Method of solidifying radioactive solid waste
Assignee: Hitachi Ltd
•
Filing: 1985-09-05
•
Granted: 1987-11-24
•
Expires: 2005-09-05
Abstract
Abstract A method of solidifying radioactive waste wherein radioactive solid waste of a predetermined shape are embedded in a solidifying material which has a modulus of elasticity that is equal to, or smaller than, the modulus of elasticity of said waste, to provide a solidified body. The modulus of elasticity of the solidifying material is adjusted to be equal to, or smaller than, that of the radioactive solid waste, in order to prevent stress concentrations at the boundaries between the solidifying material and the radioactive solid waste, particularly on the solidifying material side thereof. The invention makes it possible to prepare a solidified body with a desired durability and safety factor.
Inventors
- 👤 Tetsuo Fukasawa
- 👤 Fumio Kawamura
- 👤 Makoto Kikuchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 23:11
CPC Classifications
G; G21; G21F; G21F9/00; G21F9/04; G21F9/06; G21F9/16; G21F9/28; G21F9/30; G21F9/301; G21F9/307
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
136 words
A method of solidifying radioactive waste which comprises embedding mirabilite pellets that are obtained by drying, granulating and pelletizing radioactive solid waste, directly in a solidifying material to provide a solidified package; the solidifying material being a crosslinked plastic resin with a large distance between crosslinked points and having a modulus of elasticity that is smaller than the modulus of elasticity of the mirabilite pellets and the plastic resin being not greater than an external pressure applied to the solidified package, wherein the plastic resin is a polymer consisting of a styrene and an unsaturated polyester which contains a polybutadiene glycol, and the mirabilite pellets have a modulus of elasticity on the order of 10 3 Kg/cm 2 and the plastic resin has a modulus of elasticity on the order of 10 2 Kg/cm 2 .
Claim 2
Independent Claim
136 words
A method of solidifying radioactive waste which comprises embedding mirabilite pellets that are obtained by drying, granulating and pelletizing radioactive solid waste, directly in a solidifying material to provide a solidified package; the solidifying material being a crosslinked plastic resin with a large distance between crosslinked points and having a modulus of elasticity that is smaller than the modulus of elasticity of the mirabilite pellets and the plastic resin being not greater than an external pressure applied to the solidified package, wherein the plastic resin is a polymer consisting of a styrene and an unsaturated polyester which contains a polybutadiene glycol, and the mirabilite pellets have a modulus of elasticity on the order of 10 3 Kg/cm 2 and the plastic resin has a modulus of elasticity on the order of 10 2 Kg/cm 2 .
Claim 3
Independent Claim
123 words
A method of solidifying radioactive waste which comprises embedding mirabilite pellets that are obtained by drying, granulating and pelletizing radioactive waste, directly in a solidifying material to provide a solidified package, wherein the solidifying material is cement which contains a rubber-like binder and has a modulus of elasticity that is smaller than the modulus elasticity of said mirabilite pellets, and further a tangential stress σ at a boundary between a solid mirabilite pellets and the cement is not greater than an external pressure applied to the solidified package; and the mirabilite pellets having a modulus of elasticity on the order of 10 3 Kg/cm 2 and the plastic resin having a modulus of elasticity on the order of 10 2 Kg/cm 2 .
Claim 4
Independent Claim
123 words
A method of solidifying radioactive waste which comprises embedding mirabilite pellets that are obtained by drying, granulating and pelletizing radioactive waste, directly in a solidifying material to provide a solidified package, wherein the solidifying material is cement which contains a rubber-like binder and has a modulus of elasticity that is smaller than the modulus elasticity of said mirabilite pellets, and further a tangential stress σ at a boundary between a solid mirabilite pellets and the cement is not greater than an external pressure applied to the solidified package; and the mirabilite pellets having a modulus of elasticity on the order of 10 3 Kg/cm 2 and the plastic resin having a modulus of elasticity on the order of 10 2 Kg/cm 2 .
References Cited (Backward Citations)
US3492147A
Cited
US3669299A
Cited
US3798123A
Cited
US4134941A
Cited
SU502558A1
Cited
SU550040A1
Cited
JPS5241800A
Cited
DE2655957A1
Cited
US4222889A
Cited
DE2748098A1
Cited
DE2819086A1
Cited
US4257912A
Cited
US4268409A
Cited
US4242220A
Cited
FR2473213A1
Cited
GB2107917A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-11-23 | 1991-05-25 | 1991-11-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-11-23 | 1995-05-25 | 1995-11-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-11-23 | 1999-05-25 | 1999-11-24 | $7700.00 | Window Closed / Lapsed |