Metal-deposited laminated film and method for making capacitor elements using same
Assignee: Toray Industries Inc
•
Filing: 1985-02-04
•
Granted: 1987-11-24
•
Expires: 2005-02-04
Abstract
Abstract Capacitor elements having an ultra thin dielectric layer are made by cutting a metal-deposited polyethylene terephthalate laminated film into a predetermined width, and then separating a metal-deposited polyethylene terephthalate film from the cut laminated film and successively forming the separated metal-deposited polyethylene terephthalate film into a coil. The metal-deposited polyethylene terephthalate laminated film is composed of an oriented ultra thin polyethylene terephthalate film having a thickness of 0.2 to 2.0 μm, on one surface of which a metal layer is formed by vacuum deposition and on the other surface of which a support film is bonded with an adhesive force of 0.1 to 2.0 g/cm.
Inventors
- 👤 Toshiya Yoshii
- 👤 Kazuo Okabe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 14:59
CPC Classifications
B; B32; B32B; B32B15/00; B32B15/04; B32B15/08; B32B27/00; B32B27/06; B32B27/08; B32B27/32; B32B27/36; B32B7/00; B32B7/04; B32B7/12; H; H01; H01G; H01G4/00; H01G4/002; H01G4/005; H01G4/015; H01G4/018; H01G4/20; B32B2250/00; B32B2250/02; B32B2250/03; B32B2255/00; B32B2255/20; B32B2255/205; B32B2307/00; B32B2307/40; B32B2307/42; B32B2323/00; B32B2323/10; B32B2457/00; B32B2457/16; Y; Y10; Y10T; Y10T29/00; Y10T29/43; Y10T29/435; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/24975; Y10T428/31504; Y10T428/31678; Y10T428/31681; Y10T428/31786; Y10T428/31797
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
92 words
A peelable metal-deposited laminated film including an ultrathin peelable layer usable for a capacitor comprising an oriented polyethylene-terephthalate film having a thickness of 0.2 to 2.0 μm, a metal layer vacuum deposited at a thickness of 0.03-0.3 μm on one surface of said polyethylene-terephthalate film, and a propylene copolymer film separably bonded closely to the surface of the polyethylene-terephthalate film opposite to the metal-deposited surface, said films being bonded with an adhesive force of 0.1 to 2.0 g/cm whereby said films may readily be separated from one another without breaking the films.
Claim 2
Dependent Claim
92 words
A peelable metal-deposited laminated film including an ultrathin peelable layer usable for a capacitor comprising an oriented polyethylene-terephthalate film having a thickness of 0.2 to 2.0 μm, a metal layer vacuum deposited at a thickness of 0.03-0.3 μm on one surface of said polyethylene-terephthalate film, and a propylene copolymer film separably bonded closely to the surface of the polyethylene-terephthalate film opposite to the metal-deposited surface, said films being bonded with an adhesive force of 0.1 to 2.0 g/cm whereby said films may readily be separated from one another without breaking the films.
Claim 3
Dependent Claim
22 words
A metal-deposited laminated film according to claim 1, wherein the oriented polyethylene terephthalate film has a thickness of 0.2 to 1.0 μm.
Claim 4
Dependent Claim
40 words
A metal-deposited laminated film according to claim 1, wherein the oriented polyethylene terephthalate film is composee of a polyester having an ethylene terephthalate unit content of at least 90% by mole and a melting point of at least 250° C.
Claim 5
Dependent Claim
21 words
A metal-deposited laminated film according to claim 1, wherein the deposited metal layer has a thickness of 0.03 to 0.3 μm.
Claim 6
Dependent Claim
28 words
A metal-deposited laminated film according to claim 1, wherein the propylene copolymer film has a thickness of 5 to 30 μm and a birefringence of 0 to 0.008.
Claim 7
Dependent Claim
51 words
A metal-deposited laminated film according to claim 1, wherein the propylene copolymer film is made of a copolymer composed of 80 to 97% by mole of propylene units and 3 to 20% by mole of olefin units other than propylene units and having a melting point of 90 to 140° C.
Claim 8
Dependent Claim
17 words
A metal-deposited laminated film according to claim 1, wherein the adhesive force is 0.2 to 0.8 g/cm.
Claim 9
Dependent Claim
107 words
A peelable metal-deposited laminated film including a pair of ultrathin peelable layers usable for a capacitor comprising: (a) a propylene copolymer film; (b) oriented polyethylene-terephthalate films each having a thickness of 0.2 to 2.0 μm, which are separably bonded closely to both surfaces of the propylene copolymer film, said films being bonded with an adhesive force of 0.2 to 2.0 g/cm; and (c) a pair of spaced apart metal layers each of which is vacuum deposited on the surface of each oriented polyethylene-terephthalate film opposite to the surface which is bonded to the propylene copolymer film and each such vacuum-deposited layer having a thickness of 0.03-0.3 μm.
Claim 10
Dependent Claim
107 words
A peelable metal-deposited laminated film including a pair of ultrathin peelable layers usable for a capacitor comprising: (a) a propylene copolymer film; (b) oriented polyethylene-terephthalate films each having a thickness of 0.2 to 2.0 μm, which are separably bonded closely to both surfaces of the propylene copolymer film, said films being bonded with an adhesive force of 0.2 to 2.0 g/cm; and (c) a pair of spaced apart metal layers each of which is vacuum deposited on the surface of each oriented polyethylene-terephthalate film opposite to the surface which is bonded to the propylene copolymer film and each such vacuum-deposited layer having a thickness of 0.03-0.3 μm.
Claim 11
Dependent Claim
21 words
A metal-deposited laminated film according to claim 8, wherein each oriented polyethylene-terephthalate film has a thickness of 0.2 to 1.0 μm.
Claim 12
Dependent Claim
39 words
A metal-deposited laminated film according to claim 8, wherein each oriented polyethylene-terephthalate film is composed of a polyester having an ethylene terephthalate unit content of at least 90% by mole and a melting point of at least 250° C.
Claim 13
Dependent Claim
21 words
A metal-deposited laminated film according to claim 8, wherein each deposited metal layer has a thickness of 0.03 to 0.3 μm.
Claim 14
Dependent Claim
28 words
A metal-deposited laminated film according to claim 8, wherein the propylene copolymer film has a thickness of 5 to 30 μm and a birefringence of 0 to 0.008.
Claim 15
Dependent Claim
51 words
A metal-deposited laminated film according to claim 8, wherein the propylene copolymer film is made of a copolymer composed of 80 to 97% by mole of propylene units and 3 to 20% by mole of olefin units other than propylene units and having a melting point of 90° to 140° C.
Claim 16
Dependent Claim
17 words
A metal-deposited laminated film according to claim 8, wherein the adhesive force is 0.2 to 0.8 g/cm.
References Cited (Backward Citations)
US4559266A
Cited
US4594292A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-11-23 | 1991-05-25 | 1991-11-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-11-23 | 1995-05-25 | 1995-11-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-11-23 | 1999-05-25 | 1999-11-24 | $7700.00 | Window Closed / Lapsed |