Process for preparing a porous polymer article
Assignee: Dow Chemical Co
•
Filing: 1986-07-07
•
Granted: 1987-11-10
•
Expires: 2006-07-07
Abstract
Abstract A porous polymer article for use as a filter medium or battery separator is prepared by admixing a cellulosic compound and a thermoplastic polymer, both usually in powder form, forming the article under pressure and heat to melt and flow the thermoplastic polymer into a continuous phase and after cooling to set the polymer matrix, contacting the set admixture with a solvent, e.g. water, for the cellulosic compound which will not also dissolve the polymer matrix to produce a porous polymer which has a predetermined degree of porosity and is free from residual salt. The article so produced is also disclosed.
Inventors
- 👤 Gaylon L. Dighton
- 👤 Donald W. Pennington
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 12:33
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/26; C08J2201/00; C08J2201/04; C08J2201/046; C08J2323/00; C08J2323/02; C08J2401/00
Claims Analysis
Total Claims: 42
Claim 1
Independent Claim
115 words
A process for preparing a porous thermoplastic polymer article having a predetermined degree of porosity, which process consists of the steps of (a) admixing a water soluble cellulosic compound of predetermined particle size and a polyolefin thermoplastic compound which is insoluble in water; (b) forming the admixture into the shape desired for said article under conditions sufficient to form a continuous phase of said thermoplastic compound and a non-continuous phase of said cellulosic compound; and (c) contacting said admixture with water to solubilize a major portion of said cellulosic compound and separating the aqueous cellulosic compound-containing solution from the thermoplastic polymer whereby said porous thermoplastic polymer article having a predetermined degree of porosity is produced.
Claim 2
Dependent Claim
115 words
A process for preparing a porous thermoplastic polymer article having a predetermined degree of porosity, which process consists of the steps of (a) admixing a water soluble cellulosic compound of predetermined particle size and a polyolefin thermoplastic compound which is insoluble in water; (b) forming the admixture into the shape desired for said article under conditions sufficient to form a continuous phase of said thermoplastic compound and a non-continuous phase of said cellulosic compound; and (c) contacting said admixture with water to solubilize a major portion of said cellulosic compound and separating the aqueous cellulosic compound-containing solution from the thermoplastic polymer whereby said porous thermoplastic polymer article having a predetermined degree of porosity is produced.
Claim 3
Dependent Claim
14 words
The process of claim 1 in which said cellulosic compound is a cellulose ether.
Claim 4
Dependent Claim
21 words
The process of claim 2 in which said cellulose ether is selected from methylcellulose, hydroxyethylcellulose, hydroxypropylcellulose, hydroxyethylmethylcellulose, hydroxyethylhydroxypropylcellulose and mixtures thereof.
Claim 5
Dependent Claim
13 words
The process of claim 3 in which said cellulose ether is a methylcellulose.
Claim 6
Dependent Claim
37 words
The process of claim 4 in which said methylcellulose viscosity of a 2% solution in water at 20° C. is in the range of from about 3 to about 100,000 cps (0.003 to about 100 pascal seconds).
Claim 7
Dependent Claim
22 words
The process of claim 1 in which said thermoplastic compound is selected from a polyolefin, a chlorinated polyethylene or a polyvinyl chloride.
Claim 8
Dependent Claim
13 words
The process of claim 6 in which said thermoplastic compound is a polyolefin.
Claim 9
Dependent Claim
16 words
The process of claim 7 in which said polyolefin is selected from polyethylene, polypropylene, and polybutylene.
Claim 10
Dependent Claim
11 words
The process of claim 8 in which said polyolefin is polyethylene.
Claim 11
Dependent Claim
19 words
The process of claim 9 in which said polyethylene is selected from high density polyethylene and low density polyethylene.
Claim 12
Dependent Claim
13 words
The process of claim 10 in which said polyethylene is high density polyethylene.
Claim 13
Dependent Claim
14 words
The process of claim 6 in which said thermoplastic compound is a chlorinated polyethylene.
Claim 14
Dependent Claim
34 words
The process of claim 1 in which from about 40 to about 70 weight percent of said cellulosic compound is admixed with from about 30 to about 60 weight percent of said thermoplastic compound.
Claim 15
Dependent Claim
34 words
The process of claim 13 in which from about 40 to about 60 weight percent of said cellulosic compound is admixed with from about 60 to about 40 weight percent of said thermoplastic compound.
Claim 16
Dependent Claim
19 words
The process of claim 1 wherein said cellulosic and said thermoplastic compounds are in the form of blendable powders.
Claim 17
Dependent Claim
28 words
The process of claim 15 in which said blendable powders of said cellulosic and said thermoplastic compounds have a difference in density not greater than about 20 percent
Claim 18
Dependent Claim
37 words
The process of claim 1 further characterized in that the forming of said step (b) is carried out by heating said admixture to a temperature sufficient to melt and flow said thermoplastic compound, forming a continuous phase.
Claim 19
Dependent Claim
36 words
The process of claim 17 still further characterized in that said forming and said heating are carried out in an apparatus selected from a compression molding press, a helical screw extruder or an injection molding machine.
Claim 20
Dependent Claim
14 words
The process of claim 18 in which said apparatus is a compression molding press.
Claim 21
Dependent Claim
14 words
The process of claim 18 in which said apparatus is a helical screw extruder.
Claim 22
Dependent Claim
14 words
The process of claim 18 in which said apparatus is an injection molding machine.
Claim 23
Dependent Claim
19 words
The process of claim 17 in which said temperature is in the range of about 300°-400° F. (149°-204° C.)
Claim 24
Dependent Claim
14 words
The process of claim 22 in which said apparatus is a compression molding press.
Claim 25
Dependent Claim
26 words
The process of claim 23 in which said temperature is in the range of about 340° to about 360° F. (about 171 to about 182° C.).
Claim 26
Dependent Claim
33 words
The process of claim 17 wherein after said heating and flowing of said step (b), said admixture is cooled for a period sufficient to solidify said molten thermoplastic compound and set said admixture.
Claim 27
Dependent Claim
14 words
The process of claim 25 wherein said admixture is cooled to about ambient conditions.
Claim 28
Dependent Claim
25 words
The process of claim 1 in which said contacting of said step (c) is carried out by complete immersion of said article in flowing water.
Claim 29
Dependent Claim
23 words
The process of claim 27 in which said contacting is carried out at a temperature of from about 10 to about 80° C.
Claim 30
Dependent Claim
23 words
The process of claim 27 in which said contacting results in solubilization of 95 to about 85 weight percent of said cellulosic compound.
Claim 31
Dependent Claim
21 words
The process of claim 1 in which said cellulosic compound is a cellulose ether and said thermoplastic compound is a polyolefin.
Claim 32
Dependent Claim
19 words
The process of claim 30 in which said cellulose ether is selected from methylcellulose, hydroxyethylcellulose, hydroxypropylcellulose, hydroxyethylhydroxypropylcellulose, and hydroxyethylmethylcellulose.
Claim 33
Dependent Claim
13 words
The process of claim 31 in which said cellulose ether is a methylcellulose.
Claim 34
Dependent Claim
16 words
The process of claim 31 in which said polyolefin is selected from polyethylene, polypropylene and polybutylene.
Claim 35
Dependent Claim
11 words
The process of claim 33 in which said polyolefin is polyethylene.
Claim 36
Dependent Claim
34 words
The process of claim 30 in which from about 40 to about 70 weight percent of said cellulosic compound is admixed with from about 30 to about 60 weight percent of said thermoplastic compound.
Claim 37
Dependent Claim
26 words
The process of claim 35 in which said cellulosic and said thermoplastic compounds are blendable powders having a density difference not greater than about 20 percent.
Claim 38
Dependent Claim
20 words
The process of claim 1 in which said cellulosic compound is a methylcellulose and said thermoplastic compound is a polyethylene.
Claim 39
Dependent Claim
60 words
The process of claim 37 in which from 40 to about 60 weight percent of said methylcellulose is admixed with from about 60 to about 40 weight percent of polyethylene and heated to a temperature of from about 325 to about 375° C. for a period sufficient to flow said polyethylene into a continuous phase; and thereafter cooling said admixture.
Claim 40
Dependent Claim
28 words
The process of claim 38 in which said heating is carried out in a compression molding press and the cooled admixture is contacted by immersing in flowing water.
Claim 41
Dependent Claim
22 words
The process of claim 39 wherein said contacting is carried out at a temperature of from about 10 to about 80° C.
Claim 42
Dependent Claim
19 words
The process of claim 39 wherein prior to said contacting the admixture is fabricated into end use application shapes.
References Cited (Backward Citations)
US3454544A
Cited
US3388082A
Cited
US3367891A
Cited
US3873518A
Cited
US4015067A
Cited
US4115492A
Cited
US4425206A
Cited
US4456751A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-11-09 | 1991-05-11 | 1991-11-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-11-09 | 1995-05-11 | 1995-11-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-11-09 | 1999-05-11 | 1999-11-10 | $7700.00 | Window Closed / Lapsed |