Titanium-aluminum-silicon-oxide molecular sieve compositions and process for preparing the same

Claim 2

Crystalline molecular sieves having chemical composition in the for represented by the unit empirical formula: mR:(Ti.sub.x Al.sub.y Si.sub.z)O.sub.2 wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present per mole of (Ti x Al y Si z )O 2 and has a value of from zero to about 0.3; and "x" , "y" and "z" represent the mole fractions of titanium, aluminum and silicon, respectively, present as tetrahedral oxides, said mole fractions being such that they are within the compositional area defined by points A, B, F, E and D of FIG. 1 and having a characteristic x-ray powder diffraction pattern selected from the group consisting of Table V, or Table VII, or Table XI or Table XVIII.

Claim 3

The crystalline molecular sieves according to claim 1 wherein the mole fractions of titanium, aluminum and silicon are within the hexagonal compositional area defined by points a, b, and c of the ternary diagram of FIG. 2.

Claim 4

The crystalline molecular sieves of claim 1 having the characteristic X-ray powder diffraction pattern set forth in Table V.

Claim 5

The crystalline molecular sieves of claim 1 having the characteristic x-ray powder diffraction pattern set forth in Table VII.

Claim 6

The crystalline molecular sieves of claim 1 having the characteristic X-ray powder diffraction pattern set forth in Table XI.

Claim 7

The crystalline molecular sieves of claims 1 or 2 wherein said molecular sieves have been calcined to remove at least some of any organic template present.

Claim 8

Process for preparing crystalline molecular sieves having chemical composition in the form represented by the unit empirical formula: mR:(Ti.sub.x Al.sub.y Si.sub.z)O.sub.2 wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present per mole of (Ti x Al y si z )O 2 and has a value of from zero to about 0.3; and "x", "y" and "z" represent the mole fractions of titaniium, aluminum and silicon, respectively, present as tetrahedral oxides, said mole fractions being such that they are within the compositional area defined by points A,B,F,E, and D of FIG. 1, said sieves having a characteristic X-ray powder diffraction pattern selected from the group consisting of Table V, Table VII, Table XI and Table XVIII, comprising the step of providing at an effective temperature and for an effective time a reaction mixture composition expressed in terms of molar oxide ratios as follows: aR:(Ti.sub.x Al.sub.y Si.sub.z)O.sub.2 :b H.sub.2 O wherein "R", is an organic templating agent; "a" is an effective amount of "R"; "b" has a value of from greater than zero to about 5000; and "x", "y" and "z" represent the mole fractions of titanium, aluminum and silicon, respectively, in the mR:(Ti x Al y Si z )O 2 constituent, and each has a value of at least 0.01.

Claim 9

Process for preparing crystalline molecular sieves having chemical composition in the form represented by the unit empirical formula: mR:(Ti.sub.x Al.sub.y Si.sub.z)O.sub.2 wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present per mole of (Ti x Al y si z )O 2 and has a value of from zero to about 0.3; and "x", "y" and "z" represent the mole fractions of titaniium, aluminum and silicon, respectively, present as tetrahedral oxides, said mole fractions being such that they are within the compositional area defined by points A,B,F,E, and D of FIG. 1, said sieves having a characteristic X-ray powder diffraction pattern selected from the group consisting of Table V, Table VII, Table XI and Table XVIII, comprising the step of providing at an effective temperature and for an effective time a reaction mixture composition expressed in terms of molar oxide ratios as follows: aR:(Ti.sub.x Al.sub.y Si.sub.z)O.sub.2 :b H.sub.2 O wherein "R", is an organic templating agent; "a" is an effective amount of "R"; "b" has a value of from greater than zero to about 5000; and "x", "y" and "z" represent the mole fractions of titanium, aluminum and silicon, respectively, in the mR:(Ti x Al y Si z )O 2 constituent, and each has a value of at least 0.01.

Claim 10

Process according to claim 7 wherein the source of silicon in the reaction mixture is silica.

Claim 11

Process according to claim 7 wherein the source of aluminum in the reaction mixture is at least one compound selected from the group consisting of pseudo-boehmite and aluminum alkoxides.

Claim 12

Process according to claim 9 wherein the aluminum alkoxide is aluminum isopropoxide.

Claim 13

Process according to claim 7 wherein the souce of titanium is selected from the group consisting of alkoxides, water-soluble titanates and titanium chelates.

Claim 14

Process according to claim 7 where the organic templating agent is selected from the group consisting of quaternary ammonium or quaternary phosphonium compounds of the formula: R.sub.4 X.sub.+ wherein X is nitrogen or phosphorous and each R is alkyl containing between 1 and about 8 carbon atoms or aryl.

Claim 15

Process according to claim 7 wherein the templating agent is selected from the group consisting of tetrapropylammonium ion; tetraethylammonium ion; tripropylamine; triethylamine; triethanolamine; piperidine; cyclohexylamine; 2-methyl pyridine; N,N-dimethylbenzylamine; N,N-diethylethanolamine; dicyclohexylamine; N,N-dimethylethanolamine; choline; N,N-dimethylpiperazine; pyrrolidine; 1,4-diazabicyclo-(2,2,2) octane; N-methylpiperidine; 3-methypiperidine; N-methylcyclohexylamine; 3-methylpyridine; 4-methylpyridine; quinuclidine; N,N-dimethyl-1,4-diazabicyclo (2,2,2) octane ion; tetramethylammonium ion; tetrabutylammonium ion, tetrapentylammonium ion; di-n-butylamine; neopentylamine; di-n-pentylamine; isopropylamine; t-butylamine; ethylenediamine and 2-imidazolidone; di-n-propylamine; and a polymeric quaternary ammonium salt [(C 14 H 32 N 2 )(OH) 2 ] x wherein x is a value of at least 2. pg,64

Claim 16

The crystalline molecular sieves of claim 1 having the characteristic X-ray powder diffraction pattern set forth in Table XVIII.