Method for brazing a magnesium-containing aluminum alloy
Assignee: Denso Corp
•
Filing: 1985-12-18
•
Granted: 1987-11-10
•
Expires: 2005-12-18
Abstract
Abstract An aluminum alloy including magnesium can be joined by brazing even when flux made of potassium fluoaluminates is employed. The aluminum alloy including magnesium is heated in a vacuum, so that magnesium in the aluminum alloy evaporates from the surface of the aluminum alloy. The weight ratio of magnesium at the surface of the aluminum alloy can be reduced to less than 0.5 as a result of the heating step. The aluminum alloy treated by this operation is, thereafter covered with brazing material and clad with flux. After that, the aluminum alloy is heated in a furnace in order to melt the brazing material.
Inventors
- 👤 Hiroshi Kamiya
- 👤 Takeshi Iguchi
- 👤 Shigenobu Fukumi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 18:23
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/001; B23K35/002; B23K1/00; B23K1/20; B23K2101/00; B23K2101/04; B23K2101/14; B23K2103/00; B23K2103/08; B23K2103/10; B23K2103/16
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
117 words
A method for brazing a magnesium-containing aluminum alloy, comprising: (a) providing an element made of said alloy and having magnesium distributed generally evenly throughout at a concentration level which exceeds a predetermined threshold value; (b) thereafter, subjecting said element to a treatment operation for reducing said magnesium concentration level only in a surface portion of at least a connection site on said element to no higher than said predetermined threshold value; (c) thereafter, depositing brazing material on said element in the vicinity of said connection site; (d) thereafter, cladding said brazing material with a potassium fluoaluminate flux; and (e) thereafter, heating said element and said brazing material sufficiently to melt said brazing material at said connection site.
Claim 2
Independent Claim
117 words
A method for brazing a magnesium-containing aluminum alloy, comprising: (a) providing an element made of said alloy and having magnesium distributed generally evenly throughout at a concentration level which exceeds a predetermined threshold value; (b) thereafter, subjecting said element to a treatment operation for reducing said magnesium concentration level only in a surface portion of at least a connection site on said element to no higher than said predetermined threshold value; (c) thereafter, depositing brazing material on said element in the vicinity of said connection site; (d) thereafter, cladding said brazing material with a potassium fluoaluminate flux; and (e) thereafter, heating said element and said brazing material sufficiently to melt said brazing material at said connection site.
Claim 3
Dependent Claim
13 words
The method of claim 1, wherein: step (b) is conducted in a vacuum.
Claim 4
Dependent Claim
12 words
The method of claim 2, wherein: said vacuum is 5.0×10 -5 torr.
Claim 5
Dependent Claim
18 words
The method of claim 2, wherein: step (b) is conducted at an elevated temperature of about 600° C.
Claim 6
Dependent Claim
18 words
The method of claim 4, wherein: said element is subjected to said elevated temperature for about 20 minutes.
Claim 7
Dependent Claim
17 words
The method of claim 1 wherein: said predetermined threshold value is a magnesium:aluminum weight ratio of 0.5.
Claim 8
Dependent Claim
50 words
The method of claim 1, wherein: said element is a connector for a condenser of an automotive air conditioner and step (e) is conducted with said connector juxtaposed with an end of a coolant tube at said connection site for mounting said connector on said end of said coolant tube.
Claim 9
Dependent Claim
20 words
The method of claim 1, wherein: said aluminum alloy is one selected from the group consisting of A7001 and A7004.
References Cited (Backward Citations)
US4556165A
Cited
JPH113969A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-11-09 | 1991-05-11 | 1991-11-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-11-09 | 1995-05-11 | 1995-11-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-11-09 | 1999-05-11 | 1999-11-10 | $7700.00 | Window Closed / Lapsed |