Assignee: Mitsubishi Chemical Corp
•
Filing: 1985-11-15
•
Granted: 1987-11-03
•
Expires: 2005-11-15
Abstract
Abstract A process for producing an air-permeable film is described, comprising stretching in at least one direction a film made of a composition comprising 42 to 87 vol % of a polyolefin resin and 58 to 13 vol % of an inorganic filler and further containing an aliphatic alcohol/fatty acid ester of a fatty acid having 10 to 22 carbon atoms and an aliphatic alcohol having 1 to 12 carbon atoms in an amount of 3 to 25 parts by weight per 100 parts by weight of the above composition.
Inventors
- 👤 Katsumi Okuyama
- 👤 Hiroyasu Mizutani
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 15:50
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/18; B; B29; B29C; B29C48/00; B29C48/03; B29C48/07; B29C48/08; B29C48/09; B29C48/10; B29C48/25; B29C48/88; B29C48/90; B29C48/901; B29C48/902; B29C48/91; B29C48/911; B29C48/9135; B29C48/914; B29C55/00; B29C55/005; B29D; B29D7/00; B29D7/01; B29C48/001; B29C48/0018; B29K; B29K2105/00; B29K2105/06; B29K2105/16; B29K2995/00; B29K2995/0037; B29K2995/0072; C08J2323/00; C08J2323/02; C08J2323/04; C08J2323/08; Y; Y10; Y10S; Y10S264/00; Y10S264/13
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
97 words
A process for producing a soft, air-permeable film having substantially uniform thickness, which comprises stretching in at least one direction a film made of a composition comprising 42 to 87 vol % of a polyolefin resin and 58 to 13 vol % of an inorganic filler wherein an aliphatic alcohol/fatty acid ester of a fatty acid having 10 to 22 carbon atoms and an aliphatic alcohol having 1 to 12 carbon atoms is further added to the above composition in an amount of 3 to 25 parts by weight per 100 parts by weight of the composition.
Claim 2
Dependent Claim
97 words
A process for producing a soft, air-permeable film having substantially uniform thickness, which comprises stretching in at least one direction a film made of a composition comprising 42 to 87 vol % of a polyolefin resin and 58 to 13 vol % of an inorganic filler wherein an aliphatic alcohol/fatty acid ester of a fatty acid having 10 to 22 carbon atoms and an aliphatic alcohol having 1 to 12 carbon atoms is further added to the above composition in an amount of 3 to 25 parts by weight per 100 parts by weight of the composition.
Claim 3
Dependent Claim
35 words
The process as claimed in claim 1, wherein the polyolefin resin is an ethylene-α-olefin copolymer having a density of 0.910 to 0.940 g/cm 3 and a melt flow rate of 0.1 to 5 g/10 min.
Claim 4
Dependent Claim
65 words
The process as claimed in claim 1, wherein the polyolefin resin is a mixture of an ethylene-α-olefin copolymer having a density of 0.910 to 0.940 g/cm 3 and a melt flow rate of 0.1 to 5 g/10 min and a high density polyethylene having a density of not less than 0.941 g/cm 3 and a melt flow rate of not more than 1.0 g/10 min.
Claim 5
Dependent Claim
63 words
The process as claimed in claim 1, wherein the polyolefin resin is a mixture of an ethylene-α-olefin copolymer having a density of 0.910 to 0.940 g/cm 3 and a melt flow rate of 0.1 to 5 g/10 min and a low density polyethylene having a density of 0.910 to 0.928 g/cm 3 and a melt flow rate of 0.3 to 10 g/10 min.
Claim 6
Dependent Claim
21 words
The process as claimed in claim 1, wherein the inorganic filler has an average particle size of 0.1 to 5 μm.
Claim 7
Dependent Claim
18 words
The process as claimed in claim 1, wherein the ester is an ester of ricinolic acid and glycerol.
Claim 8
Dependent Claim
18 words
The process as claimed in claim 1, wherein the stretching ratio in one direction is 1.2 to 6.
Claim 9
Dependent Claim
13 words
The process as claimed in claim 1, wherein the stretching is biaxial stretching.
Claim 10
Dependent Claim
64 words
The process as claimed in claim 8, wherein said stretching comprises biaxially stretching a tubular unstretched film which film is guided along a truncated-conical mandrel, and subsequently cooled by blowing a gas from the outside thereof, while at the same time a gas is continuously blown into the tube of the film so that the gas penetrates through the film and goes outside thereof.
Claim 11
Dependent Claim
54 words
The process as claimed in claim 9, wherein said gas is blown into the tube of the film through a conduit which is connected to an extrenal pressurized container and penetrates through a circular die, a mandrel supporting rod and the mandrel interior and which opens at a larger diameter end of the mandrel.
Claim 12
Dependent Claim
60 words
The process as claimed in claim 2, wherein said ethylene-α-olefin copolymer comprises 1 to 20 wt. % of an α-olefin having a C 3 -C 8 molecular skeleton and 99-80 wt. % of ethylene, which copolymer is prepared by copolymerizing ethylene and at least one α-olefin having a C 3 -C 8 molecular skeleton in the presence of a catalyst.
Claim 13
Dependent Claim
28 words
The process as claimed in claim 1, wherein said polyolefin is selected from the group consisting of low density polyethyelene, high density polyethyelene, polypropylene and an ethylene-α-olefin copolymer.
Claim 14
Dependent Claim
36 words
The process as claimed in claim 12, wherein said polyolefin is a high density polyethylene having a density of at least 0.941 g/cm 3 and a melt flow rate of not more than 1.0 g/10 min.
Claim 15
Dependent Claim
33 words
The process as claimed in claim 12, wherein said polyolefin is low density polyethylene having a density of 0.910-0.928 g/cm 3 and a melt flow rate of not more than 0.3-10 g/10 min.
Claim 16
Dependent Claim
22 words
The process as claimed in claim 12, wherein said polyolefin is a polypropylene having a melt flow rate of 0.5-10 g/10 min.
Claim 17
Dependent Claim
23 words
The process as claimed in claim 1, wherein said fatty acid has 12-18 carbon atoms, and said aliphatic alcohol has 1-6 carbon atoms.
Claim 18
Dependent Claim
35 words
The process as claimed in claim 1, wherein said fatty acid is selected from the group consisting of lauric acid, myristic acid, palmitic acid, stearic acid, oleic acid, linolic acid, linolenic acid and ricinoleic acid.
Claim 19
Dependent Claim
32 words
The process as claimed in claim 1, wherein said aliphatic alcohol is selected from the group consisting of methyl alcohol, ethyl alcohol, butyl alcohol, ethylene glycol, propylene glycol, glycerol, pentaerythritol and sorbitol.
Claim 20
Dependent Claim
38 words
The process as claimed in claim 9, wherein said stretching is effected at a temperature satisfying the following equation: Tm-50≦Ts≦Tm-5 wherein Ts is the stretching temperature, and Tm is the melting point in degrees C. of the resin.
Claim 21
Dependent Claim
30 words
The process as claimed in claim 9, wherein the gas blown into the tube of the film is blown at a volume in the range of 0.1-150 Nl/m 2 .min.
References Cited (Backward Citations)
US3154461A
Cited
US3539666A
Cited
US3679538A
Cited
US3823210A
Cited
US3862030A
Cited
US3843761A
Cited
US4472328A
Cited
US4585604A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-11-02 | 1991-05-04 | 1991-11-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-11-02 | 1995-05-04 | 1995-11-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-11-02 | 1999-05-04 | 1999-11-03 | $7700.00 | Window Closed / Lapsed |