthetic resin through an annular nozzle of a foil blowing head; blowing the tubular stream emerging from said nozzle to expand said stream into a thin-wall foil tube and thereafter cooling said tube to stabilize the resulting foil; subdividing said nozzle into a plurality of independently temperature controllable sectors around the periphery of said stream and the temperatures of which control at least in part the thickness of said foil tube in corresponding regions; detecting the temperature of a mass flow of the hot thermoplastic synthetic resin emerging from said annular nozzle around the periphery of said mass flow and at a location upstream of complete expansion of said tubular stream; averaging said temperature of said mass flow for specific regions thereof corresponding to said sectors to form respective average values; forming a set point value from at least one of said average values; comparing each of said average values with said set point value and generating a respective control signal for each sector upon deviation of said average values from said set point value; and controlling the temperature of each of said sectors with the respective control signals.
Claim 3
Dependent Claim
32 words
The method defined in claim 1 wherein the averaging of said temperature of said mass flow for specific regions thereof corresponding to said sectors to form respective average values forms arithmetic averages.
Claim 4
Dependent Claim
36 words
The method defined in claim 1 wherein the sectors are provided with means for selectively raising and lowering the temperatures of said sectors and said set point value is formed by summation of said average values.
Claim 5
Dependent Claim
58 words
The method defined in claim 1 wherein the sectors are provided exclusively with means for raising the temperatures of said sectors, said step of forming said set point value from at least one of said average values including ascertaining the highest temperature one of said specific regions and using the average value thereof as said set point value.
Claim 6
Dependent Claim
58 words
The method defined in claim 1 wherein the sectors are provided exclusively with means for lowering the temperature of said sectors, said step of forming said set point value from at least one of said average values including ascertaining the lowest temperature one of said specific regions and using the average value thereof as said set point value.
Claim 7
Dependent Claim
40 words
The method defined in claim 1 wherein the temperature of said mass flow of the hot thermoplastic synthetic resin emerging from said annular nozzle around the periphery of said mass flow is detected prior to the expansion of said stream.
Claim 8
Dependent Claim
41 words
The method defined in claim 1 wherein the temperature of said mass flow of the hot thermoplastic synthetic resin emerging from said annular nozzle around the periphery of said mass flow is detected in a region of expansion of said stream.
Claim 9
Dependent Claim
40 words
The method defined in claim 1 wherein the temperature of said mass flow of the hot thermoplastic synthetic resin emerging from said annular nozzle around the periphery of said mass flow is detected by measuring the integral wall temperature thereof.
Claim 10
Dependent Claim
41 words
The method defined in claim 1 wherein the temperature of said mass flow of the hot thermoplastic synthetic resin emerging from said annular nozzle around the periphery of said mass flow is detected by measuring the external surface wall temperature thereof.
Claim 11
Dependent Claim
38 words
The method defined in claim 1 wherein the temperature of said mass flow of the hot thermoplastic synthetic resin emerging from said annular nozzle around the periphery of said mass flow is detected by measuring infrared emissions therefrom.
References Cited (Backward Citations)
GB1396164A
Cited
US3795719A
Cited
US3920365A
Cited
US3974248A
Cited
NL7701816A
Cited
US4189288A
Cited
US4209476A
Cited
US4325897A
Cited
US4339403A
Cited
US4351785A
Cited
US4464318A
Cited
US4425290A
Cited
US4488861A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-12-07 | 1991-06-08 | 1991-12-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-12-07 | 1995-06-08 | 1995-12-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-12-07 | 1999-06-08 | 1999-12-08 | $7700.00 | Window Closed / Lapsed |